Truan-Sheng Lui

When hot forging 7075 aluminum alloy, as a military material durable enough for most of its applications, it needs to be heat-treated to ensure the target material property achieves the application requirements. However, the material properties change because of heat throughout usage. In this study, a new approach was devised to heat treat the alloy to prevent material property changes. The study further clarified the effect of rapid heat treatment on the high-temperature resistance of a hot forging 7075 aluminum alloy. Infrared (IR) heat treatment was used as a rapid heating technique to effectively replace the conventional resistance heat (RH) treatment method. Our experimental result showed that IR heat treatment resulted in better age hardening at the initial aging stage, where its tensile strength and elongation appeared like that of a resistance heat treatment. More so, based on hardness and tensile test results, the IR-heated treatment process inhibited the phase transformation of precipitations at a higher temperature, improving high-temperature softening resistance and enhancing the thermal stability of the hot forging 7075 aluminum alloy.

We used selective laser melting (SLM) Inconel 718 (coded AS) to carry out three heat treatment processes: (1) double aging (coded A), (2) solid solution + A (coded SA), (3) homogenization + SA (coded HSA) in order to investigate the effects of microstructure changes and tensile strength enhancement on erosion resistance. The as-SLM IN718 and three heat-treated specimens were subjected to clarify the effects of erosion-induced phase transformation on tensile mechanical properties. All heat-treated specimens showed better erosion resistance than as-SLM IN718 did at all impact angles. The as-SLM IN718 and the three heat-treated specimens produced new γ′ phase or metal-oxide via particle erosion, which increased the surface hardness of the material. The thickness of the erosion affected zone is 200 μm, which is the main cause of tensile embrittlement.

In this study, powder bed fusion Ti-6Al-4V alloy flake was subjected to heat treatment at 800 °C for 4 h for inducing the complete transformation of the α’ phase into the α+β phases. An erosion experiment with 450 µm mean particle diameter of Al₂O₃ particles at a 90° impact on both the as- powder bed fusion (PBF) Ti-6Al-4V and the 4-h 800 °C heat-treated specimens to clarify the particle erosion-induced phase transformation behavior and its effect on mechanical properties. Particle erosion-induced phase transformation to the α phase was observed on both the as-PBF Ti-6Al-4V and the heat-treated specimens. It brought about a sequential formation from the surface to the bottom: (1) a surface softened zone, (2) a hardened zone, and (3) a hardness stabilization zone. The as-PBF Ti-6Al-4V was positively eroded by erosion particles, decreasing strength and ductility. In the case of the heat-treated specimens, we found decreased strength yet an increased ductility.

In this study, selective laser melting (SLM) Ti-6Al-4V is subjected to heat treatment for 4 h at 400 °C, 600 °C, and 800 °C, followed by air cooling. After heat treatment at 400 °C and 600 °C, the ductility was lower (strength increased). This was could be for two reasons: (1) high temperature tensile properties, and (2) particle erosion wear induced phase transformation. Finally, the particle erosion rates of as-SLM Ti-6Al-4V and heat treatment for 4 h at 800 °C (labeled 800-AC) were investigated and compared; the lamellar α + β phases in 800-AC are difficult to destroy with erosion particles, resulting in the erosion resistance of 800-AC being higher than that of the martensitic α’ needles in the as-SLM Ti-6Al-4V at all impact angles (even the hardness of the 800-AC specimen was lower). The as-SLM Ti-6Al-4V alloy needs heat treatment to have better wear resistance.

The ductility enhancement of an AA7075 aluminum alloy aided by a friction stir process (FSP) and various heat treatments was investigated and compared in terms of outcome with full annealing (O). The results indicate that a big improvement in the tensile ductility was achieved by freezing the sample at temperatures below 0 °C after the solution treatment and water quenching (W treatment), and further improvement could be acquired via a friction stir process due to grain refinement (40%) were at least 1.5-fold greater than that of the annealed alloy. In addition, serrated flow could be observed in the tensile flow curves, and both the Piobert–Lüders effect and the Portevin–LeChatelier (PL) effect could be observed. The enhancement in the tensile ductility was examined in terms of the existence of intermetallic particles and the supersaturated concentration of the solid solution.

