In this work, 2‐(6‐oxido‐6H‐dibenzoxaphosphorin‐6‐yl)‐methanol (ODOPM) was synthesized, and covalently introduced into vinyl ester resin (VER) by combining with 4,4′‐diphenylmethane diisocyanate (MDI). The influences of ODOPM and MDI on the thermal properties, flame retardancy, and flame‐retardant mode‐of‐action of the resin were investigated. When the phosphorus addition reaches 1.3 wt%, the limiting oxygen index (LOI) of VER/ODOPM‐1.3 boosts to 30.3% and vertical burning (UL‐94) rating increases to V‐0. Compared with the virgin VER, the peak heat release rate (PHRR) and total heat release (THR) of VER/ODOPM‐1.3 are significantly reduced by 64.2% and 35.1%, respectively. The introduction of ODOPM and MDI significantly enhances the flame retardancy of VER. ODOPM and MDI are chemically linked to the polymer network of VER, which increases the glass transition temperature (T_g) and rigidity. This work offers a facile method for improving both thermal and flame‐retardant properties of vinyl ester resin.

This work reported a flame‐retardant, single‐component epoxy resin (EP) via introducing diphenylphosphine (DPP) and benzimidazolyl‐substituted cyclotriphosphazene (BICP) into EP. The differential scanning calorimetry (DSC) test showed that the onset curing temperature of DPP/BICP‐15/10 was 50°C lower than that of BICP‐12 due to the catalytic decomposition effect of DPP toward BICP under heating. Besides, the shelf life of DPP/BICP‐15/10 at room temperature reached ~14 days, demonstrating good storage stability. EP/DPP/BICP maintained satisfactory thermal properties and showed excellent flame retardancy with a UL‐94V‐0 classification. Compared with the unmodified EP sample, the peak heat release rate (PHRR) and total heat release (THR) of DPP/BICP‐15/13 were decreased by ~68.1% and ~55.1%, respectively. Hence, this flame‐retardant, single‐component epoxy resin with satisfactory comprehensive properties exhibited great potential for versatile industrial applications.