The application of superamphiphobic coatings improves the surface’s ability to repel fluids, thereby greatly enhancing its various functions, including anti-fouling, anti-corrosion, anti-icing, anti-bacterial, and self-cleaning properties. This maximizes the material’s potential for industrial applications. This work utilized the agglomeration phenomenon exhibited by nano-spherical titanium dioxide (TiO₂) particles to fabricate 1H,1H,2H,2H-perfluorodecyltriethoxysilane (PFDTES) modified TiO₂ (TiO₂@fluoroPOS) fillers with low surface energy. This was achieved through the in-situ formation of protective armor on the surface of the agglomerates using the sol-gel method and fluorination modification. Polyvinylidene fluoride-tetrafluoropropylene (PVDF-HFP) and TiO₂@fluoroPOS fillers were combined using a spraying technique to prepare P/TiO₂@fluoroPOS coatings with superamphiphobicity. Relying on the abundance of papillae, micropores, and other tiny spaces on the surface, the coating can capture a stable air film and reject a variety of liquids. When the coatings were immersed in solutions of 2 mol/L HCl, NaCl, and NaOH for a duration of 12 h, they retained their exceptional superamphiphobic properties. Owing to the combined influence of the armor structure and the organic binder, the coating exhibited good liquid repellency during water jetting and sandpaper abrasion tests. Furthermore, the coating has shown exceptional efficacy in terms of its ability to be anti-icing, anti-waxing, and self-cleaning.

Transmission engineering components need to fulfill requirements for adequate wear resistance and fatigue resistance, which are related to their surface properties. In this paper, we combined shot peening and nitrogen ion implantation to improve the surface properties of 16Cr3NiWMoVNbE gear steel. The average surface roughness decreased slightly after the ion implantation because of the high-speed impact of implanted ions having the surface etching role. The maximum compressive residual stress of the near-surface layer after the surface treatment increased by more than 11.8–15.9% compared with shot peening. The nitrogen ions diffused through the peening deformation channel, and the deformation degree and the implantation temperature were positively correlated with the diffusion process. The surface nano-hardness obtained by ion implantation after shot peening was increased by 124.4% compared to the AR state.