Erfan Zal Nezhad

With an expectation of an increased number of revision surgeries and patients receiving orthopedic implants in the coming years, the focus of joint replacement research needs to be on improving the mechanical properties of implants. Head-stem trunnion fixation provides superior load support and implant stability. Fretting wear is formed at the trunnion because of the dynamic load activities of patients, and this eventually causes the total hip implant system to fail. To optimize the design, multiple experiments with various trunnion geometries have been performed by researchers to examine the wear rate and associated mechanical performance characteristics of the existing head-stem trunnion. The objective of this work is to quantify and evaluate the performance parameters of smooth and novel spiral head-stem trunnion types under dynamic loading situations. This study proposes a finite element method for estimating head-stem trunnion performance characteristics, namely contact pressure and sliding distance, for both trunnion types under walking and jogging dynamic loading conditions. The wear rate for both trunnion types was computed using the Archard wear model for a standard number of gait cycles. The experimental results indicated that the spiral trunnion with a uniform contact pressure distribution achieved more fixation than the smooth trunnion. However, the average contact pressure distribution was nearly the same for both trunnion types. The maximum and average sliding distances were both shorter for the spiral trunnion; hence, the summed sliding distance was approximately 10% shorter for spiral trunnions than that of the smooth trunnion over a complete gait cycle. Owing to a lower sliding ability, hip implants with spiral trunnions achieved more stability than those with smooth trunnions. The anticipated wear rate for spiral trunnions was 0.039 mm³, which was approximately 10% lower than the smooth trunnion wear rate of 0.048 mm³ per million loading cycles. The spiral trunnion achieved superior fixation stability with a shorter sliding distance and a lower wear rate than the smooth trunnion; therefore, the spiral trunnion can be recommended for future hip implant systems.

Total hip replacement (THR) is a common orthopedic surgery technique that helps thousands of individuals to live normal lives each year. A hip replacement replaces the shattered cartilage and bone with an implant. Most hip implants fail after 10–15 years. The material selection for the total hip implant systems is a major research field since it affects the mechanical and clinical performance of it. Stress shielding due to excessive contact stress, implant dislocation due to a large deformation, aseptic implant loosening due to the particle propagation of wear debris, decreased bone remodeling density due to the stress shielding, and adverse tissue responses due to material wear debris all contribute to the failure of hip implants. Recent research shows that pre-clinical computational finite element analysis (FEA) can be used to estimate four mechanical performance parameters of hip implants which are connected with distinct biomaterials: von Mises stress and deformation, micromotion, wear estimates, and implant fatigue. In vitro, in vivo, and clinical stages are utilized to determine the hip implant biocompatibility and the unfavorable local tissue reactions to different biomaterials during the implementation phase. This research summarizes and analyses the performance of the different biomaterials that are employed in total hip implant systems in the pre-clinical stage using FEA, as well as their performances in in vitro, in vivo, and in clinical studies, which will help researchers in gaining a better understanding of the prospects and challenges in this field.

In this study, a graphene oxide nanoribbons–functionalized carbon nanotubes–graphene oxide (GNFG) complex was hydrothermally synthesized as a nanomaterial for reinforcing cementitious composites, using a modified Hummers’ method. Three types of components existed in the GNFG: Type I, the functionalized carbon nanotubes–graphene oxide nanoribbons (FCNTs–GNR); and types II and III are graphene oxide (GO) and functionalized carbon nanotubes (FCNTs), respectively, which exist independently. The dispersivity of GNFG and its effects on the mechanical properties, hydration process, and microstructures of cement pastes were evaluated, and the results were compared with those using cement pastes incorporating other typical carbon nanomaterials. The results demonstrated that dispersion of GNFG in aqueous solutions was superior to that of the CNTs, FCNTs, and GO/FCNTs mixture. Furthermore, the highly-dispersed GNFG (0.05 wt.%) improved the mechanical properties of the cement paste after 28 days of hydration and promoted the hydration of cement compared to CNTs, GO, and GO/FCNTs mixture (0.05 wt.%). The results in this study validated the feasibility of using GNFG with enhanced dispersion as a new nano-reinforcing agent for various cementitious systems.

Implantable antennas are mandatory to transfer data from implants to the external world wirelessly. Smart implants can be used to monitor and diagnose the medical conditions of the patient. The dispersion of the dielectric constant of the tissues and variability of organ structures of the human body absorb most of the antenna radiation. Consequently, implanting an antenna inside the human body is a very challenging task. The design of the antenna is required to fulfill several conditions, such as miniaturization of the antenna dimension, biocompatibility, the satisfaction of the Specific Absorption Rate (SAR), and efficient radiation characteristics. The asymmetric hostile human body environment makes implant antenna technology even more challenging. This paper aims to summarize the recent implantable antenna technologies for medical applications and highlight the major research challenges. Also, it highlights the required technology and the frequency band, and the factors that can affect the radio frequency propagation through human body tissue. It includes a demonstration of a parametric literature investigation of the implantable antennas developed. Furthermore, fabrication and implantation methods of the antenna inside the human body are summarized elaborately. This extensive summary of the medical implantable antenna technology will help in understanding the prospects and challenges of this technology.

