Kaiming Wu
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Research Subjects
Research Interests
Kaiming Wu has a total of 5 co-authors. Here are the top co-authors by number of shared publications:
- Jing Liu
The State Key Laboratory of Refractories and Metallurgy, Hubei Province Key Laboratory of Systems Science in Metallurgical Process, Collaborative Innovation Center for Advanced Steels, Wuhan University of Science and Technology, Wuhan 430081, China
1 shared publication - Lin Cheng
The State Key Laboratory of Refractories and Metallurgy, Hubei Province Key Laboratory of Systems Science on Metallurgical Processing, International Research Institute for Steel Technology, Collaborative Center on Advanced Steels, Wuhan University of Science and Technology, Wuhan 430081, China
1 shared publication - Meng Tang
The State Key Laboratory of Refractories and Metallurgy, Hubei Province Key Laboratory of Systems Science in Metallurgical Process, Wuhan University of Science and Technology, Wuhan 430081, China
1 shared publication - Xian Zhang
The State Key Laboratory of Refractories and Metallurgy, Hubei Province Key Laboratory of Systems Science in Metallurgical Process, Wuhan University of Science and Technology, Wuhan 430081, China
1 shared publication - Yan Chen
Shanghai Aerospace Equipment Manufacturer, Shanghai 200245, China
1 shared publication
Latest Publications
- Open Access
Mechanism Understanding of the Role of Rare Earth Inclusions in the Initial Marine Corrosion Process of Microalloyed Steels
In this study, the corrosion behavior of rare earth (RE) microalloyed steels was first evaluated through potentiodynamic polarization tests and corrosion weight loss experiments, and then the corrosion morphologies were observed by scanning electron microscope (SEM). After immersion in a NaCl solution, the sulfides (or oxygen sulfides) dissolved preferentially, followed by corrosion at the boundary between the Fe matrix and oxides. Afterwards, the inclusions fell off as a whole, which promoted pitting nucleation. The first principle modeling demonstrated that the work functions of various kinds of inclusions descended in the following order: La2Zr2O7 > LaAlO3 > (La2O3 ≈ Fe ≈ La2O2S) > La2S3, which provided a theoretical explanation to the dissolution behaviors of inclusions. That is, inclusions containing sulfur tend to dissolve preferentially, whereas the oxides do not dissolve easily. Subsequently, the surface current distributions were detected by the scanning vibrating electrode technique (SVET), which provided more microscopic insight into the role of inclusions in the corrosion propagation. Results showed that the active sites of pitting nucleation accelerated the transverse propagation of corrosion. Finally, local corrosion spread to the whole surface as uniform corrosion.
Open AccessMechanism Understanding of the Role of Rare Earth Inclusions in the Initial Marine Corrosion Process of Microalloyed Steels
In this study, the corrosion behavior of rare earth (RE) microalloyed steels was first evaluated through potentiodynamic polarization tests and corrosion weight loss experiments, and then the corrosion morphologies were observed by scanning electron microscope (SEM). After immersion in a NaCl solution, the sulfides (or oxygen sulfides) dissolved preferentially, followed by corrosion at the boundary between the Fe matrix and oxides. Afterwards, the inclusions fell off as a whole, which promoted pitting nucleation. The first principle modeling demonstrated that the work functions of various kinds of inclusions descended in the following order: La2Zr2O7 > LaAlO3 > (La2O3 ≈ Fe ≈ La2O2S) > La2S3, which provided a theoretical explanation to the dissolution behaviors of inclusions. That is, inclusions containing sulfur tend to dissolve preferentially, whereas the oxides do not dissolve easily. Subsequently, the surface current distributions were detected by the scanning vibrating electrode technique (SVET), which provided more microscopic insight into the role of inclusions in the corrosion propagation. Results showed that the active sites of pitting nucleation accelerated the transverse propagation of corrosion. Finally, local corrosion spread to the whole surface as uniform corrosion.