Andreas Ewald Bumberger

In this work, we investigated La0.6Sr0.4CoO3−δ / SrTi0.3Fe0.7O3−δ multilayer systems with different layer thicknesses. Reciprocal space mapping showed splitting of the reflections in the sample with 5 nm layers while for 15 nm thick layers reflections have been elongated. Using transmission electron microscopy, we investigated this phenomenon at the atomic scale and showed that the alternating 15 nm layers gradually increase their tensile out-of-plane strain, whereas the sample with 5 nm layers maintains a relatively stable strain state. In-plane strain relaxation is similar in both samples. Still, it differs in the strain relaxation mechanism, which involves the formation of amorphous regions in the 5 nm sample and the formation of edge dislocations in the 15 nm sample. Electron energy loss spectroscopy was employed to probe the oxidation states of Co, Fe, and Ti. In both samples, the oxygen vacancy concentration increases toward the surface.

A highly intuitive, yet physically meaningful approach to understanding the impedance of MIECs based on a four-terminal transmission line model.

Chemical capacitance measurements reveal the impact of oxygen vacancies on the electrochemical properties of epitaxial LiNi _0.5 Mn _1.5 O _{4− δ} thin films. Oxygen deficiency not only impacts the amount of redox active Mn, but also promotes electron trapping.

Spinels of the general formula Li_2-δM₂O₄ are an essential class of cathode materials for Li-ion batteries, and their optimization in terms of electrode potential, accessible capacity, and charge/discharge kinetics relies on an accurate understanding of the underlying solid-state mass and charge transport processes. In this work, we report a comprehensive impedance study of sputter-deposited epitaxial Li_2-δMn₂O₄ thin films as a function of state-of-charge for almost the entire tetrahedral-site regime (1 ≤ δ ≤ 1.9) and provide a complete set of electrochemical properties, consisting of the charge-transfer resistance, ionic conductivity, volume-specific chemical capacitance, and chemical diffusivity. The obtained properties vary by up to three orders of magnitude and provide essential insights into the point defect concentration dependences of the overall electrode potential. We introduce a defect chemical model based on simple concentration dependences of the Li chemical potential, considering the tetrahedral and octahedral lattice site restrictions defined by the spinel crystal structure. The proposed model is in excellent qualitative and quantitative agreement with the experimental data, excluding the two-phase regime around 4.15 V. It can easily be adapted for other transition metal stoichiometries and doping states and is thus applicable to the defect chemical analysis of all spinel-type cathode materials.

The electron beam, during high-resolution transmission electron microscopy, was employed to induce a phase transition in La0.6Sr0.4CoO2.5 (LSC) from a brownmillerite ordering to an oxygen deficient perovskite structure. Prior to irradiation, a strongly alternating out-of-plane lattice parameter was observed, reflecting electrostatic interactions between AO and BO/BO2 planes in the brownmillerite ordering. During electron beam irradiation for one hour, the oxygen vacancy ordering vanished gradually, and a uniform cubic perovskite structure prevailed. To exclude beam-induced heating effects, in situ heating experiments were performed, revealing a stable brownmillerite ordering in the relevant temperature range (up to at least 500 °C). Thus, we conclude that the phase transition is caused by knock-on processes that affect oxygen vacancies in terms of a transition from structural vacancies toward extremely high concentrations of randomly distributed point defects in the ABO3 structure.

Electrochemical impedance spectroscopy was used to investigate the chemical capacitance of La_0.6Sr_0.4CoO_3-δ (LSC) thin-film electrodes under anodic polarization (i.e., in the electrolysis mode). For this purpose, electrodes with different microstructures were prepared via pulsed-laser deposition. Analysis of dense electrodes and electrodes with open porosity revealed decreasing chemical capacitances with increasing anodic overpotentials, as expected from defect chemical considerations. However, extremely high chemical capacitance peaks with values in the range of 10⁴ F/cm³ at overpotentials of >140 mV were obtained after annealing for several hours in synthetic air and/or after applying high anodic bias voltages of >750 mV. From the results of several surface analysis techniques and transmission electron microscopy, it is concluded that closed pores develop upon both of these treatments: (i) During annealing, initially open pores get closed by SrSO₄, which forms due to strontium segregation in measurement gases with minute traces of sulfur. (ii) The bias treatment causes mechanical failure and morphological changes including closed pores in the bulk of dense films. Under anodic polarization, high-pressure oxygen accumulates in those closed pores, and this causes the capacitance peak. Model calculations based on a real-gas equation allow us to properly predict the experimentally obtained capacitance increase. We demonstrate that analysis of the chemical capacitance of oxygen electrodes in solid oxide electrolysis cells can thus be used as a nondestructive observation tool to detect and quantify closed porosity with a lower detection limit between 10^-4 and 10^-3.

The changes of the surface morphology and the surface chemistry of LSC thin films grown on different substrates were tracked for 100 hours under SOFC operation conditions. Atomic force microscopy was used to monitor the formation of particles at the LSC surface. Depending on the thin film structure (polycrystalline vs. epitaxial), different particle formation dynamics were observed. Electron microscopy was employed to investigate the chemistry of the segregated particles and revealed that the particles were Sr- and S-rich. Secondary ion mass spectrometry and X-ray photoelectron spectroscopy measurements were performed on degraded LSC thin films, which also found significant amounts of sulfur on the LSC surface, despite no deliberate addition of sulfur compounds, as well as A-site cation enrichment. Impedance spectroscopy was used to track the polarization resistance of LSC grown on YSZ over the same degradation period and a strong increase inthe polarization resistance and in its activation energy was revealed (1.09 to 1.73 eV). The experimental results indicate that sulfur adsorption on LSC surfaces is omnipresent in the investigated conditions and even trace amounts of sulfur compounds present in nominally pure measurement gases account for particle formation and multiple degradation effects under operating conditions.

The electrochemical effects of anisotropic lattice deformation during La_0.6Sr_0.4FeO_3−δgrowth by pulsed laser deposition are investigated byin situimpedance spectroscopy.

Lithium insertion materials are an essential class of mixed ionic and electronic conductors, and their electrochemical properties depend on the resistive and capacitive interplay of ions and electrons. However, complete sets of the corresponding elementary material parameters, that is, composition-dependent ionic and electronic conductivity, chemical capacitance, and charge-transfer resistance, are rarely reported for lithium-ion battery electrode materials. Moreover, the interpretation of these properties from a defect chemical point of view is not very common. In this work, the impedance of sputtered Li1-delta CoO2 thin films is analyzed to extract the fundamental electrochemical properties as a function of state-of-charge (SOC). Within the accessible SOC range, the charge transfer resistance and ionic conductivity vary by more than 1 order of magnitude. The chemical capacitance determined from impedance spectra agrees excellently with the differential capacitance from charge/discharge curves, and, in the dilute regime, even matches the absolute values predicted by defect thermodynamics. The evolution of lithium diffusivity along the charge curve is deconvoluted into the separate contributions of ionic conductivity and chemical capacitance. Finally, we apply the principles of defect chemistry to evaluate the observed trends in terms of lithium activity and point defect concentrations and provide a tentative defect model that is consistent with our results. The consistency of impedance measurements, cycling data, and thermodynamic theory highlights the key role of the chemical capacitance as a powerful material descriptor and emphasizes the relevance of defect chemical concepts for all lithium insertion electrode materials.