George J. Nelson

Degradation of low cobalt lithium-ion cathodes was tested using a full factorial combination of upper cut-off voltage (4.0 V and 4.3V vs. Li/Li⁺) and operating temperature (25°C and 60°C). Half-cell batteries were analyzed with electrochemical and microstructural characterization methods. Electrochemical performance was assessed with galvanostatic cycling, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS) supported by distribution of relaxation times (DRT) analysis. Electrode microstructure was characterized with scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray absorption near edge structure (XANES) imaging. Higher cut-off voltage cycling shows presence of NiO_x formation, a low diffusivity rock-salt phase, in both CV and XRD data. XRD patterns confirmed that the rock-salt phase was beginning to form at the low cut-off voltage at high temperature, but in much lower intensity than at the high cut-off voltage. Higher temperature accelerates degradation processes at both voltages. Degradation factors at high temperature include NiOx formation, cathode material dissolution, and electrolyte decomposition. SEM analysis suggests that supporting phases may isolate and disconnect active material particles reducing capacity retention and battery life cycle. DRT analysis and XANES imaging show that both high temperature samples revealed a NiO_x phase based on an increased diffusive impedance and a visible shift in the XANES spectra. The low cut-off voltage, high temperature sample showed a split peak and shift to lower energies indicating early formation of the NiO_x phase. The diffusive impedance, which hinders intercalation and deintercalation, is driven by the formation of the NiO_x phase. While primarily driven by cut-off voltage, elevated temperature also contributes to this degradation mechanism.

Our previous work on an air-cooled stack of five pouch-format lithium-ion (Li-ion) cells showed that non-uniform temperature can cause accelerated degradation, especially of the middle cell. In this work, a stack of five similar cells was cycled at a higher C-rate and water-cooled to create a larger temperature gradient for comparison with the air-cooled stack. It was hypothesized that the larger temperature gradient in the water-cooled stack would exacerbate the degradation of the middle cell. However, the results showed that the middle cell degraded slightly slower than the side cells in the water-cooled stack. This trend is opposite to that in the air-cooled stack. This difference could be attributed to the combined effects of a smaller temperature rise and larger temperature gradient in the water-cooled stack than in the air-cooled stack. Post-mortem analysis of cycled cells and a fresh cell showed that the degradation mainly came from the anode. Increased lithium plating and decreased porosity in the side cells are possible mechanisms for the faster degradation compared with the middle cell. It was also found that all the cells in the water-cooled stack experienced a phenomenon of capacity drop and recovery after a low C-rate reference performance test and extended rest. This phenomenon can be attributed to lithium diffusion between the anode active area and the anode overhang area.

The Oak Ridge National Laboratory is planning to build the Second Target Station (STS) at the Spallation Neutron Source (SNS). STS will host a suite of novel instruments that complement the First Target Station’s beamline capabilities by offering an increased flux for cold neutrons and a broader wavelength bandwidth. A novel neutron imaging beamline, named the Complex, Unique, and Powerful Imaging Instrument for Dynamics (CUPI2D), is among the first eight instruments that will be commissioned at STS as part of the construction project. CUPI2D is designed for a broad range of neutron imaging scientific applications, such as energy storage and conversion (batteries and fuel cells), materials science and engineering (additive manufacturing, superalloys, and archaeometry), nuclear materials (novel cladding materials, nuclear fuel, and moderators), cementitious materials, biology/medical/dental applications (regenerative medicine and cancer), and life sciences (plant–soil interactions and nutrient dynamics). The innovation of this instrument lies in the utilization of a high flux of wavelength-separated cold neutrons to perform real time in situ neutron grating interferometry and Bragg edge imaging—with a wavelength resolution of δλ/λ ≈ 0.3%—simultaneously when required, across a broad range of length and time scales. This manuscript briefly describes the science enabled at CUPI2D based on its unique capabilities. The preliminary beamline performance, a design concept, and future development requirements are also presented.

