Paolo Posa

Directed Energy Deposition Laser Beam (DED-LB) is a promising additive manufacturing technique that uses a laser source and a powder stream to build or repair metal components. Repair applications offer significant economic and environmental benefits but are more challenging to develop, especially for components that are difficult to process due to their intricate geometries and materials. Process conditions can change precipitously, and it is essential to implement monitoring systems that ensure high process stability and, consequently, superior end-product quality. In the present work, a mid-wave infrared coaxial camera was used to monitor the melt pool geometry. To simulate the challenging repair process conditions of the DED-LB process, experimental tests were carried out on substrates with different thicknesses. The stability of the deposition process on nickel-based superalloys was analyzed by means of MATLAB algorithms. Thus, the effect of open-loop and closed-loop monitoring with back control on laser power on the process conditions was assessed and quantified. Metallographic analysis of the produced samples was carried out to validate the analyses performed by the monitoring system. The occurrence of production defects (lack of fusion and porosity) related to parameters not directly controllable by monitoring systems, such as penetration depth and dilution, was determined.

The main objective of this study is to evaluate residual stresses in AISI 316L and 18Ni Maraging 300 functionally graded materials with continuous variation of composition within a single layer using the contour method. The manufacture of this kind of layer-level continuous functionally graded materials by employing a Powder Bed Fusion-Laser Beam system utilizing a blade/roller-based powder spreading technique has only been recently devised and a proper residual stress analysis is still required. In fact, as the mechanical properties of additively manufactured samples are significantly influenced by the direction of construction, the same holds true for the direction along which the compositional variation is made. Furthermore, in this study, the impact of solution annealing and aging heat treatment, which are necessary for enhancing the mechanical properties of martensitic steel, on residual stresses was explored. Additionally, the effect of adopting material-differentiated process parameters was investigated. The results indicated that each specimen displayed areas of tensile stress concentration on the upper and lower surfaces, balanced by compression in the center. The application of heat treatment led to a decrease in the maximum tensile stress of 8% and provided a uniform and significant stress reduction within the maraging steel. Finally, the implementation of material-specific process parameters for the three composition zones in conjunction with the heat treatment resulted in a reduction in the maximum residual stress of 35% and also a significantly lower residual stress field throughout the specimen.

In this work, a systematic study was conducted on the fabrication of multi-material components obtained employing Laser-Powder Bed Fusion (L-PBF) technology. The idea of making multi-material components is a winning capability of additive technologies because it allows for the fabrication of Functionally Graded Materials (FGMs) with the customization of parts according to different required properties. This study aims to determine the ability of an inexpensive system, adaptable to the L-PBF machines already on the market, with a powder-spreading technique based on coaters or rollers, to produce parts with continuously variable properties in each layer. Also, the correlation between certain selectable factors in the production design and the result obtained in terms of metallurgical and mechanical properties and chemical composition was investigated. The factors studied were the relative position of the different materials within the powder chamber and the geometry of the equipment designed to produce the cFGMs components. The performed tests involved the use of two materials, a nickel-based superalloy, and a stainless steel, having different chemical, physical, and mechanical properties to obtain gradual property variations in the manufactured samples. Based on the results of post-process characterization obtained via metallographic, chemical, and mechanical analysis, the relative positions of the materials and the geometry of the developed equipment have a limited effect on the sample’s manufactured properties. The characteristics of the FGM zone depend on the nature of the employed powders, and its extent coincides with that defined during the design of the divider.

In this work, a systematic study was conducted on the fabrication of multi-material components obtained employing Laser-Powder Bed Fusion (L-PBF) technology. The idea of making multi-material components is a winning capability of additive technologies because it allows the fabrication of Functionally Graded Materials (FGMs) with the customization of parts according to different required properties. The transition from one material to another was achieved gradually and continuously within the same layer using ad-hoc equipment designed for L-PBF systems with a powder spreading technique based on coaters or rollers. The influence of the relative position of the different materials within the powder chamber and the geometry of the developed equipment on the metallurgical and mechanical properties of the manufactured samples was evaluated. The performed tests involved the use of two materials, a nickel-based superalloy, and a stainless steel, having different chemical, physical and mechanical properties to obtain gradual properties variation in the manufactured samples. Based on the results of post-process characterization obtained through metallographic, chemical, and mechanical analysis, the relative positions of the materials and the geometry of the developed equipment have a limited effect on the sample’s manufactured properties. The characteristics of the FGM zone depend on the nature of the employed powders, and its extent coincides with that defined during the design of the divider.

The capabilities of additive manufacturing (AM) techniques have been extensively examined in the literature. However, scientific gaps persist on the feasibility of realizing a coated component manufactured by using various materials processed by combining different AM processes. From this perspective, this study focuses on the manufacturing of a directed energy deposition (DED) coating by using 18Ni (300) maraging steel powder on AISI 316L components realized by laser-powder bed fusion (L-PBF), in order to assess the production of components with high geometrical complexity combined with high mechanical surface properties in selected areas. The quality of the manufactured coatings was assessed in-process through the implementation of an optical monitoring system and real-time image processing. In addition, an in-depth metallurgical analysis (microstructural and chemical) of the interface between the DED coating and the L-PBF component was carried out. Finally, hardness tests were performed on both the as-deposited and heat-treated coatings to confirm the high mechanical performance of the final component surface. The results revealed the potential of producing cost-effective and geometrically complex parts, such as molds or tools with internal cooling channels, that implement mechanically high-performance surfaces.

The selective laser melting process is a growing technology for the manufacture of parts with very complex geometry. However, not all materials are suitable for this process, involving rapid localized melting and solidification. Tungsten has difficulties due to the high melting temperature. This study focuses on the possibility of processing a WC/Co/Cr composite powder using selective laser melting. Samples were fabricated and characterized in terms of density, defects, microstructure and hardness. Tests were conducted with hatch spacing of 120 μm and process speed of 40 mm/s. A constant laser power of 100 W and a powder layer thickness of 30 μm were used. A relative density of 97.53%, and therefore a low porosity, was obtained at an energy density of 12.5 J/mm². Microscopic examination revealed the presence of small cracks and a very heterogeneous distribution of the grain size.