In order to gain a knowledge of the heat emitted from a variety of sources at the blind heading of an underground gold mine, the present study conducts an in situ measurement study in a blind heading within the load haul dumps (LHDs) that are operating. The measurements can provide a reliable data basis for the setting of numerical simulations. The results demonstrate that the distances between the forcing outlet and the mining face (denoted as Z_m), as well as the heat generation from LHDs (denoted as Q_L), has brought significant impacts on the airflow velocity, relative humidity, and temperature distributions in the blind heading. Setting Z_m to 5 m could achieve a relative optimal cooling performance, also indicating that when the LHD is fully operating in the mining face, employing the pure forcing system has a limited effect on the temperature decrease of the blind heading. According to the numerical simulations, a better cooling performance can be achieved based on the near-forcing-far-exhausting (NFFE) ventilation system.

In view of the accidents such as rock mass breakage, roof fall and coal slide in coal mines, polyurethane/mesoscopic fly ash (PU/MFA) reinforcement materials were produced from polymethylene polyphenylene isocyanate (PAPI), the polyether polyol, flame retardant, and MFA using stannous octanate as a catalyst. 3-Glycidoxypropyltrimethoxysilane (GPTMS) was grafted on MFA surface, aiming to improve the mechanical properties of PU/MFA composites. The analyses of infrared spectroscopy and compression resistance reveal that the GPTMS can be successfully attached to the surface of MFA, and the optimum modification dosage of GPTMS to MFA is 2.5 wt. % (weight percent). On this basis, the effect of GPTMS on the mechanical properties of PU/MFA reinforcement materials during the curing process was systematically investigated through a compression test, a fracture toughness test, a three-point bending test, a bond property test, and a dynamic mechanics analysis. The results show that the compression property, fracture toughness, maximum flexural strength, and bond strength of PU/MFA composites increase by 21.6%, 10.1%, 8.8%, and 19.3%, respectively, compared with the values before the modification. Furthermore, the analyses of scanning electron microscope and dynamic mechanics suggest that the coupling agent GPTMS can successfully improve the mechanical properties of PU/MFA composites because it eliminates the stress concentration and exerts a positive effect on the crosslink density and hardness of PU/MFA composites.