Maddury Somayazulu

Anomalous lattice expansion of bcc Ta is observed in helium-loaded diamond anvil cell (DAC) experiments near 6 GPa and above 400 K, while co-loaded W, Mo, and Au exhibit normal thermal expansion. The Ta volume expansion increases with temperature, reaching ∼13% near 650 K before plateauing, and is largely retained after recovery to ambient conditions. Time-resolved measurements at 500 K reveal progressive expansion over several hours, consistent with gradual, thermally activated He incorporation. The largely retained expansion during subsequent cooling and holding at 400 K indicates that the incorporated He is predominantly kinetically trapped. The data reveal two distinct regimes: below ∼550 K, modest and spatially uniform expansion consistent with interstitial He trapping at isolated, randomly distributed vacancies; above ∼550 K, He-vacancy cluster growth producing dramatically larger expansion, peak broadening, and a core–shell microstructure revealed by micrometer-resolution x-ray diffraction mapping. These results demonstrate that He is not always a passive pressure medium in DAC experiments and reveal a previously unrecognized regime of He-mediated lattice modification in Ta, complementing conventional ion-implantation studies relevant to nuclear and fusion structural materials.

In laser-heated diamond anvil cell (DAC) experiments, the effective heated region typically decreases in size with increasing pressure, leading to steeper thermal gradients. Under these conditions, chromatic aberration in the optical path from sample to detector can significantly create bias in spectro-radiometric temperature measurement. We present a radiance-mapping approach using a hyperspectral camera that records 25 spectral channels spanning 605–875 nm at each pixel in a single exposure, providing spatially and spectrally resolved radiance in each frame. This enables chromatic effects to be recorded and corrected in data processing. We developed a procedure for hyperspectral mapping, involving per-camera calibration, crosstalk removal, measured spectral throughput functions, and optional sub-pixel co-registration to minimize chromatic distortion. The calibrated radiance maps are then used to derive temperature maps of the laser-heated hotspots. For smaller heating spots, the radiance mapping approach reveals chromatic shifts that conventional spectro-radiometric methods cannot quantify. Ambient-pressure heating experiments confirm accurate temperature retrieval. At high pressure, application of the hyperspectral system to a platinum-heating experiment at 12 GPa demonstrates stable temperature reconstruction under steep thermal gradients. Beyond mitigating chromatic aberrations, the ability to diagnose optical artifacts separately from emissivity variations during controlled test experiments or in situ suggests a path toward more rigorous spectral emissivity analysis and improved modeling of thermal transport in laser-heated DAC experiments.

We report the P-V-T equation of state measurements of B ₄ C to 50 GPa and approximately 2500 K in laser-heated diamond anvil cells. We obtain an ambient temperature, third-order Birch–Murnaghan fit to the P-V data that yields a bulk modulus K ₀ of 221(2) GPa and derivative, (d K /d P ) ₀ of 3.3(1). These were used in fits with both a Mie–Grüneisen–Debye model and a temperature-dependent, Birch–Murnaghan equation of state that includes thermal pressure estimated by thermal expansion ( α ) and a temperature-dependent bulk modulus (d K ₀ /d T ). The ambient pressure thermal expansion coefficient ( α ₀ + α ₁ T ), Grüneisen γ ( V ) = γ ₀ ( V / V ₀ ) ^q and volume-dependent Debye temperature, were used as input parameters for these fits and found to be sufficient to describe the data in the whole P-T range of this study. This article is part of the theme issue ‘Exploring the length scales, timescales and chemistry of challenging materials (Part 1)’.

The phenomenon of high temperature superconductivity, approaching room temperature, has been realized in a number of hydrogen-dominant alloy systems under high pressure conditions1-12. A significant discovery in reaching room temperature superconductivity is the photo-induced reaction of sulfur, hydrogen, and carbon that initially forms of van der Waals solids at sub-megabar pressures. Carbonaceous sulfur hydride has been demonstrated to be tunable with respect to carbon content, leading to different superconducting final states with different structural symmetries. A modulated AC susceptibility technique adapted for a diamond anvil cell confirms a Tc of 260 kelvin at 133 GPa in carbonaceous sulfur hydride. Furthermore, direct synchrotron infrared reflectivity measurements on the same sample under the same conditions reveal a superconducting gap of ~85 meV at 100 K in close agreement to the expected value from Bardeen-Cooper-Schrieffer (BCS) theory13-18. Additionally, x-ray diffraction in tandem with AC magnetic susceptibility measurements above and below the superconducting transition temperature, and as a function of pressure at 107-133 GPa, reveal the Pnma structure of the material is responsible for the close to room-temperature superconductivity at these pressures.

High-Pressure Collaborative Access Team (HPCAT) is a synchrotron-based facility located at the Advanced Photon Source (APS). With four online experimental stations and various offline capabilities, HPCAT is focused on providing synchrotron x-ray capabilities for high pressure and temperature research and supporting a broad user community. Overall, the array of online/offline capabilities is described, including some of the recent developments for remote user support and the concomitant impact of the current pandemic. General overview of work done at HPCAT and with a focus on some of the minerals relevant work and supporting capabilities is also discussed. With the impending APS-Upgrade (APS-U), there is a considerable effort within HPCAT to improve and add capabilities. These are summarized briefly for each of the end-stations.

Nanothreads are one-dimensional nanomaterials composed of a primarily sp³ hydrocarbon backbone, typically formed through the compression of small molecules to high pressures. Although nanothreads have been synthesized from a range of precursors, controlling reaction pathways to produce atomically precise materials remains a difficult challenge. Here, we show how heteroatoms within precursors can serve as “thread-directing” groups by selecting for specific cycloaddition reaction pathways. By using a less-reactive diazine group within a six-membered aromatic ring, we successfully predict and synthesize the first carbon nanothread material derived from pyridazine (1,2-diazine, C₄H₄N₂). Compared with previous nanothreads, the synthesized polypyridazine, shows a predominantly uniform chemical structure with exceptional long-range order, allowing for structural characterization using vibrational spectroscopy and X-ray diffraction. The results demonstrate how thread-directing groups can be used for reaction pathway control and the formation of chemically precise nanothreads with a high degree of structural order.

In this short contribution, we examine Raman spectroscopic data from high-pressure and high-temperature experiments with an Ag-Cl₂ system, and find that they are in good agreement with previously observed and calculated spectra of polychloride species. Our results imply the formation of a hitherto unknown AgCl_x compound, which warrants further study.