Mithilesh Yadav

In this study, novel superabsorbent polymer composites based on natural acacia gum (AG) were synthesized via graft copolymerization of itaconic acid (IA) in the presence of inorganic kaolin powder. The polymerization was initiated by ammonium persulfate (APS) and crosslinked with N,N'-methylenebisacrylamide (N-MBA). Key variables influencing the polymerization process, including the concentrations of KPS, IA, N-MBA and the AG/kaolin weight ratio, were systematically studied to optimize water swelling capacity. The structural characterization of the synthesized composites was performed using FTIR spectroscopy and SEM analysis. The FTIR spectrum revealed a new absorption band at 1671 cm–1, confirming the successful integration of kaolin powder and the formation of inorganic-organic polymer linkages. Additionally, the degree of neutralization was examined, along with the evaluation of critical parameters such as free absorbency capacity, absorbency under load of 16.9 g/g and centrifuge retention capacity of 55.1 g/g. The results demonstrate the potential of these superabsorbent polymer composites for various applications due to their enhanced water absorption properties.

Zirconia and 10%, 20%, and 30% cerium-doped zirconia nanoparticles (ZCO), ZCO-1, ZCO-2, and ZCO-3, respectively, were prepared using auto-combustion method. Binary nanohybrids, ZrO₂@rGO and ZCO-2@rGO (rGO = reduced graphene oxide), and ternary nanohybrids, ZrO₂@rGO@MoS₂ and ZCO-2@rGO@MoS_2, have been prepared with an anticipation of a fruitful synergic effect of rGO, MoS₂, and cerium-doped zirconia on the tribo-activity. Tribo-activity of these additives in paraffin oil (PO) has been assessed by a four-ball lubricant tester at the optimized concentration, 0.125% w/v. The tribo-performance follows the order: ZCO-2@rGO@MoS₂ > ZrO₂@rGO@MoS₂ > ZCO-2@rGO > ZrO₂@rGO > MoS₂ > ZrO₂ > rGO > PO. The nanoparticles acting as spacers control restacking of the nanosheets provided structural augmentation while nanosheets, in turn, prevent agglomeration of the nanoparticles. Doped nanoparticles upgraded the activity by forming defects. Thus, the results acknowledge the synergic effect of cerium-doped zirconia and lamellar nanosheets of rGO and MoS₂. There is noncovalent interaction among all the individuals. Analysis of the morphological features of wear-track carried out by scanning electron microscopy (SEM) and atomic force microscopy (AFM) in PO and its formulations with various additives is consistent with the above sequence. The energy dispersive X-ray (EDX) spectrum of ZCO-2@rGO@MoS₂ indicates the existence of zirconium, cerium, molybdenum, and sulfur on the wear-track, confirming, thereby, the active role played by these elements during tribofilm formation. The X-ray photoelectron spectroscopy (XPS) studies of worn surface reveal that the tribofilm is made up of rGO, zirconia, ceria, and MoS₂ along with Fe₂O₃, MoO₃, and SO₄²⁻ as the outcome of the tribo-chemical reaction.

This paper presents the dielectric characteristics of nanocomposite films of poly(vinyl alcohol) (PVA) embedded with silver (Ag) nanoparticles and graphene oxide(GO). The nanocomposite films were fabricated by using the solvent casting approach. The morphological analysis was carried out through scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The dielectric relaxation behavior of nanocomposite films was analyzed in the frequency range of 10¹ to 10⁶ Hz, by varying GO loading. The temperature effect was investigated over the temperature range of 40 to 150 °C. The effect of ionic liquid (IL) was also explored by comparing the dielectric behavior of films fabricated without using ionic liquid. The conductive filler loading variation showed a significant effect on dielectric permittivity(ε′), complex impedance (Z*) and electric conductivity (σ_ac)_. The obtained results revealed that the dielectric permittivity (ε′) increased by incorporating Ag nanoparticles and increasing GO loading in PVA matrix. An incremental trend in dielectric permittivity was observed on increasing the temperature, which is attributed to tunneling and hopping mechanism. With an increase in nanofiller loading, the real part of impedance (Z′) and imaginary part of impedance (Z″) were found to decrease. Further, the semicircular nature of Nyquist plot indicated the decrease in bulk resistivity on increasing GO loading, temperature and incorporating ionic liquid. On the basis of above findings, the obtained GO-Ag-PVA nanocomposite films can find promising applications in charge storage devices.