The grain size of high strength 7075 hot-rolled aluminum plates was refined by a friction stir process (FSP) to improve their mechanical properties. The results of the tensile ductility tests, which were conducted at various tool rotational speeds, in the friction stir zone indicate significant tensile ductility loss, which even resulted in a ductile-to-brittle transition (DBT). DBT depends on the tool rotational speed. Our 1450 rpm specimens showed large data fluctuation in the tensile ductility and the location of the fracture controlled the formation of friction stir induced bands (FSIB). The crack initiation site located at FSIB was due to the tool rotational speed (1670 rpm). A higher heat-input causes the formation of FSIB, which is accompanied with micro-voids. This contributes significantly to tensile cracking within the stir zone after the application of the aging treatment. This investigation aimed to determine the dominant factor causing tensile ductility loss at the stir zone, which is the major restriction preventing further applications.

This present study applied Cu∙Zn/Al ribbon in place of a traditional Cu ribbon to a photovoltaic (PV) ribbon. A hot-dipped and an electroplated Sn PV ribbon reflowed onto an Ag electrode on a Si solar cell and estimated the feasibility of the tested module (Ag/Solder/Cu∙Zn/Al). After bias-aging, a bias-induced thermal diffusion and an electromigration promoted the growth of intermetallic compounds (IMCs) (Cu₆Sn₅, Ag₃Sn). To simulate a photo-generated current in the series connection of solar cells, an electron with Ag-direction (electron flows from Ag to Al) and Al-direction (electron flows from Al to Ag) was passed through the Al/Zn∙Cu/Solder/Ag structure to clarify the growth mechanism of IMCs. An increase in resistance of the Ag-direction-biased module was higher than that of the Al-direction biased one due to the intense growth of Cu₆Sn₅ and Ag₃Sn IMCs. The coated solder of the electroplated PV ribbon was less than that of the hot-dipped one, and thus decreased the growth reaction of IMCs and the cost of PV ribbon.

This study was conducted for high temperature aging (HTA) to simultaneously reduce current treatment time and increase the tensile ductility of 7075 aluminum alloy. Various high temperatures and different durations for artificial aging were compared. We investigated the microstructure and the tensile properties of 7075 aluminum alloy extruded rod after various HTAs, and compared them with the outcomes of full annealing (O). The total elongation (TE) of the specimen after solution heat treatment (490 °C, 1 h) and artificial aging (280 °C, 12 h) was about 25%. For full annealing, it is known as 21%. The reason for this was the formation of the η phase in the matrix, which had fewer large particles (Al-Cu phase). The hardening of HTA specimens is higher than that of O, indicating necking resistance during homogeneous plastic deformation. Thereby, HTA treatment increases the formability of 7075 aluminum alloy.

Post-forging heat treatment is often necessary to achieve the mechanical properties required for aluminum alloy forged parts. In this study, hot-forged 6082 suspension parts are used to study the effect of rapid infrared (IR) heat treatment. The insoluble particles present in the matrix after the solutionizing process are observed. Experimental results show that using rapid IR heat treatment leads to superior solutionizing, and thus a larger critical onset strain in serrated tensile flow. The rapid IR heat treatment also had a more significant precipitation effect, which enhanced the mechanical properties of the material.

To avoid the phenomenon of abnormal grain coarsening, and increase the Young’s modulus of forgings, an infrared heat treatment was used on different mass forgings and compared with the results of an air furnace heat treatment. This work focused on the effects of microstructural evolution and the mechanical properties of two different mass 6082 real forgings. The experimental results show that infrared heat treatment can effectively reduce the mass effect after heat treatment, inhibit the coarse grains formed, and keep the non-equiaxed grains along the metal flows, thus significantly improving the ductility of the material. In addition, the rapid heating characteristic of infrared can effectively shorten the duration of heat treatment and greatly enhance the Young’s modulus and the vibration resistance of 6082 entity forgings.