By restricting the dilated deformation, surface modification can stimulate multiple shear banding and improve the plasticity of bulk metallic glasses (BMGs). Aimed at modifying the surface of BMGs by thin layers, a crystalline Ni coating with ultrafine grains was coated on the surface of a Ti-based BMG by electroless plating. With a thickness of about 10 μm, the prepared thin coating could effectively limit the fast propagation of primary shear bands and stimulate the nucleation of multiple shear bands. As a result, the compression plasticity of the coated Ti-based BMG was improved to about 3.7% from near 0% of the non-coated BMG. Except for a small amount of Ni coating was adhered to the BMG substrate after fracture, most of the coatings were peeled off from the surface. It can be attributed to the abnormal growth of some coarse grains/particles in local region of the coating, which induces a large tensile stress at the interface between the coating and the BMG substrate. It is suggested that, for electroless nickel plating, improving the adhesive bonding strength between the coating and the substrate has a better geometric restriction effect than simply increasing the thickness of the coating.

Magnesium-based bulk metallic glass matrix composites (BMGMCs) have better plasticity than the corresponding bulk metallic glasses (BMGs); however, their strength and density are often compromised due to the fact that the effective reinforcement phase is mostly plastic heavy metal. For lightweight SiC-particle reinforced BMGMCs, interface wettability and the sharpness of the particles often reduce the strengthening effect. In this work, SiC particles were coated with a thin Cu coating by electroless plating, and added to Mg₅₄Cu_26.5Ag_8.5Gd₁₁ melt in an amount of 5 wt % to prepare a BMGMC. The microstructure of the interface, mechanical behavior and fracture morphology of the BMGMC were studied by scanning electron microscopy and quasi-static compression testing. The results showed that the Cu coating improved the wettability between SiC and the matrix alloy without obvious interfacial reactions, leading to the dispersion of SiC particles in the matrix. The addition of Cu-coated SiC particles improved the plastic deformation ability of Mg₅₄Cu_26.5Ag_8.5Gd₁₁ BMG, proving that electroless plating was an effective method for controlling the interface microstructure and mechanical behavior of BMGMCs.

Mg-Zn-Ca metallic glass (MG) is effective for degrading azo dyes; however, the related surface evolution and degradation mechanisms are little known. We comparatively investigated the initial surface corrosion morphologies of melt-spun Mg₆₆Zn₃₀Ca₄ MG in deionized water and artificial seawater. It was found that the basic corrosion behavior of the MG was the same, except that the corrosion process was accelerated in seawater. The presence of NaCl obviously promotes the formation of nano-ZnO on the surface of ribbons, causing the rapid degradation of azo dyes due to the photocatalytic effect. The degradation efficiency when combined with 3.5 wt % NaCl was over 100 times higher than that without NaCl. This indicates that Mg-Zn-Ca MG ribbons are effective additives for the degradation of azo dyes in seawater.