Perovskite solar cells (PSCs) have great potentials in photovoltaics due to their high power conversion efficiency and low processing cost. PSCs are usually fabricated from PbI2/dimethylformamide solution with some toxic additives, such as N-methyl pyrrolidone and hexamethylphosphoramide. Here, we use an environmental friendly aprotic polar solvent, 1,3-dimethyl-2-imidazolidinone (DMI), to fabricate perovskite films. By adding 10 vol% DMI in the precursor solution, high-quality perovskite films with smooth surface are obtained. By increasing annealing temperature from 100 to 130 °C, the average grain size of the perovskite increases from ~ 216 to 375 nm. As a result, the efficiency of the PSCs increases from 10.72 to 14.54%.

Flexible heterojunction solar cells were fabricated from carbon nanotubes (CNTs) and mono-crystalline Si thin films at room temperature. The Si thin films with thickness less than 50 μm are prepared by chemically etching Si wafer in a KOH solution. The initial efficiency of the thin-film solar cell varies from approximately 3% to 5%. After doping with a few drops of 1 M HNO3, the efficiency increases to 6% with a short-circuit current density of 16.8 mA/cm2 and a fill factor of 71.5%. The performance of the solar cells depends on the surface state and thickness of Si thin films, as well as the interface of CNT/Si. The flexible CNT/Si thin-film solar cells exhibit good stability in bending-recovery cycles.