Antimony-based materials possess high theoretical capacities and suitable potential, which could be promising anode materials for sodium-ion batteries (SIB). However, poor stabilities and sluggish kinetics are drawbacks. Building heterojunction is an ideal method to solve these issues. Its unique structure develops internal electric fields spontaneously to boost the charge transport and relieve stress. Nevertheless, the controllable preparation of face-to-face (2D) heterojunctions is still hard-pressed. Herein, [ ]–[ ] nanoheterojunctions, which consist of two-dimensional [ ]–[ ] nanoblades attached to a one-dimensional Te nanorod, are fabricated through a two-step solvothermal method. Among that, the density of nanoblades is adjustable through the engineering feed ratio. When employed as anodes for SIBs, [ ]–[ ] nanoheterojunctions display a reversible capacity of 463.2[ ]mAh[ ]g[ ] at 100[ ]mA[ ]g[ ]. Even a capacity of 305.5[ ]mAh[ ]g[ ] remains after 1000 cycles under a high current of 1.5[ ]A[ ]g[ ]. Moreover, the density functional theory (DFT) calculations also identify the high conductivity of heterojunction. This work offers an effective way to design the structures and properties of heterojunctions, further expanding their application range.

(Si/graphite)@C and (Si/graphite/graphene)@C were synthesized by coating asphalt-cracked carbon on the surface of a Si-based precursor by spray drying, followed by heat treatment at 1000 °C under vacuum for 2h. The impact of graphene on the performance of silicon–carbon composite-based anode materials for lithium-ion batteries (LIBs) was investigated. Transmission electron microscopy (TEM) and selected area electron diffraction (SAED) images of (Si/graphite/graphene)@C showed that the nano-Si and graphene particles were dispersed on the surface of graphite, and thermogravimetric analysis (TGA) curves indicated that the content of silicon in the (Si/graphite/graphene)@C was 18.91%. More bituminous cracking carbon formed on the surface of the (Si/graphite/graphene)@C due to the large specific surface area of graphene. (Si/Graphite/Graphene)@C delivered first discharge and charge capacities of 860.4 and 782.1 mAh/g, respectively, initial coulombic efficiency (ICE) of 90.9%, and capacity retention of 74.5% after 200 cycles. The addition of graphene effectively improved the cycling performance of the Si-based anode materials, which can be attributed to the reduction of electrochemical polarization due to the good structural stability and high conductivity of graphene.