Wendong Song

Mangroves are highly productive blue carbon ecosystems that preserve high organic carbon concentrations in soils. In this study, particle size, bulk elemental composition and stable carbon isotope were determined for the sediment cores collected from the landward and seaward sides of two mangrove forests of different ages (M1, ca. 60; M2, ca. 4 years old) to determine the effects of geomorphic setting and age (L1 = old mangrove and S1 = salt marsh stand in M1; L2 = young mangrove and S2 = bare mudflat in M2) on sediments and organic carbon accumulation. The objective of this study was to determine the feasibility of the northernmost human-planted mangroves in China to accumulate sediment and carbon. Our results showed that fine-grained materials were preserved well in the interior part of the mangroves, and the capacity to capture fine-grained materials increased as the forest aged. The biogeochemical properties (C/N: 5.9 to 10.8; δ¹³C: −21.60‰ to −26.07‰) indicated that the local organic carbon pool was composed of a mixture of autochthonous and allochthonous sources. Moreover, the accumulation of organic carbon increased with the forest age. The interior part of the old mangrove had the highest organic carbon stock (81.93 Mg C_org ha⁻¹). These findings revealed that mangrove reforestation had positive effects on sediments and organic carbon accretion.

The preparation process of metalocking key from 304 stainless steel was studied, and the mechanical properties of raw materials and metalocking key were studied. It is found that after this preparation process, the hardness of metalocking key increases by more than 20%, the tensile strength increases by more than 50%, the yield strength increases by more than 120%, and the elastic limit increases by more than 50%. Finally, scanning electron microscope (SEM) element analysis and metallography were used to characterize the microstructure analysis. It indicated that much of the austenitic stainless steel is converted to martensite due to cold rolling, which led to the significant strengthening of metalocking key properties.

In this study, mangrove seedlings Kandelia obovata were firstly introduced to Zhoushan in Eastern China at 29° 93′ N from Xuwen in South China at 20° 34′ N in April 2016. In order to analyze ecophysiological differences of K. obovata seedlings domesticated in Zhoushan, the growth status and antioxidant system of K. obovata exposed to natural low temperature were studied through situ measurements. The results showed that K. obovata seedlings introduced artificially to Zhoushan grew slowly when subjected to natural cold stress. The chlorophyll contents exhibited a decreased tendency. In addition, 2-butanol and 2,3-butanediol were firstly found in K. obovata after being moved to Zhoushan, which are specific substances produced by K. obovata under low-temperature stress. Moreover, there was a synergistic competition mechanism in the antioxidant enzyme system in K. obovata, in which superoxide dismutase (SOD) would convert oxygen radicals to hydrogen peroxide, and then catalase (CAT) and peroxidase (POD) could work together to remove hydrogen peroxide. This study provides a foundation for better understanding of the response of mangroves to natural low temperature at high latitudes.

In this study, modified activated fishbone charcoal (MAFC) was successfully prepared to remove emulsified oil from oily wastewater. Various characteristic techniques, including SEM, XRD, FTIR, and BET, were employed to investigate the morphology, texture, and surface properties of as-prepared samples. BET results demonstrated that the specific surface area of fishbone charcoal increased from 69.8 m²/g to 206.0 m²/g after treatment with K₂CO₃ as an activating agent, while the total pore volume of MAFC increased from 0.003 cm³/g to 0.3 cm³/g, accompanied by the formation of abundant pore structures. It was observed that 90.1% of emulsified oil (100 mg/L) was successfully removed by MAFC under our experimental conditions. The results of a kinetic and isotherm model analysis indicated that the adsorption experimental data were not only consistent with the Langmuir adsorption isotherm but were also well-described by the pseudo-second-order adsorption model. It is expected that this highly efficient and inexpensive MAFC can be a promising bio-adsorbent for removing organic pollutants from industrial wastewater.

The aim of this study was to optimize the adsorption performance of activated carbon (AC), derived from the shell of Penaeus vannamei prawns, on heavy metal ions. Inexpensive, non-toxic, and renewable prawn shells were subjected to carbonization and, subsequently, KOH-activation to produce nanoporous K-Ac. Carbonized prawn shells (CPS) and nanoporous KOH-activated carbon (K-Ac) from prawn shells were prepared and characterized by FTIR, XRD, BET, SEM, and TEM. The results showed that as-produced K-Ac samples were a porous material with microporous and mesoporous structures and had a high specific surface area of 3160 m²/g, average pore size of about 10 nm, and large pore volume of 2.38 m³/g. Furthermore, batches of K-Ac samples were employed for testing the adsorption behavior of Cd²⁺ in solution. The effects of pH value, initial concentration, and adsorption time on Cd²⁺ were systematically investigated. Kinetics and isotherm model analysis of the adsorption of Cd²⁺ on K-Ac showed that experimental data were not only consistent with the Langmuir adsorption isotherm, but also well-described by the quasi-first-order model. Finally, the adsorption behaviors of as-prepared K-Ac were also tested in a ternary mixture of heavy metal ions Cu²⁺, Cr⁶⁺, and Cd²⁺, and the total adsorption amount of 560 mg/g was obtained.