Increasing electrode thickness can increase the energy density of lithium-ion batteries. However, increasing electrode thickness increases transport limitations and the risk of lithium plating. This work analyzes prospective improvements to the conventional lithium-ion cell that may facilitate high energy density and fast charging capabilities. A 2D lithium-ion battery model is applied to understand the impact of thick electrode at different C-rates in a single cell stack. Five different cell geometries were analyzed for this work: one conventional cell and four test cases in which the conventional electrode geometries were modified by adding electrolyte channels to increase the rate transfer capability of lithium ions at high C-rates and reduce the risk of lithium plating. All five configurations were simulated in discharge at C/10, C/2, and 1 C followed by simulated charging at 1 C, 3 C, and 5 C with no rest period prior to charge. The addition of electrolyte channels in the anode only results in improved performance with respect to reduced plating risk. Dimensionless parameter analysis was performed to compare the battery performance with different electrode modifications at different C-rates. Scaling behavior based on these parameters clarifies the benefits and limitations of the varied electrode modification approaches.

Electrochemical changes were successfully monitored through the coupling of external loading, electrochemical impedance spectroscopy (EIS), and distribution of relaxation times (DRT) analysis. The development of the testing methods allows for detailed observation of changes due to mechanical loading and distinguishes responses between different cell geometries. Comparison of the force vs displacement, voltage vs displacement, and distribution of relaxation times plots to the different cell geometries display failure modes specific to geometry as well as the impact of different loading profiles. Numerical modeling confirmed the movement within individual cells and predicted locations with the most deformation based on the external loading condition applied. The results gathered from combining mechanical loading, electrochemical response, and numerical modeling, yield a viable approach to establishing an improved understanding of the effects of mechanical loading on the electrochemical response of multiple battery geometries and the methods herein may be extensible to additional battery chemistries.

Sodium-ion batteries have emerged as a strong contender among the beyond lithium-ion chemistries due to elemental abundance and the low cost of sodium. Tin (Sn) is a promising alloying electrode with high capacity, redox reversibility, and earth abundance. Tin electrodes, however, undergo a series of intermediate reactions exhibiting multiple voltage plateaus upon sodiation/desodiation. Phase transformations related to incomplete sodiation in tin during cycling, in the presence of a frail solid electrolyte interphase layer, can quickly weaken the structural stability. The structural dynamics and reactivity of the electrode/electrolyte interface, being further dependent on the size and morphology of the active material particle in the presence of different electrolytes, dictate the electrode degradation and survivability during cycling. In this study, we paint a comprehensive picture of the underpinnings of the electrochemical and mechanics coupling and electrode/electrolyte interfacial interactions in alloying Sn electrodes. We elicit the fundamental role of electrode/electrolyte complexations in the Sn electrode structure-property-performance relationship based on multimodal analytics, including electrochemical, microscopy, and tomography analyses.

High-capacity electrochemical alloying materials, such as tin and tin-based alloys, present an opportunity for the advancement of lithium-ion batteries. However, the destructive effects of volumetric expansion must be mitigated in order to sustain this high capacity during extended cycling. One way to mitigate these effects is by alloying Sn with more malleable metals to accommodate the strain related to severe volumetric expansion. Ex situ X-ray microtomography data of cycled Cu₆Sn₅ pellets were used to quantify the microstructural changes that occur during lithiation and delithiation. The microtomography data were segmented into three distinct phases to evaluate phase size distributions, specific surface area, and tortuosity. Electrodes lithiated and then delithiated showed the most substantial reduction in overall phase sizes. This suggests that full lithiation of the Sn followed by partial delithiation of the Li_4.4Sn to Li₂CuSn can cause substantial microstructural changes related to volume expansion on lithiation and structural collapse upon delithiation. When considering other microstructural characteristics, this subset of the electrodes analyzed showed the highest tortuosity values. These results show that in addition to the mechanical degradation of the electrodes, excessive volume expansion can also influence transport networks in the active material and supporting phases of the electrode. While based on studies of the active–inactive alloy Cu₆Sn₅ for lithium-ion battery applications, the insights obtained are expected to be applicable to other alloy electrodes and battery chemistries.