Zhuo Qin
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Research Subjects
Zhuo Qin has a total of 6 co-authors. Here are the top co-authors by number of shared publications:
- Changqing Zhang
State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metal, Lanzhou University of Technology, Lanzhou 730050, China
2 shared publications - Chen Rong
School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
2 shared publications - Shuwen Wang
School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
1 shared publication - Weijie Wang
School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
1 shared publication - Wenchen Shi
School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
1 shared publication - Xin Jin
School of Material Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
1 shared publication
Latest Publications
- Open Access
The Preliminary Exploration of Micro-Friction Stir Welding Process and Material Flow of Copper and Brass Ultra-Thin Sheets
In the friction stir welding (FSW) of ultra-thin dissimilar metal sheets, different physical material properties, the reduction of plastic metal in the weld zone, and insufficient plastic metal flow lead to poor weld seam shapes and joint qualities. Therefore, it is necessary to study the flow behavior during the FSW of ultrathin sheets. In this study, micro friction stir welding (μFSW) was conducted and analyzed for the butt welding of 0.6-mm-thick ultrathin brass (H62-H) and pure copper (T2-Y) sheets. By analyzing the electric signals of the temperature and force during the welding process, testing the mechanical properties, and analyzing the metallography of the joint, the influences of the process parameters on the metal flow behavior during μFSW were studied. In the proper process conditions, the material preferentially migrated and concentric vortex flow occurred in the vicinity of the shoulder and tool pin action areas. The copper was pushed from the retreating side (RS) to the advancing side (AS) of the weld, allowing it to flow more fully. A mixture of both materials formed at the bottom of the weld nugget, and less migration occurred in the heat-affected zone of the AS at this time. The highest tensile strength can reach 194 MPa, accounting for 82.6% of the copper. The presence of brittle phases Cu5Zn8, AgZn3 and AgZn caused the hardness to fluctuate slightly.
Open AccessThe Preliminary Exploration of Micro-Friction Stir Welding Process and Material Flow of Copper and Brass Ultra-Thin Sheets
In the friction stir welding (FSW) of ultra-thin dissimilar metal sheets, different physical material properties, the reduction of plastic metal in the weld zone, and insufficient plastic metal flow lead to poor weld seam shapes and joint qualities. Therefore, it is necessary to study the flow behavior during the FSW of ultrathin sheets. In this study, micro friction stir welding (μFSW) was conducted and analyzed for the butt welding of 0.6-mm-thick ultrathin brass (H62-H) and pure copper (T2-Y) sheets. By analyzing the electric signals of the temperature and force during the welding process, testing the mechanical properties, and analyzing the metallography of the joint, the influences of the process parameters on the metal flow behavior during μFSW were studied. In the proper process conditions, the material preferentially migrated and concentric vortex flow occurred in the vicinity of the shoulder and tool pin action areas. The copper was pushed from the retreating side (RS) to the advancing side (AS) of the weld, allowing it to flow more fully. A mixture of both materials formed at the bottom of the weld nugget, and less migration occurred in the heat-affected zone of the AS at this time. The highest tensile strength can reach 194 MPa, accounting for 82.6% of the copper. The presence of brittle phases Cu5Zn8, AgZn3 and AgZn caused the hardness to fluctuate slightly.
- Open Access
A Study on Microstructure and Mechanical Properties of Micro Friction Stir Welded Ultra-Thin Al-1060 Sheets by the Shoulderless Tool
The welding tool is the key of micro friction stir welding (μFSW), which affects the heat input and the plastic forming of weld metal. In this paper, 0.8-mm-thick ultra-thin 1060-H24 aluminum sheets μFSW butt joints were used to compare and analyze the influence of the conventional tool and shoulderless tool on weld shaping, microstructure and mechanical properties. Besides, by measuring the axial force, transverse force and weld temperature in μFSW process, the influence of these two different tools on the heat input and metal flow mechanism of the weld were analyzed. The results show that the weld generated by the shoulderless tool has narrower width, less heat input and metal involved in plastic forming resulting in smaller HAZ (heat affected zone). The hardness of NZ (nugget zone) is obviously increased compared with that of the base metal. The highest tensile strength can reach 108.6 MPa, accounting for 78.6% of the base metal and 117.3% of the joint by the conventional tool. But the welding defects have to be overcome for industrial application of the shoulderless tool.
Open AccessA Study on Microstructure and Mechanical Properties of Micro Friction Stir Welded Ultra-Thin Al-1060 Sheets by the Shoulderless Tool
The welding tool is the key of micro friction stir welding (μFSW), which affects the heat input and the plastic forming of weld metal. In this paper, 0.8-mm-thick ultra-thin 1060-H24 aluminum sheets μFSW butt joints were used to compare and analyze the influence of the conventional tool and shoulderless tool on weld shaping, microstructure and mechanical properties. Besides, by measuring the axial force, transverse force and weld temperature in μFSW process, the influence of these two different tools on the heat input and metal flow mechanism of the weld were analyzed. The results show that the weld generated by the shoulderless tool has narrower width, less heat input and metal involved in plastic forming resulting in smaller HAZ (heat affected zone). The hardness of NZ (nugget zone) is obviously increased compared with that of the base metal. The highest tensile strength can reach 108.6 MPa, accounting for 78.6% of the base metal and 117.3% of the joint by the conventional tool. But the welding defects have to be overcome for industrial application of the shoulderless tool.