Giovanni Borsoi

External Thermal Insulation Composite Systems (ETICSs) are increasingly applied in both new construction and energy retrofitting, where long-term durability under environmental exposure is critical to preserving thermal efficiency. Moisture ingress represents a key degradation factor, reducing insulation performance and undermining energy savings promoted by the ETICS. The effectiveness of these systems is strongly influenced by surface protection, which also reflects aesthetic and biological resistance. This study investigates the influence of three commercial protective surface coatings, characterized by hydrophobicity, photocatalytic activity, and resistance to biological growth, on ETICS finishes based on acrylic, natural hydraulic lime (NHL), and silicate binders. An artificial aging protocol was employed to evaluate coating stability and compatibility with the finishing layers. Results show that acrylic-based finishes provided superior durability and protection, while coatings on NHL and silicate substrates exhibited lower performance. Notably, a TiO₂ enriched photocatalytic coating, despite improved self-cleaning potential, demonstrated the least durability. The findings highlight that optimal ETICS protection requires coatings that combine low water absorption, effective drying, and biological resistance, thereby ensuring sustained thermal and energy performance over time.

Over the past two decades, the application of nanostructured materials in construction, such as concrete, paint, coatings, glass, renders, plasters, thermal insulation, steel, and even sensors, has become increasingly prevalent. However, previous studies and reports have raised concerns about the ecotoxicity and long-term impact of nanomaterials on human health and the environment. National and international legislation and regulations are struggling to keep up with the rapid development of nanomaterials, taking into account their unique characteristics and essential requirements for application and commercialization. This paper, based on existing standards for conventional materials and bibliometric networks of papers focused on nanomaterials, conducts a critical review and proposes relevant indicators for the application of nanomaterials in the construction sector. These indicators should be mandatory and are divided into environmental, human health, and economic perspectives, providing a risk assessment framework for applying nanomaterial-based constructive solutions oriented to environmental, social, and economic sustainability.

There is no doubt that nanotechnology and nanoscience open new doors to new applications and products that can potentially revolutionize the practice field and how we conserve built heritage materials. However, we are living at the beginning of this era and the potential benefits of nanotechnology to specific conservation practice needs are not always fully understood. This opinion/review paper aims to present reflections and answer a question that we are often asked when working directly with stone field conservators: why should we use a nanomaterial instead of a conventional product? Why does size matter? To answer this question, we revise the basic concepts of nanoscience with implications for the built heritage conservation field.

External Thermal Insulation Composite Systems (ETICS) are widely used constructive solutions which aim at enhancing the building thermal performance. Nevertheless, ETICS can often present anomalies (e.g., stains and microcracks) throughout their service life, and vandalism actions, as in the case of graffiti, are rather common in urban areas. The removal of undesired graffiti is generally carried out through invasive chemical–mechanical methods, which may affect the durability of the ETICS. The adoption of anti-graffiti products can be a feasible protection method; however, no comprehensive studies were already addressed on these substrates. This study aims at evaluating the effectiveness, compatibility, and durability of three anti-graffiti products (with permanent, semi-permanent, and sacrificial properties) when applied on different ETICS. The removal of aerosol graffiti paints was carried out with a low-invasive and eco-friendly removal method (i.e., low-pressure steam jet). The water transport properties, as well as color, gloss, and roughness, were evaluated before and after graffiti removal. The durability of the anti-graffiti was also assessed by artificial aging cycles. Results showed that graffiti removal was rather efficient on ETICS with acrylic-based finishing coats and when using (semi) permanent anti-graffiti products (with ΔE*_ab < 5, i.e., not macroscopically visible, when comparing cleaned and reference surfaces), although these products can reduce their effectiveness after aging. Conversely, unsatisfactory graffiti cleaning was observed on ETICS with lime-based or silicate-based finishing coats (with ΔE*_ab > 5), with considerable alteration also of the water transport properties (reducing water absorption and slowing down the drying kinetic).

This Special Issue examines the synthesis, characterization, and manufacturing of nanoparticles and their potential advantages and applications for the conservation of built cultural heritage materials

The energy performance and thermal comfort of buildings are decisive factors for users. Thus, solutions such as the external thermal insulation systems (ETICS) that can be installed in either new buildings or buildings under thermal retrofitting, reducing the energy consumption while improving thermal comfort, tend to become mainstream. This paper purposes to quantify the environmental and economic impacts of various ETICS protection solutions to assist in decision-making at the project phase. In this study, products available on the Portuguese market are considered. The protection products considered are hydrophobic agents, biocides, multifunctional, and self-cleaning. The products are compared by type of protection, presenting some of the most impactful components, following a multicriteria analysis of some of those products gathered into different solutions, with the objective of demonstrating the influence of the weights assigned to environmental and economic indicators. Several data-linked problems were identified, such as the quantity and quality of data available for analysis, crucial to their reliability; thus, an index for quality of information was developed in order to compare different products. In the multicriteria analysis, the weights of the sensitivity analysis between environmental and economic indicators highly influence the “best solution”; therefore, stakeholders need to clearly define their objectives.

External Thermal Insulation Composite Systems (ETICS) are constructive solutions widely used to increase the thermal insulation in new and retrofitted buildings. However, these systems can present several anomalies due to their constant exposure to weathering agents and anthropic factors. Water is generally the major cause of degradation. Thus, the application of water-repellent products can minimize the appearance of anomalies and increase the durability of the systems. In this paper, acrylic-based and siloxane-based hydrophobic products were applied to ETICS, with the aim of assessing the compatibility, effectiveness, and durability of these products. The moisture transport properties and mould susceptibility were assessed through laboratory tests on untreated and treated specimens. The durability of the hydrophobic treatments was also evaluated through artificial aging tests (heat-cold and freeze-thaw cycles). Results show that the protection products generally decreased water absorption, slightly decreased the drying rate, and presented adequate water vapor permeability. After aging, the products still had reasonable effectiveness and, with one exception, improved the water vapor diffusion of the systems. Additionally, ETICS underwent an alteration in the finishing coat (possible modification of the porosity) due to the aging cycles. No clear linear correlation was found between the contact angle values and water absorption results, evidencing the influence of other factors related to the composition of the water-repellent products.

The production of Portland cement (OP) is commonly associated to significant level of energy consumption and gas emissions. The use of calcium sulfoaluminate cement (CSA) can be a sustainable alternative binder, since its production releases about half of the CO₂ emissions and its clinker requires 200 °C lower temperatures, when compared to OP. Furthermore, CSA has fast setting time and achieves higher strength in shorter periods, as well as reduced shrinkage. This paper discusses the incorporation of CSA in rendering mortars and basecoat mortars for ETICS (External Thermal Insulation Composite Systems). The physical-mechanical properties of mortars made with OP and CSA cements were experimental evaluated. The results showed that the introduction of CSA generally improves shrinkage, compressive strength, water absorption at low pressure, enhances the tensile bending strength and decreases the setting time. The amount of CSA introduced into the mixture significantly affected the properties of the cement matrix.