Yajing Wang

In this paper, Moso bamboo (Phyllostachys heterocycle) before and after heat treatment were used as raw materials to prepare transparent bamboo (TB). In an acidic environment, the lignin contained in the bamboo material was removed to obtain a bamboo template, and an epoxy resin similar to the cellulose refractive index was used for vacuum impregnation into the bamboo template to obtain a transparent bamboo material. The purpose of this study was to compare the physical and chemical properties of TB and original bamboo and the differences between TBs before and after heat treatment, taken from different parts of bamboo, in order to explore the performance advantages and disadvantages of TB as a new material. The Fourier transform infrared spectroscopy analysis (FTIR), scanning electron microscope testing (SEM), three elements analysis, light transmittance testing, and mechanical strength testing were used to study the molecular composition, microstructure, chemical composition, light transmittance, and tensile strength of the TB samples. The results showed that the lignin content of the delignified bamboo templates was greatly reduced. In addition, the SEM images showed that a large amount of epoxy resin (type E51 and type B210 curing agent) was covered on the cross-section surface and pores of the TB samples. The FTIR showed that the epoxy molecular groups appeared on the TB, and the delignified bamboo template and the resin had a good synergy effect. According to the light transmittance testing, the original bamboo samples hardly contained light transmittance under visible light. The transmittance of transparent inner bamboo (TIB) and transparent heat-treated inner bamboo (THIB) could reach about 11%, and the transmittance of transparent outer bamboo (TOB) and transparent heat-treated outer bamboo (THOB) was about 2%. The light transmittance had been significantly improved when compared with the original bamboo samples. The transmittances of the TB samples before and after heat treatment in different parts of bamboo were different. In the visible light irradiation range, the light transmittances of TB samples were as follows: TIB > THIB and THOB > TOB. Meanwhile, the tensile strength of TB was reduced, especially for TOB and THOB. In addition, TB has a wide range of raw materials, and the preparation process is environmentally friendly. It can be used for decorative materials in homes, buildings, etc., and has a great application potential.

Two common tree species of Betula alnoides (Betula) and New Zealand pine (Pinups radiata D. Don) were selected as the raw materials to prepare for the partially transparent wood (TW) in this study. Although the sample is transparent in a broad sense, it has color and pattern, so it is not absolutely colorless and transparent, and is therefore called partially transparent. For ease of interpretation, the following “partially transparent wood” is referred to as “transparent wood (TW)”. The wood template (FW) was prepared by removing part of the lignin with the acid delignification method, and then the transparent wood was obtained by impregnating the wood template with a refractive-index-matched resin. The goal of this study is to achieve transparency of the wood (the light transmittance of the prepared transparent wood should be improved as much as possible) by exploring the partial delignification process of different tree species on the basis of retaining the aesthetics, texture and mechanical strength of the original wood. Therefore, in the process of removing partial lignin by the acid delignification method, the orthogonal test method was used to explore the better process conditions for the preparation of transparent wood. The tests of color difference, light transmittance, porosity, microstructure, chemical groups, mechanical strength were carried out on the wood templates and transparent wood under different experimental conditions. In addition, through the three major elements (lignin, cellulose, hemicellulose) test and orthogonal range analysis method, the influence of each process factor on the lignin removal of each tree species was obtained. It was finally obtained that the two tree species acquired the highest light transmittance at the experimental level 9 (process parameters: NaClO₂ concentration 1 wt%, 90 °C, 1.5 h); and the transparent wood retained most of the color and texture of the original wood under partial delignification up to 4.84–11.07%, while the mechanical strength with 57.76% improved and light transmittance with 14.14% higher than these properties of the original wood at most. In addition, the wood template and resin have a good synergy effect from multifaceted analysis, which showed that this kind of transparent wood has the potential to become the functional decorative material.

The waterborne coating uses water as its solvent, which will partially dissolve wood extractives when it is applied to wood surfaces. This influences both the coating curing process and the mechanical properties of the cured coating. To investigate these influences, the mechanical properties of waterborne polyacrylic coating on control and extractive-free wood surfaces were investigated by nanoindentation. Reductions to elastic modulus (E_r) and hardness (H) of the coating layer was observed in the wood cell walls adjacent to or away from coating layers. Extraction treatment resulted in significant decrease of the E_r and H of the coating layer on extractive-free wood surface comparing with control wood, but the values slightly increased for extractive-free wood cell walls compared to a control. E_r and H of coating in wood cell lumen were higher than the average value of coating layer on wood surface in both the control and extractive-free wood. The E_r of wood cell wall without coating filled in lumen was significantly higher than those of filling with coating. However, there was no distinct difference of H. The E_r and H of CCML in extractive-free wood were 15% and 6% lower than those in control ones, respectively.