This study, for the first time, rendered crab shell activated biochar modified by potassium hydroxide (KOH) impregnation (CSAB), revealing a new potential application in the removal of diesel oil from oily wastewater. The structural characteristics of crab shell biochar (CSB) and CSAB were investigated by SEM, and the crystal structure and optical properties of as-prepared samples were analyzed using XRD and FTIR. Results showed that CSAB had stratified surface structure morphology, abundant functional groups, and that its high specific surface area could reach up to 2441 m²/g, which was about eight times larger than that of untreated CSB (307 m²/g). An adsorption isotherm study indicated that the actual adsorption process both of CSAB and CSB were found to fit better with the Freundlich equation. Moreover, chemical interaction controlled the adsorption kinetics efficiency while the adsorption equilibrium capacity was 93.9 mg/g. Due to its highly developed pore structure, unique surface characteristics, and effective adsorption performance, this low-cost activated carbon had the potential to serve as an efficient adsorbent for water pollution purification.

With the vigorous advancement of global economic integration, The international trade in goods has become busier and busier, and the maritime industry has been booming. The number of ships has increased greatly, and the discharge of ships has become an important factor affecting the environment. For the international maritime organization (IMO) has decided to implement 0.5% of global sulfur restrictions by 2020, Zhejiang free trade zone has been paying attention to the dynamic and development trend of sulfur emission in the global shipping industry. And the obstacles to the bonded oil supply business of Zhoushan free trade zone in the low sulfur era are deeply thought and analyzed. The paper focuses on three main countermeasures and analyzes the advantages and disadvantages of these three countermeasures. It is hoped that the plan selection of future ships to deal with sulfur emission limit will be helpful.

Biomass is known to efficiently adsorb pollutants from wastewater. In this paper, we demonstrated that a new antistatic oil-cleaning material can be prepared and assembled by using two surfactants, alkyl polyglucosides (APG) and dimethyl octadecyl hydroxy ethyl ammonium nitrate (SN), to modify calcined mussel shell powder (CMSP) through a two-step hydrotherm-assisted adsorption. The pore size and structure of CMSP was measured by BET and a contact angle meter was used to characterize the surface wetting ability. XRD, FTIR, XPS, SEM, TEM, and HRTEM were employed to determine the surface structure of CMSP modified by surfactants APG and SN (MMO). In order to further characterize properties of the surface morphology and crystal structure, the HRTEM was employed to show that the MMO surface had a single crystal structure: calcite, with a crystal plane spacing of 0.2467 nm. The surface of MMO appeared to be fluffy and disperse. The antistatic and degreasing ability of as-prepared samples (MMO) was evaluated by a ZC-36 high resistance meter and BD-457 whiteness meter. The results showed that when the calcination temperature of CMSP reached 1000 °C, and the addition amount of APG and SN was 0.8 g and 0.16 g, it had an optimum antistatic effect with a surface resistivity (R_s) of 1.35 × 10⁸ Ω, and a detergency rate to oil of 17.35%. This study aims to embrace a green solution to reduce environmental pressure and make use of waste, which is of great significance to environmental protection.

In this work, a new nano-Bi₂MoO₆/diatomite composite photocatalyst was successfully synthesized by a facile solvothermal method. Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and UV-vis diffuse reflection spectroscopy (DRS) were employed to investigate the morphology, crystal structure, and optical properties. It was shown that nanometer-scaled Bi₂MoO₆ crystals were well-deposited on the surface of Bi₂MoO₆/diatomite. The photocatalytic activity of the obtained samples was evaluated by the degradation of rhodamine B (RhB) under the visible light (λ > 420 nm) irradiation. Moreover, trapping experiments were performed to investigate the possible photocatalytic reaction mechanism. The results showed that the nano-Bi₂MoO₆/diatomite composite with the mass ratio of Bi₂MoO₆ to diatomaceous earth of 70% exhibited the highest activity, and the RhB degradation efficiency reached 97.6% within 60 min. The main active species were revealed to be h⁺ and•O²⁻. As a photocatalytic reactor, its recycling performance showed a good stability and reusability. This new composite photocatalyst material holds great promise in the engineering field for the environmental remediation.