Continuous morphological control of anisotropic particles is always an important challenge in the field of materials. In this study, a new strategy for continuous fabrication of polymer particles with various morphologies induced by electricity is reported using complex emulsions as template. A synthetic electro‐responsive surfactant containing ferrocene group is used to prepare complex emulsions, which contain a polymerizable monomer as inner phase. With the increasing time of electrical stimulation on the complex emulsions, hollow, hemispherical, mushroom‐like, and spherical particles are constructed successively after photopolymerization. The Marangoni effect caused by the heterogeneity in the interfacial tension at the droplet surface is the reason for the reconfigurable morphology of the complex emulsion. The controllable complex emulsions by electricity present a versatile platform for constructing fine control of the microstructure and shape anisotropy of particles having customized shapes and functionalities, opening a new possibility for designing sophisticated architectures.

The high crystallization at room temperature and high cost of polyoxytetramethylene glycol (PTMG) have become obstacles to its application. To overcome these problems, a segment of PTMG can be incorporated into a block copolymer. In this work, polypropylene (PPO) glycol-polyoxytetramethylene (PPO-PTMG) multiblock copolymers were designed and synthesized through a chain extension between hydroxyl (OH)-terminated PPO and PTMG oligomers. The chain extenders, feed ratios of the catalyst/chain extender/OH groups, reaction temperature, and time were optimized several times to obtain a PPO-PTMG with low crystallization and high molecular weight. Multiblock copolymers with low crystallization and high average molecular weight (M_n = 1.0–1.4 × 10⁴ Dalton) were harvested using m-phthaloyl chloride as the chain extender. The OH-terminated PPO-PTMG multiblock copolymer with high M_n and a functionality near two was further siliconized by 3-isocyanatopropyltrimethoxysilane to synthesize a novel silyl-terminated polyether. This polyether has an appropriate vulcanizing property and potential applications in sealants/adhesive fields.