Wenxiang Zhao

The machining process of aluminum alloy usually produces built-up edge and tool sticking problems due to their low hardness and large plastic deformation, which may further affect the machined surface quality and tool life. This paper aims to investigate the influence of different cutting fluids on the machined surface quality and tool life during the milling process of 7050 aluminum alloy. A novel cutting fluid (QC-2803) was considered in the study, which is synthesized by addition of alkyl alcohol amide and chlorinated polyolefin, and the traditional cutting fluid (CCF-10) was used as the control group. The physical and chemical properties of two cutting fluids were characterized. The milling process of 7050 aluminum alloy was carried out under two different cutting fluid conditions. The machined surface morphology, cutting force and tool wear morphology were observed during the process. Results show that the surface tension of the novel cutting fluid is significantly lower than that of the traditional cutting fluid, which makes it easier to produce a lubricating film between the aluminum alloy and tool, and further benefits the machined surface quality and tool life. As a result, the surface roughness and cutting force are reduced by ~20.0% and ~42.9%, respectively, and the tool life is increased by 25.6% in the case of the novel cutting fluid (QC-2803). The results in this paper revealed the important laws of cutting fluid with metal surface quality, cutting performance and tool wear, which helps to control the machined surface quality and tool life by the selection of cutting fluid during metal milling.

Superalloy parts place high demands on machined surface integrity and serviceability. In the machining process of superalloys, the cutting fluid is usually used to improve the machining performance. Cutting fluids with cooling and lubrication functions have a relatively large effect on the surface microstructure and residual stress as well. The corrosion damage caused by cutting fluid to the machined surface, during machining and residual, are also worth considering. In this paper, the machining performance of typical binary Ni Cr solid solution, age-hardened, nickel-based superalloy NiCr20TiAl T6, under two commonly used cutting fluids, Blasocut and E709, was analyzed, including cutting performance, surface quality, machining surface corrosion characteristics, and so on. The results showed that the surface residual stress could be improved by adding both cutting fluids compared with the deionized water. Blasocut had better lubrication properties, which could reduce friction and heat production. Pitting holes were found on the polished surface after 45 days with E709 cutting fluid, which was more corrosive than Blasocut. According to this research, a reasonable cutting fluid can be selected to reduce the surface corrosion and improve the service life and performance of parts.

Magnesium alloys have been widely used as lightweight engineering structural materials, but their service performances are severely restricted by corrosion failure. In this paper, the influence of corrosive medium and surface defect energy on the corrosion behavior of rolled ZK61M alloy was investigated. The corrosion tests were conducted in different concentrations of sodium chloride solution for different durations, and the polarization curves and electrochemical impedance spectroscopy were reported. The surface morphology of rolled ZK61M alloy before and after corrosion tests were analyzed. The results showed that the corrosion tendency became stronger with the increase of the concentration of corrosive medium and the number of surface defects of ZK61M alloy. Moreover, the initial corrosion pattern was the pitting caused by micro galvanic corrosion at the surface defect, which gradually developed into uniform corrosion. Furthermore, the main damage occurred at the grain boundary, resulting in the destruction of grain bonding force and the removal of material along the rheological layer. The oxidation corrosion mechanism was mainly the anodic dissolution mechanism.

In this paper, the pain point that cold chain transportation urgently needs for an efficient disinfection method is pointed out. Thus, this work aims at solving the problems and improving the disinfection efficiency in cold chain transportation. While Ultraviolet-C (UVC) irradiation is an effective method by which to kill viruses, it is difficult to apply the commonly used UVC-LED disinfection light source to ice-covered cold chain transportation due to its uneven light field distribution. Thus, the light field regulation of UVC-LED disinfection for cold chain transportation is studied. A UVC-LED chip with a wavelength of 275 nm was used as a light source, and parallel light was obtained by collimating lenses. Then, microlens array homogenization technology was used to shape the UVC light into a uniform light spot, with an energy space uniformity rate of 96.4%. Moreover, a simulation was conducted to compare the effects of the ice layer on the absorption of UVC light. Finally, an experiment was carried out to verify that the disinfection efficiency can be increased nearly by 30% with the proposed system by disinfecting E. coli (Escherichia coli), and the results indicate that the proposed system is an effective disinfection solution during cold chain transportation.

Percutaneous coronary intervention (PCI) with stent implantation is one of the most effective treatments for cardiovascular diseases (CVDs). However, there are still many complications after stent implantation. As a medical device with a complex structure and small size, the manufacture and post-processing technology greatly impact the mechanical and medical performances of stents. In this paper, the development history, material, manufacturing method, and post-processing technology of vascular stents are introduced. In particular, this paper focuses on the existing manufacturing technology and post-processing technology of vascular stents and the impact of these technologies on stent performance is described and discussed. Moreover, the future development of vascular stent manufacturing technology will be prospected and proposed.