Danying Zuo

In order to promote the sustainability of cementitious materials, it is imperative to reduce the level of environmental pollution and energy consumption during their production, as well as extend the service life of building elements. This study utilized limestone, calcined clay and gypsum as supplementary cementitious materials to prepare LC3 mortar, replacing 50% of ordinary silicate cement. Three types of microcapsules (M1, M2 and M3) were prepared using IPDI as a healing agent and polyethylene wax, polyethylene wax/nano-CaCO₃ or polyethylene wax/ferrous powder as shell materials. The microcapsules were added to the LC3 mortar and tested for their effects on the mechanical properties, pore structure and permeability of mortars. Pre-loaded and pre-cracked mortar specimens were subjected to room temperature or under an applied magnetic field to evaluate the self-healing ability of the microcapsules on mortars. The kinetics of the curing reaction between IPDI and moisture were investigated using quasi-first-order and quasi-second-order reaction kinetic models. The experimental results showed that the mortar (S3) mixed with electromagnetic inductive microcapsules (M3) exhibited the best self-healing ability. The compressive strength retention, the percentage of pores larger than 0.1 μm, recovery of chloride diffusion coefficient and maximum amplitude after self-healing of S3 were 92.2%, 42.6%, 78.9% and 28.87 mV, respectively. Surface cracks with an initial width of 0.3~0.5 mm were healed within 24 h. The curing reaction between IPDI and moisture during self-healing followed a quasi-second-order reaction kinetic model.

This review provides an overview of microcapsule self-healing technology and its application in the field of cement-based materials, as well as future prospects. The presence of cracks and damage in cement-based structures during service has a significant impact on their lifespan and safety performance. Microcapsule self-healing technology shows promise in achieving self-healing by encapsulating healing agents within microcapsules, which are released upon damage to the cement-based material. The review starts by explaining the fundamental principles of microcapsule self-healing technology and explores various methods for preparing and characterizing microcapsules. It also investigates the influence of incorporating microcapsules on the initial properties of cement-based materials. Additionally, the self-healing mechanisms and effectiveness of microcapsules are summarized. Finally, the review discusses the future development directions for microcapsule self-healing technology, outlining potential areas for further research and advancement.

Kapok is a hollow fiber with a 90% hollow degree. Compared with cotton fiber, kapok fiber has excellent performances, such as good hygroscopicity, and a good warmth retention property. In this work, desized indigo kapok/cotton denim fabrics were bleached in different ways: Laser, cellulose enzyme, sodium hypochlorite, potassium permanganate and hydrogen peroxide. After bleaching, the K/S values, tensile strength, air permeability, thickness, color fastness to rubbing and the crease recovery angle of denim fabrics were measured through the spectrophotometer, tensile strength tester, air permeability tester, thickness tester, rubbing fastness tester and fabric crease elasticity tester, respectively. The surfaces of fabrics and fibers were observed by scanning electron microscopy (SEM). Results show that the kapok/cotton fabrics were color-faded after five kinds of bleaching, the K/S values of denim with laser bleaching was declined dramatically, while there was a little change in the permeability. The tensile strength and the weight of the fabrics were decreased, and cloth which was bleached with potassium permanganate was most affected. The color fastness to rubbing and the crease recovery angle of denim fabrics with laser treatment is most suitable for industrial production. In general, laser bleaching is the better way to fade the kapok/cotton denim fabrics. Meanwhile, after five kinds of bleaching, the physical properties of kapok/cotton denim fabrics were similar to those of cotton denim fabric, which indicates that kapok/cotton denim fabric is suitable for the existing industrial bleaching technology.

In this paper, the sulfonated poly(phthalazinone ether ketone) (SPPEK) nanofibers with low sulfonation degree are fabricated by electrospinning for the first time. The optimized concentration of SPPEK for electrospinning is 0.16 g ml⁻¹ and the suitable solvent is the mixture of DMAc and NMP. The resulting SPPEK nanofibers show smooth surfaces and uniform diameters of about 50 nm. Proton conductivities of the SPPEK mat and membrane are tested and compared. The result indicates that the proton conductivity of the SPPEK mat is almost five times as high as that of the SPPEK membrane because of the formation of long‐range proton pathways on the surfaces of SPPEK nanofibers. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 130: 4581–4586, 2013