NH₄V₄O₁₀ nanobelts were synthesized and decorated into TiN nanotube arrays as supercapacitor electrode with a specific capacitance of 749.0 F g⁻¹ at 5 mV s⁻¹ and a capacity retention of 85.7% after 200 cycles.

Hierarchical TiN nanotube mesh (HTNM) is prepared by calcining TiO₂ nanotube mesh (TONM) in NH₃ flow where the TONM is fabricated by electrochemical anodic oxidation of Ti mesh. Calcining temperature affects not only phase composition but also morphology of the HTNM, which further affects its optical absorption and solar water evaporation conversion efficiency (η). The η can reach to 85.36% under 2.5 kW m⁻² simulated solar irradiation because HTNM efficiently utilizes solar light. Moreover, it can be reutilized because of its stabilities of the phase composition and nanostructure during the measurements of solar water evaporation performance.

BiFeO₃ thin films with a mixture of tunable R-like and c axis elongated low symmetry phase (T-like phase) are fabricated on STO (001) substrate through controlling of the substrate temperature. Almost pure T-like phase can be grown on STO substrate at 600°C. Comparing with the situations on LAO (001), it is found that, strains from the LAO substrate may be the only reason that induces the T-like phase at higher temperatures. At lower temperatures, the island growth induced strains alone can also generate T-like phase on STO substrate.