Gaoyang Liu

Proton exchange membrane water electrolysis (PEMWE) is a green hydrogen production technology with great development prospects. As an important part of PEMWE, bipolar plates (BPs) play an important role and put forward special requirements due to the harsh environments on both the anode and cathode. Recently, metal-based BPs, particularly stainless steel and titanium BPs have attracted much attention from researchers all over the world because of their advantages of high corrosion resistance, low resistivity, high thermal conductivity, and low permeability. However, these metallic BPs are still prone to being oxidized and are facing with hydrogen embrittlement problems in the PEMWE working environment, which would result in reduced output power and premature failure of the PEMWE stack. In order to reduce the corrosion rate and maintain low interfacial contact resistance, the surface modification of the metallic BPs with protective coatings, such as precious metals (e.g., Au, Pt, etc.) and metal nitrides/carbides, etc., have been extensively investigated. However, the above-mentioned coating materials are restricted by the high-cost materials, complex equipment, and the complicated operation process. In this review, the surface modification of metallic BPs based on silane treatment, conductive polymers, e.g., polyaniline (PANI) and polypyrrole (PPy) as well as some nanoparticles-promoted polymer hybrid coatings which have been investigated for PEMWE, are summarized and reviewed. As for the silane treatment, the dense silane can not only effectively enhance the corrosion resistance but also improve the adhesion between the substrate and the conductive polymers. As for PANI and PPy, the typical value of corrosion current density of a PANI coating is 5.9 μA cm⁻², which is significantly lower than 25.68 μA cm⁻² of the bare metal plate. The introduction of nanosized conductive particles in PANI can further reduce the corrosion current density to 0.15 μA cm⁻². However, further improvement in the electrical conductivity is still desired to decrease the interface contact resistance (ICR) to be lower than 10 mΩ cm². In addition, serious peeling off of the coating during long-term operation also needs to be solved. Typically, the conductive polymer reinforced by graphene, noble metals, and their compounds in the form of nanoparticle-promoted polymer hybrid coatings could be a good choice to obtain higher corrosion resistance, durability, and conductivity and to extend the service life of PEMWE. Especially, nanoparticle-promoted polymer hybrid coatings consisting of polymers and conductive noble metals or nitrides/carbides can be controlled to balance the conductivity and mechanical properties. Due to the advantages of a simple preparation process, low cost, and large-scale production, nanoparticle-promoted polymer hybrid coatings have gradually become a research hotspot. This review is believed to enrich the knowledge of the large-scale preparation process and applications of BPs for PEMWE.

The membrane electrode assembly (MEA) is the core component of proton exchange membrane (PEM) water electrolysis cell, which provides a place for water decomposition to generate hydrogen and oxygen. The microstructure, thickness, IrO₂ loading as well as the uniformity and quality of the anodic catalyst layer (ACL) have great influence on the performance of PEM water electrolysis cell. Aiming at providing an effective and low-cost fabrication method for MEA, the purpose of this work is to optimize the catalyst ink formulation and achieve the ink properties required to form an adherent and continuous layer with doctor blade coating method. The ink formulation (e.g., isopropanol/H₂O of solvents and solids content) were adjusted, and the doctor blade thickness was optimized. The porous structure and the thickness of the doctor blade coating ACL were further confirmed with the in-plane and the cross-sectional SEM analyses. Finally, the effect of the ink formulation and the doctor blade thickness of the ACL on the cell performance were characterized in a PEM electrolyzer under ambient pressure at 80 °C. Overall, the optimized doctor blade coating ACL showed comparable performance to that prepared with the spraying method. It is proved that the doctor blade coating is capable of high-uniformity coating.

The liquid and gas diffusion layer is a key component of proton exchange membrane water electrolyzer (PEMWE), and its interfacial contact resistance (ICR) and corrosion resistance have a great impact on the performance and durability of PEMWE. In this work, a novel hybrid coating with Au contacts discontinuously embedded in a titanium oxidized layer was constructed on a Ti felt via facile electrochemical metallizing and followed by a pre-oxidization process. The physicochemical characterizations, such as scanning electron microscopy, energy dispersive spectrometer, and X-ray diffraction results confirmed that the distribution and morphology of the Au contacts could be regulated with the electrical pulse time, and a hybrid coating (Au-TiO₂/Ti) was eventually achieved after the long-term stability test under anode environment. At the compaction force of 140 N cm⁻², the ICR was reduced from 19.7 mΩ cm² of the P-Ti to 4.2 mΩ cm² of the Au-TiO₂/Ti. The corrosion current density at 1.8 V (RHE) is 0.689 μA cm⁻². Both the ICR and corrosion resistance results showed that the prepared protective coating could provide comparable ICR and corrosion resistance to a dense Au coating.

Proton exchange membrane fuel cells (PEMFCs) are the most promising clean energy source in the 21st century. In order to achieve a high power density, electrocatalytic performance, and electrochemical stability, an ordered array structure membrane electrode is highly desired. In this paper, a new porous Pt-TiO₂@C ordered integrated electrode was prepared and applied to the cathode of a PEMFC. The utilization of the TiO₂@C support can significantly decrease the loss of catalyst caused by the oxidation of the carbon from the conventional carbon layer due to the strong interaction of TiO₂ and C. Furthermore, the thin carbon layer coated on TiO₂ provides the rich active sites for the Pt growth, and the ordered support and catalyst structure reduces the mass transport resistance and improves the stability of the electrode. Due to its unique structural characteristics, the ordered porous Pt-TiO₂@C array structure shows an excellent catalytic activity and improved Pt utilization. In addition, the as-developed porous ordered structure exhibits superior stability after 3000 cycles of accelerated durability test, which reveals an electrochemical surface area decay of less than 30%, considerably lower than that (i.e., 80%) observed for the commercial Pt/C.