Ki-Joong Kim

This is a presentation for the 2026 graphite roundtable meeting. It includes synthesizing highly crystalline graphite from coal via a catalytic graphitization process.

Metal–organic frameworks (MOFs) are a class of highly ordered nanoporous crystals that possess a designable framework and unique chemical versatility. MOF thin films are ideal for nanotechnology-enabling applications, such as optoelectronics, catalytic coatings, and sensing. Mg-MOF-74 has been drawing increasing attention due to its remarkable CO₂ uptake capacity among MOFs and other commonly used CO₂ absorbents. Mg-MOF-74 thin films are currently fabricated by immersing selected substrates in precursor solutions, followed by a traditional solvothermal synthesis process. Herein, we introduce a rapid, easy, and cost-effective synthesis protocol to fabricate MOF thin films in an additive manner. In this work, the controllable synthesis of Mg-MOF-74 thin films directly on optical supports is reported for the first time. Dense, continuous, and uniform Mg-MOF-74 thin films are successfully fabricated on bare glass slides, with an average growth rate of up to 85.3 nm min⁻¹. The structural and optical properties of the resulting Mg-MOF-74 thin films are characterized using X-ray diffraction, atomic force microscopy, scanning electron microscopy, UV-Vis-NIR spectroscopy, and Fourier Transform Infrared Spectroscopy (FTIR). The CO₂ adsorption performance of the resulting Mg-MOF-74 thin films is studied using FTIR for the first time, which demonstrates that, as per the length of the light path for gas absorption, 1 nm Mg-MOF-74 thin film could provide 400.9 ± 18.0 nm absorption length for CO₂, which is achieved via the extraordinary CO₂ adsorption by Mg-MOF-74. The synthesis protocol enables the rapid synthesis of MOF thin films, highlighting Mg-MOF-74 in more CO₂-related applications, such as enhanced CO₂ adsorption and MOF-enhanced infrared gas sensing.

Iron detection is of growing importance in the critical minerals sector, where unwanted iron ions are typically removed during the processing of target critical metals. The ideal sensor should utilize inexpensive, scalable materials along with a low-cost, robust, and easy-to-use analysis platform. Here, we demonstrate a simple acid–base synthesis of luminescent iron-responsive carbon dots by reacting ethanolamine, phosphoric acid, and m-phenylenediamine. The carbon dots exhibit selective, iron-specific emission quenching, with the ability to detect part-per-billion levels of iron ions even in 0.1 M HCl. After benchmarking the purified materials using a commercial spectrometer, a “low-cost” process is demonstrated in which carbon dots with minimal purification are coupled with a portable fiber-optic spectrometer for analyzing iron content. Carbon dot-coated paper strips are also evaluated as another convenient platform for iron analysis. Taken together, the sensing material and platforms demonstrated here are well-suited for detecting trace quantities of iron in environmentally relevant conditions, with potential applications in tracking iron removal processes during critical mineral production as one exciting area of interest.

Synthetic graphite is made predominantly from a petroleum-derived needle coke using the Acheson method. This involves heating the needle coke at elevated temperatures of ~ 3000 °C for more than 7 days. High-temperature heating is the most technically challenging, expensive, and energy-intensive aspect of graphite manufacturing. We will present a strategy for synthesizing high-quality graphite powder from coal using a low-temperature catalytic graphitization process. The use of a catalyst drops the processing temperatures to 1500 °C and processing times to a few hours. The graphite produced with this process has been characterized and has been shown to have comparable physical/chemical properties with commercially sourced graphite materials. We will also present a sustainable method to recover and reuse the catalyst and acid used to retrieve the catalyst. This overcomes a long-standing technical hurdle associated with using catalysts for manufacturing graphite.

Polyethylene (PE) waste is a challenge to upcycle into useful materials because this plastic tends to decompose into volatile compounds when heated at relatively low temperatures. In this work, we report a chemical process that addresses this challenge by converting mixtures of linear low-density polyethylene (LLDPE), low-density polyethylene (LDPE), and high-density polyethylene (HDPE) waste into a hybrid graphitic porous carbon (HGPC) that can be used as a zinc-ion hybrid capacitor cathode. The process uses a low temperature thermal oxidation pre-treatment step, with assistance of an inert solid additive (KCl) to increase the effective surface area of the PE melt, to functionalize, cross-link, and stabilize the PE waste followed by carbonization and catalytic graphitization steps at higher temperatures with a potassium carbonate (K2CO3) catalyst. The PE waste derived HPGC (PW-HPGC) has a hybrid structure composed of graphene-like carbon nanosheets grown on the surface of carbon particles, high porosity with the Brunauer–Emmett–Teller (BET) specific surface area up to 1,763 m2g-1, and good graphitic degree with average Raman I2D/IG ratios of 0.53. When used as a cathode material for zinc-ion hybrid capacitors, this PW-HGPC exhibits an excellent specific capacity up to 126.7 mAhg-1 at high mass loading of 10 mgcm-2. Moreover, PW-HGPC exhibits remarkable cycling stability with capacity retention of >94% after 10,000 cycles at a current density of 2.0 A g-1.

