Tonghan Yang

In this experiment, a series of MnCoGe_1−xLa_x (x = 0, 0.01, 0.03) alloy samples were prepared using a vacuum arc melting method. The crystal structure and magnetic properties of alloys were investigated using X-ray diffraction (XRD), Rietveld method, physical property measurement system (PPMS), and vibrating sample magnetometer (VSM) analyses. The results show that all samples were of high-temperature Ni₂In-type phases, belonging to space group P6₃/mmc (194) after 1373 K annealing. The results of Rietveld refinement revealed that the lattice constant and the volume of MnCoGe_1−xLa_x increased along with the values of La constants. The magnetic measurement results show that the Curie temperatures (T_C) of the MnCoGe_1−xLa_x series alloys were 294, 281, and 278 K, respectively. The maximum magnetic entropy changes at 1.5T were 1.64, 1.53, and 1.56 J·kg⁻¹·K⁻¹, respectively. The respective refrigeration capacities (RC) were 60.68, 59.28, and 57.72J·kg⁻¹, with a slight decrease along the series. The experimental results show that the doping of La results in decreased T_C, basically unchanged magnetic entropy, and slightly decreased RC.

The phase relationships of the ternary Co-Ni-In system at 673 K and 873 K were investigated by means of powder X-ray diffraction, scanning electron microscopy equipped with energy dispersive spectroscopy, and optical microscopy. Though CoIn₂ does not exist at 873 K, the ternary solid solution Co_1−xNi_xIn₂ exists at both 673 K and 873 K with different composition ranges. The Rietveld refinements were carried out to investigate the crystal structure of Co_1−xNi_xIn₂ (x = 0.540, and 0.580) and Ni_2−xCo_xIn₃ (x = 0.200). The magnetization dependence of temperature (MT) curves of Ni_2−xCo_xIn₃ (x = 0.200) and Co_1−xNi_xIn₂ (x = 0.540) are similar to those of the ferromagnetic shape memory alloys Ni-Mn-A (A = Ga, Sn, and In), but do not undergo martensitic transformation. The maximum magnetic entropy changes in Ni_2−xCo_xIn₃ (x = 0.200) and Co_1−xNi_xIn₂ (x = 0.540) under 3T are 1.25 and 1.475 J kg⁻¹K⁻¹, respectively.

This paper presents the study of the properties of objects that were fabricated with fused deposition modeling technology while using Poly (lactic acid)/Walnut shell powder (PLA/WSP) biocomposite filaments. The WSP was treated while using NaOH followed by silane. The infrared spectrum of treated and untreated WSP was characterized. The result was that thermal and mechanical properties could be improved by adjusting the concentration of silane. The experimental results showed: the surface compatibility between WSP and PLA was dramatically improved through treatment with KH550. The crystalline, thermal gravity, and thermal degradation temperatures of biocomposite with untreated WSP were improved from 1.46%, 60.3 °C, and 239.87 °C to 2.84%, 61.3 °C, and 276.37 °C for the biocomposites with treated WSP, respectively. The tensile, flexural, and compressive strengths of biocomposites were raised each by 8.07%, 14.66%, and 23.32%. With the determined silane concentration, PLA/10–15 wt.% treated WSP biocomposites were processed and tested. The results showed that the tensile strength was improved to 56.2 MPa, which is very near to that of pure PLA. Finally, the porous scaffolds with controllable porosity and pore size were manufactured.