Zhang Yuan

Various welding positions need be used in laser welding of structures with complex configurations. Therefore, it is necessary to gain knowledge of how the welding positions can influence the keyhole and weld pool behavior in order to better control the laser weld quality. In the present study, a computational fluid mechanics (CFD) model was constructed to simulate the laser-welding process of the titanium alloy Ti6Al4V, with which the keyhole stability and the fluid flow characteristics in weld pool were studied for four welding positions, i.e., flat welding, horizontal welding, vertical-up welding, and vertical-down welding. Results showed that the stability of the keyhole was the best in flat welding, the worst in horizontal welding, and moderate in vertical welding positions. Increasing heat input (the ratio of laser power to welding speed) could increase the keyhole stability. When the small heat input was used, the dimensions and flow patterns of weld pools were similar for different welding positions. When the heat input was increased, the weld pool size was increased, and the fluid flow in the weld pool became turbulent. The influences of gravity became significant when a large heat input was used, especially for laser welding with vertical positions. Too high a heat input in vertical-up laser welding would lead to oscillation and separation of molten metal around the keyhole, and in turn result in burn-through holes in the laser weld. Based on the present study, moderate heat input was suggested in positional laser welding to generate a stable keyhole and, meanwhile, to guarantee good weld quality.

To obtain satisfactory welds in positional laser beam welding, it is necessary to know how process parameters will influence the quality of welds in different welding positions. In this study, the titanium alloy Ti6Al4V sheets were laser welded in two vertical welding positions (vertical up and vertical down), and the appearance, porosity, strength, and ductility of the laser joints were evaluated. Results show that undercuts of the vertical up welds were greater than that of vertical down welds, while the porosity contents were much higher in vertical down welds than that in vertical up welds. When welding with a higher heat input, the vertical up welding position resulted in poor weld profiles (undercuts and burn-through holes), whereas the vertical down welding position led to excessive porosity contents in welds. Both severe undercut and excessive porosity were detrimental to the tensile properties of the welds. Weld appearance was improved and porosity contents were reduced by using a lower heat input, achieving better weld quality. Therefore, it is suggested that process parameter settings with relatively high laser powers and welding speeds, which can result in lower heat inputs, are used when laser welding the Ti6Al4V titanium alloys vertically.

Laser welding has been increasingly utilized to manufacture a variety of components thanks to its high quality and speed. For components with complex shapes, the welding position needs be continuously adjusted during laser welding, which makes it necessary to know the effects of the welding position on the quality of the laser welds. In this paper, the weld quality under two (flat and horizontal) welding positions were studied comparatively in the laser welding of Ti6Al4V titanium alloy, in terms of weld profiles, process porosity, and static tensile strengths. Results show that the flat welding position led to better weld profiles, less process porosity than that of the horizontal welding position, which resulted from the different actions of gravity on the molten weld metals and the different escape routes for pores under different welding positions. Although undercuts showed no association with the fracture positions and tensile strengths of the welds, too much porosity in horizontal laser welds led to significant decreases in the strengths and specific elongations of welds. Higher laser powers and travel speeds were recommended, for both flat and horizontal welding positions, to reduce weld porosity and improve mechanical properties.