Nitrogen vacancy (NV)-containing nanodiamonds are widely used in quantum sensing applications due to their high sensitivity to magnetic fields, relatively low cost, and ability to be initialized, manipulated, and read out at room temperature. Quantum sensing techniques such as optically detected magnetic resonance (ODMR) and spin relaxometry have exploited the sensitivity of the NV nanodiamonds to magnetic fields to detect a range of analytes, such as pH, metal ions, and biomolecules. However, diversifying the sensing targets accessible by NV diamond quantum sensors typically requires careful engineering of the diamond surface chemistry with stimuli-responsive functional groups. Here, a simple protocol for coating NV nanodiamonds with the zeolitic imidazole framework 8 (ZIF-8), a widely used metal-organic framework, is presented. ZIF-8 is a highly porous material that has been used as a selective sensor for gasses, metal ions, and other analytes. The material is well-characterized by x-ray diffraction, transmission electron microscopy, scanning electron microscopy, x-ray photoelectron spectroscopy, and luminescence spectroscopy. Encapsulation of NV nanodiamonds with a porous scaffold such as ZIF-8 provides a promising method for improving the selectivity for the quantum sensing of various analytes. Importantly, the ZIF-8 coating does not impact the luminescence properties of the NV diamond, which is a key readout in ODMR and spin relaxometry sensing approaches. Indeed, the ODMR spectra with and without the ZIF-8 shell is nearly identical. Moreover, the ZIF-8 coating increases the longitudinal spin relaxation time of the NV nanodiamond by a factor of 4 relative to aggregated diamond, a desirable outcome for spin relaxation-based quantum sensing. Metal-organic framework composites with nanodiamonds thus are an exciting strategy for enhancing NV nanodiamond performance in applications such as quantum sensing and quantum-enhanced nuclear magnetic resonance spectroscopy.

A combination of projected demand increases for economically critical minerals and a monopolistic global marketplace for these minerals has caused concern over supply chain vulnerabilities, which would impact energy, national defense, and advanced technology production. Domestic production of critical minerals is hindered by expensive and non-portable methods for analyzing metal concentration, which is vital both for resource prospecting and process monitoring. Here, a suite of luminescent materials along with portable instrumentation is presented for fluorescence-based detection of trace concentrations of critical minerals (cobalt, rare earth elements, and aluminum) as well as common gangue metals that are removed during processing (iron and aluminum). A metal-organic framework comprised of zinc, adenine, and trimesic acid immobilized on a fiber optic tip is capable of sensing part-per-billion concentrations of terbium, europium, dysprosium, and samarium through a sensitization approach, in which individual elements produce characteristic emission bands enabling multiple rare earths to be simultaneously detected and distinguished. A deep-UV light emitting diode is used as the excitation source, while a portable spectrometer is used to detect the emitted light. A similar optical set-up is coupled with two different carbon dot materials, which can detect low part-per-million concentrations of cobalt and iron in acidic environments. Metal-organic framework thin films comprised of copper and 2-aminoterephthalic acid are used in tandem with a portable optical set-up to further detect aluminum, with successful deployment in real fly ash leachates. Taken together, these technologies provide an inexpensive and sensitive path towards characterizing economically critical metals.

Amine-based sorbents are highly effective for direct air capture (DAC) due to their excellent CO2 capture efficiency under ultra-dilute conditions. However, these sorbents can suffer degradation when exposed to combinations of heat, oxygen, and other atmospheric components, indicating a need for improved sorbent stability. In this study, we developed amidoxime functionalized polymer of intrinsic microporosity (PIM-1-AO) fibers with tethered amines, specifically tris(2-aminoethyl)amine (TAEA) and tris(3-aminopropyl)amine (TAPA), denoted as PIM-1-AO-TAEA and PIM-1-AO-TAPA, respectively. In addition, large scale sorbent fiber spinning has been successfully performed by producing meters of fibers in the lab. We demonstrated that substituting TAEA with TAPA, which has propyl chains instead of ethyl chains, reduces oxidative degradation under regeneration conditions. The findings revealed that PIM-1-AO-TAPA not only significantly outperforms PIM-1-AO-TAEA after accelerated aging process, but also outperforms any other sorbent used in DAC aged under similar conditions. Moreover, PIM-1-AO-TAPA sorbent fibers showed one of the highest amine efficiencies (0.25) considering the low amine loading (21%) coupled with robust CO2 uptake performance (1.12 mmol/g) under DAC conditions.