Fengxiang Chen

Carbon nanotubes (CNTs) are promising candidates for numerous cutting-edge fields because of their excellent properties. However, the inherent black color of CNTs cannot satisfy the aesthetic/fashion requirement, and the flammability of CNTs severely restricts their application in high-temperature environments with oxygen. Here, we realized a structural coloration of CNTs by coating them with amorphous TiO ₂ layers. By tuning the TiO ₂ coating thickness, both CNT fibers and membranes exhibited controllable and brilliant colors, which exhibited remarkable superdurability that could endure 2000 cycles of laundering tests and more than 10 months of high-intensity ultraviolet irradiation. The TiO ₂ -coated CNTs exhibited a notable fire-retardant performance and could endure 8 hours of fire burning. The structural coloration of CNTs with excellent fire retardance substantially improves their performance and broadens their applications.

Aramid fibers are widely used in many cutting‐edge fields, including space, aviation, military, and electronics. However, their poor UV resistance and surface inertness seriously hinder their utilization, especially in harsh environments. Here, a dual‐layer ultrathin Al₂O₃–TiO₂ coating with a thickness of 70–180 nm is fabricated on aramid fibers by a modified atomic layer deposition (ALD) method. The tenacity of ALD‐coated aramid fibers decreases only by ≈0.85% after exposure to intense UV light (4260 W m⁻²) under high temperature (>200 ℃) for 90 min, which equals to continuous exposure to sunlight for about 17 500 days. The as‐prepared aramid fibers also show excellent laundering durability, thermal and chemical stabilities. This work presents a green and damage‐free approach to achieve the highly anti‐UV aramid fibers without sacrificing their outstanding performance, which is expected to guide material design for future innovations in functional fibers and devices.

As the most favored high-quality biopolymer, silk fiber is widely used in the textile and medical industries owing to its impressive mechanical properties, wear comfort properties, and biocompatibility. However, its photo-instability, chemical instability, and thermal instability seriously hinder its utilization in luxurious fashionable apparels. Therefore, we herein report the preparation of an ultra-thin and uniform TiO2-Al2O3 cloth with a thickness of just six thousandths that of fiber on silk-worm silk fiber via atomic layer deposition. In this ultra-thin composite cloth, the outer TiO2 layer acts as a sacrificial ultraviolet (UV) absorbent to dissipate large amounts of UV energy. Free radicals and electrons generated by the TiO2 layer are effectively blocked outside the surface of the bulk silk fiber by the inner insulating Al2O3 layer. The excellent UV-resistance of the modified silk fiber was confirmed by a lack of fade in the silk fabric after exposure to UV light for 60 min (equal to continuous exposure to strong sunlight for 3285 d). Compared with silk fiber, the tenacity of the prepared SF-200Al2O3-800TiO2 increased by 18.9% even after sunlight exposure. In addition, both the chemical and thermal stabilities of the modified silk fiber were improved. This technology is expected to have potential applications in various fields, such as high-end fabric development and smart materials, and will further guide material design for future innovations in functional fibers and devices.