Xiaolong Wang
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Research Subjects
Xiaolong Wang has a total of 5 co-authors. Here are the top co-authors by number of shared publications:
- Bo Liang
State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China
1 shared publication - Hongli Zhao
State Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China
1 shared publication - Jingkai Yang
State Key Laboratory of Metastable Materials Science and Technology, Hebei Key Laboratory of Nano-Biotechnology, Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004, China
1 shared publication - Qingyin Di
State Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China
1 shared publication - Xuan Wang
State Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China
1 shared publication
Latest Publications
- Open Access
Mutual Effects of Fluorine Dopant and Oxygen Vacancies on Structural and Luminescence Characteristics of F Doped SnO2 Nanoparticles
SnO2 and F doped SnO2 (FTO) nanoparticles (NPs) have been synthesized by the hydrothermal method with subsequent annealing at 500 °C. The microstructure and photoluminescence (PL) property of SnO2 and FTO NPs have been investigated, and an assumption model about the luminescence process of FTO NPs has been proposed. All of the SnO2 and FTO NPs possess polycrystalline tetragonal rutile structures, and the average size in the range of 16.5–20.2 nm decreases with the increasing of F doping content. The doping element F is shown a uniformly distribution by electron energy loss spectroscopy (EELS) mapping. The oxygen vacancy concentration becomes higher as is verified by Raman and X-ray photoelectron spectra (XPS). There are three kinds of oxygen chemical states in SnO2 and FTO NPs, in which Oα corresponds to oxygen vacancies. The room temperature PL position is observed to be independent of F doping content. F− may substitute O2− into the SnO2 lattice by generating and one extra e−, which can combine with or to generate or to ensure charge balance.Open AccessMutual Effects of Fluorine Dopant and Oxygen Vacancies on Structural and Luminescence Characteristics of F Doped SnO2 Nanoparticles
SnO2 and F doped SnO2 (FTO) nanoparticles (NPs) have been synthesized by the hydrothermal method with subsequent annealing at 500 °C. The microstructure and photoluminescence (PL) property of SnO2 and FTO NPs have been investigated, and an assumption model about the luminescence process of FTO NPs has been proposed. All of the SnO2 and FTO NPs possess polycrystalline tetragonal rutile structures, and the average size in the range of 16.5–20.2 nm decreases with the increasing of F doping content. The doping element F is shown a uniformly distribution by electron energy loss spectroscopy (EELS) mapping. The oxygen vacancy concentration becomes higher as is verified by Raman and X-ray photoelectron spectra (XPS). There are three kinds of oxygen chemical states in SnO2 and FTO NPs, in which Oα corresponds to oxygen vacancies. The room temperature PL position is observed to be independent of F doping content. F− may substitute O2− into the SnO2 lattice by generating and one extra e−, which can combine with or to generate or to ensure charge balance.