Considering the increase in research regarding environmental pollution reduction, the utilization of cementitious material, a commonly used construction material, in photocatalysts has become a desirable research field for the widespread application of photocatalytic degradation technology. Nano-reinforcement technology for cementitious materials has been extensively researched and developed. In this work, as a new and promising reinforcing agent for cementitious materials, the photocatalytic performance of titanium dioxide nanotube (TNT) was investigated. The degradation of methylene blue was used to evaluate the photocatalytic performance of the TNT-reinforced cement paste. In addition, cement paste containing micro-TiO₂ (m-TiO₂) and nano-TiO₂ (n-TiO₂) particles were used for comparison. Moreover, the effect of these TiO₂-based photocatalytic materials on the cement hydration products was monitored via X-ray diffraction (XRD) and thermogravimetric analysis (TG). The results indicated that all the TiO₂ based materials promoted the formation of hydration products. After 28 days of curing, the TNT-reinforced cement paste contained the maximum amount of hydration products (Ca(OH)₂). Furthermore, the cement paste containing TNT exhibited better photocatalytic effects than that containing n-TiO₂, but worse than that containing m-TiO₂.

In this work, nickel cobaltite (NiCo₂O₄) nanosheets with a porous structure were fabricated on nickel foam as a working electrode for supercapacitor applications. The nanosheets were fabricated by electrochemical deposition of nickel–cobalt hydroxide on the nickel foam substrate at ambient temperature in a three-electrode cell followed by annealing at 300 °C to transform the coating into a porous NiCo₂O₄nanosheet. Field emission scanning electron microscopy and transmission electron microscopy revealed a three-dimensional mesoporous structure, which facilitates ion transport and electronic conduction for fast redox reactions. For one cycle, the NiCo₂O₄electrodeposited nickel foam has a high specific capacitance (1734.9 F g⁻¹) at a current density (CD) of 2 A g⁻¹. The electrode capacitance decreased by only approximately 12.7% after 3500 cycles at a CD of 30 A g⁻¹. Moreover, a solid-state asymmetric supercapacitor (ASC) was built utilising the NiCo₂O₄nanosheets, carbon nanotubes, and a polyvinyl alcohol-potassium hydroxide gel as the anode, cathode, and solid-state electrolyte, respectively. The ASC displayed great electrochemical properties with a 42.25 W h kg⁻¹energy density at a power density of 298.79 W kg⁻¹.

In this study, we synthesized binder-free NiCo₂O₄@NiCo₂O₄ nanostructured materials on nickel foam (NF) by combined hydrothermal and cyclic voltammetry deposition techniques followed by calcination at 350 °C to attain high-performance supercapacitors. The hierarchical porous NiCo₂O₄@NiCo₂O₄ structure, facilitating faster mass transport, exhibited good cycling stability of 83.6% after 5000 cycles and outstanding specific capacitance of 1398.73 F g⁻¹ at the current density of 2 A·g⁻¹, signifying its potential for energy storage applications. A solid-state supercapacitor was fabricated with the NiCo₂O₄@NiCo₂O₄ on NF as the positive electrode and the active carbon (AC) was deposited on NF as the negative electrode, delivering a high energy density of 46.46 Wh kg⁻¹ at the power density of 269.77 W kg⁻¹. This outstanding performance was attributed to its layered morphological characteristics. This study explored the potential application of cyclic voltammetry depositions in preparing binder-free NiCo₂O₄@NiCo₂O₄ materials with more uniform architecture for energy storage, in contrast to the traditional galvanostatic deposition methods.

In this study, to fabricate a non-binder electrode, we grew nickel–cobalt sulfide (NCS) nanotubes (NTs) on a Ni foam substrate using a hydrothermal method through a two-step approach, namely in situ growth and an anion-exchange reaction. This was followed by the electrodeposition of double-layered nickel-cobalt hydroxide (NCOH) over a nanotube-coated substrate to fabricate NCOH core-shell nanotubes. The final product is called NCS@NCOH herein. Structural and morphological analyses of the synthesized electrode materials were conducted via SEM and XRD. Different electrodeposition times were selected, including 10, 20, 40, and 80 s. The results indicate that the NCSNTs electrodeposited with NCOH nanosheets for 40 s have the highest specific capacitance (SC), cycling stability (2105 Fg⁻¹ at a current density of 2 Ag⁻¹), and capacitance retention (65.1% after 3,000 cycles), in comparison with those electrodeposited for 10, 20, and 80 s. Furthermore, for practical applications, a device with negative and positive electrodes made of active carbon and NCS@NCOH was fabricated, achieving a high-energy density of 23.73 Whkg⁻¹ at a power density of 400 Wkg⁻¹.