Wetting behavior of molten metals on solid substrates is a critical phenomenon influencing numerous industrial applications, including welding, anti-corrosion coatings, and metal additive manufacturing (AM). In particular, molten metal jetting (MMJ), an emerging AM technology, requires that the molten metal remain pinned at the nozzle exit. Thus, each new metal requires a specific nozzle material to ensure consistent droplet ejection and deposition, making it important to rapidly identify the appropriate wetting combinations. However, traditional measurements of wetting angles require expensive equipment and only allow one combination of materials to be investigated at a time which can be time consuming. This work introduces a rapid screening method based on sessile droplet experiments to evaluate wetting profiles across multiple metal–substrate combinations simultaneously. This study investigates the wetting interactions of molten Al alloy (Al4008), Cu, and Sn on various ceramic and metal substrates to identify optimal material combinations for MMJ nozzle designs. Results demonstrate that Al4008 achieves wetting on ceramic substrates such as AlN, TiO₂, and SiC, with varying mechanisms including chemical reactions and weak surface interactions. Additionally, theoretical predictions regarding miscibility gaps and melting point differences were verified for Cu and Sn on refractory metals like Mo and W. Findings from this study contribute to the establishment of a materials compatibility library, enabling the selection of wetting/non-wetting combinations for stable MMJ operation. This resource not only advances MMJ technologies but also provides valuable insights for broader applications such as welding, coating, and printed electronics.

Here the discovery of refractory multi-principal element alloys (MPEAs) with high-temperature strength and stability is pursued within a constrained and application-relevant design space. A comprehensive approach is developed and applied to explore all 165 ternary systems in the Al-Ce-Fe-Hf-Mo-Nb-Ta-Ti-V-W-Zr family. A subset of ternary systems that contain large areas in composition–temperature space with high strength and robust BCC phase stability is found. Twelve sets of high-performing alloys are identified, each set optimized for one combination of phase constraint, optimization target, and temperature range. Preliminary mechanical tests support the viability of the method. This work highlights the importance of considering phase stability, exploring non-equiatomic regions of composition space, and applying application-relevant constraints. Parts I and II provide three down-selection techniques for identifying high-performing BCC refractory MPEAs, design guidelines, and many candidates predicted to have BCC phase stability and strengths 2–3 times higher than any reported to date.