In this study, green composite films based on cellulose nanocrystal/chitosan (CNC/CS) were fabricated by solution casting. FTIR, XRD, SEM, and TEM characterizations were conducted to determine the structure and morphology of the prepared films. The addition of only 4 wt.% CNC in the CS film improved the tensile strength and Young’s modulus by up to 39% and 78%, respectively. Depending on CNC content, the moisture absorption decreased by 34.1–24.2% and the water solubility decreased by 35.7–26.5% for the composite films compared with neat CS film. The water vapor permeation decreased from 3.83 × 10⁻¹¹ to 2.41 × 10⁻¹¹ gm⁻¹ s⁻¹Pa⁻¹ in the CS-based films loaded with (0–8 wt.%) CNC. The water and UV barrier properties of the composite films showed better performance than those of neat CS film. Results suggested that CNC/CS nanocomposite films can be used as a sustainable packaging material in the food industry.

Polyamide 6 (PA6)/poly(vinylidene fluoride) (PVDF) blend-based nanocomposites were successfully prepared using a twin screw extruder. Carbon nanotube (CNT) and organo-montmorillonite (30B) were used individually and simultaneously as reinforcing nanofillers for the immiscible PA6/PVDF blend. Scanning electron micrographs showed that adding 30B reduced the dispersed domain size of PVDF in the blend, and CNT played a vital role in the formation of a quasi-co-continuous PA6-PVDF morphology. Transmission electron microscopy observation revealed that both fillers were mainly located in the PA6 matrix phase. X-ray diffraction patterns showed that the presence of 30B facilitated the formation of γ-form PA6 crystals in the composites. Differential scanning calorimetry results indicated that the crystallization temperature of PA6 increased after adding CNT into the blend. The inclusion of 30B retarded PA6 nucleation (γ-form crystals growth) upon crystallization. The Young’s and flexural moduli of the blend increased after adding CNT and/or 30B. 30B exhibited higher enhancing efficiency compared with CNT. The composite with 2 phr 30B exhibited 21% higher Young’s modulus than the blend. Measurements of the rheological properties confirmed the development of a pseudo-network structure in the CNT-loaded composites. Double percolation morphology in the PA6/PVDF blend was achieved with the addition of CNT.

Eco-friendly cellulose nanocrystal/silver/alginate (CNC/Ag/Alg) bionanocomposite films were successfully prepared by blending of CNC with Ag/Alg solution. The CNC was fabricated from cellulose microcrystal (CMC) by acid hydrolysis method. The Ag nanoparticles (AgNPs) were generated by using Alg as a reducing agent through hydrothermal process. AgNPs-included composite films showed characteristic plasmonic effect of the AgNPs with the maximum absorption at 491 nm and they also showed high ultraviolet (UV) barrier properties. The CNC/Ag/Alg composite films were analyzed by using scanning electron microscopy, transmission electron microscopy, optical microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction technique. Depending on the type of nanofillers, tensile strength of the composite films increased by 39–57% and water vapor permeation decreased by 17–36% compared with those of the neat Alg films. The Ag/Alg and CNC/Ag/Alg films showed brown color as detected from the increase of both ‘b’ and ‘a’ parameters by colorimeter. The UV and water barrier properties of Alg based composite films were found higher than the Alg films. The obtained results suggested that the prepared composite films can be used in food packaging applications.

In this study, a graphene nanoplatelet (GNP) was used as a reinforcing filler to prepare poly(vinylidene fluoride) (PVDF)/high density polyethylene (HDPE) blend-based nanocomposites through a melt mixing method. Scanning electron microscopy confirmed that the GNP was mainly distributed within the PVDF matrix phase. X-ray diffraction analysis showed that PVDF and HDPE retained their crystal structure in the blend and composites. Thermogravimetric analysis showed that the addition of GNP enhanced the thermal stability of the blend, which was more evident in a nitrogen environment than in an air environment. Differential scanning calorimetry results showed that GNP facilitated the nucleation of PVDF and HDPE in the composites upon crystallization. The activation energy for non-isothermal crystallization of PVDF increased with increasing GNP loading in the composites. The Avrami n values ranged from 1.9–3.8 for isothermal crystallization of PVDF in different samples. The Young’s and flexural moduli of the blend improved by more than 20% at 2 phr GNP loading in the composites. The measured rheological properties confirmed the formation of a pseudo-network structure of GNP-PVDF in the composites. The electrical resistivity of the blend reduced by three orders at a 3-phr GNP loading. The PVDF/HDPE blend and composites showed interesting application prospects for electromechanical devices and capacitors.