Mohammad A. Al-Saleh

This study investigated the comparative effects of various maleic anhydride-grafted polymeric compatibilizers such as polyethylene-graft-maleic anhydride, polypropylene-graft-maleic anhydride, polyethylene(alt)-graft-maleic anhydride and poly(styrene-ethylene/butylene-styrene)-graft-maleic anhydride on the final properties of polypropylene (PP) carbon nanotube (CNT) composites. Polypropylene nanocomposites (PP-CNT) were prepared by melt mixing using a laboratory scale twin-screw extruder. The mechanical test results showed that the incorporation of CNTs along with various compatibilizers increased the tensile strength (10.3%) and tensile modulus (24.2%). The tensile modulus and yield stress of the PP-CNT nanocomposites were significantly higher than those of the pristine PP. Differential Scanning Calorimetry (DSC) analysis revealed that the addition of CNTs slightly increased the melting temperature of the crystallization peaks. In the compatibilized PP-CNT composites, the CNTs were well dispersed to enhance the onset of degradation and maximum decomposition temperatures. The frequency-dependent rheological behaviors of PP-CNT nanocomposites indicated that the storage modulus (G′), loss modulus (G″), and complex viscosity (η*) PP increased for the compatibilized system. The XRD results indicated that the addition of CNTs and compatibilizers slightly affected the crystalline nature of PP. Scanning electron microscopic images of the fractured surfaces presented in the micrographs showed the brittle nature of the surface morphology of PP-CNT nanocomposites.

In this research work, graphene nanoplatelets (GNP) were selected as alternative reinforcing nanofillers to enhance the properties of polypropylene (PP) using different compatibilizers called polypropylene grafted maleic anhydride (PP-g-MA) and ethylene-octene elastomer grafted maleic anhydride (POE-g-MA). A twin screw extruder was used to compound PP, GNP, and either the PP-g-MA or POE-g-MA compatibilizer. The effect of GNP loading on mechanical and thermal properties of neat PP was investigated. Furthermore, the influence and performance of different compatibilizers on the final properties, such as mechanical and thermal, were discussed and reported. Tensile, flexural, impact, melting temperature, crystallization temperature, and thermal stability were evaluated by using a universal testing system, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). For mechanical properties, it was found that increasing GNP content from 1 wt.% to 5 wt.% increased tensile strength of the neat PP up to 4 MPa. The influence of compatibilizers on the mechanical properties had been discussed and reported. For instance, the addition of PP-g-MA compatibilizer improved tensile strength of neat PP with GNP loading. However, the addition of compatibilizer POE-g-MA slightly decreased the tensile strength of neat PP. A similar trend of behavior was observed for flexural strength. For thermal properties, it was found that both GNP loading and compatibilizers have no significant influence on both crystallization and melting temperature of neat PP. For thermal stability, however, it was found that increasing the GNP loading had a significant influence on improving the thermal behavior of neat PP. Furthermore, the addition of compatibilizers into the PP/GNP nanocomposite had slightly improved the thermal stability of neat PP.

The methodology to study an eco-friendly and non-toxic, Schizophyllan, biopolymer for enhanced oil recovery (EOR) polymer flooding is described. The methodology is divided into two parts; the first part estimates the molar concentration of the biopolymer, which is needed to prepare the biopolymer solution with optimal viscosity. This is required to improve the sweep efficiency for the selected reservoir in Kuwait. The second part of this generalized methodology evaluates the biopolymer solution capability to resist degradation and maintain its essential properties with the selected reservoir conditions. The evaluation process includes thermal and mechanical assessment. Furthermore, to study the biopolymer solution behavior in both selected reservoir and extreme conditions, the biopolymer solution samples were prepared using 180 g/L and 309 g/L brine. It was found that the prepared biopolymer solution demonstrated great capability in maintaining its properties; and therefore, can be introduced as a strong candidate for EOR polymer flooding with high salinity brines.