Mahmoud Sayed

We assessed the effect of non-protein thiols (NPSH), reduced glutathione (GSH) and n-acetylcysteine (NAC), on resin shear bond strength (SBS) to hydrogen peroxide (H₂O₂)-treated dentin, and their effects on the characteristics of dentin in comparison to ascorbic acid (AA) and sodium thiosulfate (STS). H₂O₂-treated dentin was conditioned with 5% AA, GSH, NAC, or STS applied for 1 or 5 min. The positive control group received H₂O₂ without antioxidant application, and the first negative control group received distilled water (DW). The specimens received resin bonding immediately after treatment except for the second negative control group (delayed bonding). Microhardness, roughness, and topography were studied. The SBS values of all antioxidants were statistically greater than the positive control group (p < 0.05); however, NAC and AA applied for 1 min demonstrated the highest values, which were comparable to delayed bonding. All treatments removed the smear layer except DW, H₂O₂, and STS. The negative effect of H₂O₂ on resin–dentin bonding was mitigated by the application of the antioxidants; however, their efficiencies were dependent on the antioxidant type and time of application. NAC was more effective in optimizing resin bonding to bleached dentin compared to GSH at 1 min application and STS at both application times but was comparable to AA. Negligible negative effects on the substrate’s roughness and microhardness were detected. The antioxidant properties of the agent and its capacity to remove the smear layer are the processes underpinning the ability of a certain antioxidant to reverse the effect of H₂O₂ on bonding.

Resin composites are commonly used in pediatric dentistry, but there is limited evidence on adhesion to primary teeth, especially primary enamel. In this study, three bonding strategies were assessed - one-step self-etch (1-SE), two-step self-etch (2-SE), and three-step etch-and-rinse (3-ER) - by measuring the immediate and aged microshear bond strength (µSBS) to sound primary enamel. 120 extracted human primary molars with sound buccal surfaces were used for µSBS testing. Six adhesive protocols (two per bonding strategy) were selected and µSBS was measured either after 24 h or 10,000 thermal cycles (n = 10). Confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM) were used to determine failure modes. Furthermore, 18 primary molars were etched using the different adhesive protocols (n = 3) for the measurement of surface roughness (Sa) using CLSM and morphological analysis using SEM. After 24 h, there was no significant difference in µSBS between 1-SE and 2-SE strategies (p = 0.96), but the 2-SE strategy yielded significantly higher µSBS after thermocycling (p < 0.001). The highest µSBS was obtained using the 3-ER strategy regardless of aging (p < 0.001). The 3-ER strategy clearly exposed enamel prisms and resulted in the highest Sa (p < 0.001). In contrast, if SE strategies were used, enamel prisms were barely recognizable, and Sa was not significantly different from baseline (p > 0.95). The 3-ER strategy is optimal for bonding to primary enamel. The etching effect of SE strategies is weaker, resulting in lower µSBS. Thermocycling revealed that the bonding durability of the 1-SE strategy is inferior to that of to multi-step strategies.

The effect of a surface pre-reacted glass ionomer (S-PRG)-containing sealant on the demineralization inhibition and remineralization of intact enamel adjacent to the sealant material was investigated. BeautiSealant (BTS, S-PRG sealant, Shofu), Teeth Mate F-12.0 (TMF, fluoride-releasing sealant, Kuraray Noritake Dental), and an experimental silica-filler sealant were investigated. After pH cycling for 10 days, the enamel surface adjacent to the sealant material was observed using confocal laser microscopy and scanning electron microscopy. The polymerized sealant disks were immersed in a demineralized solution (pH: 4.3) to measure pH change. The enamel specimens with polymerized sealant disks were additionally immersed in demineralized solution, followed by energy-dispersive X-ray spectroscopy. The demineralized area of BTS was significantly smaller than that of TMF and SS (p < 0.05). The surfaces adjacent to the sealant of TMF and SS were demineralized, while the surface of BTS was comparatively intact. An increase in pH values were observed in the BTS and TMF groups. Enamel surfaces presented an inhibition of demineralization for BTS and TMF, but not for SS. Fluoride uptake from the polymerized sealant was greater for BTS than for TMF. The S-PRG-containing sealant showed a buffering ability, demineralization inhibition, promotion of remineralization, and it can be advised for clinical applications.

Background: Enamel mineral density is dependent on a balanced dynamic process of demineralization and remineralization. Objective: We evaluated the remineralization potential of experimental calcium- containing primer (CaP) application on enamel subsurface lesions. Methods: Demineralized enamel samples obtained from bovine incisor teeth were prepared and cut buccolingually. All samples were divided into 4 main groups according to the type of primer: CLEARFIL SE BOND 2 Primer (SEP), experimental calcium-containing primer (CaP) and bond: CLEARFIL SE BOND 2 Bond (SEB), CLEARFIL Protect Bond (PBB) treatment: (1) SEP-SEB (2) SEP-PBB (3) CaP-SEB (4) CaP-PBB. Each group was subdivided according to storage time in artificial saliva: immediately, 1 month and 6 months. Then, the samples were analyzed using transverse micro radiography (TMR). Additionally, the samples treated with each primer were prepared for scanning electron microscope (SEM) and energy dispersive X-ray spectroscopy (EDS) observation. Two-way ANOVA was used for the statistical analysis of mineral loss (ΔZ: vol%·µm). Results: CaP-PBB had the significantly lowest ΔZ at all storage times, while SEP-SEB had the highest ΔZ (p < 0.05). SEM observations revealed that new crystals were formed on the surface after 6 months, and the ratio of calcium on the enamel increased in the EDS analysis. Conclusion: Experimental calcium-containing primer can provide additional mineral deposition, with even further deposition when combined with a fluoride-containing bond.

This study evaluated the effect of mechanical abrasion on the surface integrity, color change (ΔE) and antibacterial properties of demineralized and sound dentin surfaces treated with silver-diammine-fluoride (SDF). The dentin specimens were divided into two groups: sound and demineralized dentin, then divided into three sub-groups, control (no-treatment), SDF, and SDF + potassium-iodide (KI). Each sub-group was further divided into two groups, one exposed to mechanical brushing and the other without brushing. Specimens were analyzed for the ΔE, surface roughness/surface loss and antibacterial properties (CFU, optical density and fluorescent microscope). Repeated Measures ANOVA was used for statistical analysis of color change while one-way ANOVA was used for CFU analysis. SDF and SDI + KI groups showed significant reduction in ΔE with brushing in the sound dentin group unlike the demineralized group. The surface roughness values were higher for both SDF and SDF + KI groups but roughness values significantly decreased after brushing. Both SDF and SDF + KI groups revealed significantly less surface loss than control. The SDF group showed high anti-bacterial effect after brushing, unlike SDF + KI group. So, we concluded that mechanical brushing improved the esthetic outcome. While, SDF and SDF + KI could protect the dentin surface integrity. SDF-treated dentin possesses an antibacterial property even after mechanical brushing.