A series of novel flame retardants (aluminum diethylphosphinate and melamine) were used to improve the fire performance of phenolic resin. Fourier transform infrared spectroscopy (FTIR) was used to characterize the modification results. Thermo-gravimetric analysis (TGA) was used to study the thermal decomposition of phenolic resin system, and the flame retardancy of phenolic resin system was tested by vertical combustion test (UL-94) and limiting oxygen index (LOI). The combustion properties of modified phenolic resin were further tested with a cone calorimeter(CCT). Finally, the structure of carbon residue layer was measured by scanning electron microscopy (SEM). The results show that with the introduction of 10 wt % aluminum diethylphosphinate in phenolic resin, the LOI reaches 33.1%, residual carbon content increase to 55%. The heat release rate (HRR) decreased to 245.6 kW/m², and the total heat release (THR) decreased to 58.6 MJ/m². By adding 10 wt % aluminum diethylphosphinate and 3 wt % melamine, the flame retardancy of the modified resin can pass UL-94 V-0 flame retardant grade, LOI reaches 34.6%, residual carbon content increase to 59.5%. The HRR decreases to 196.2 kW/m² at 196 s, relatively pure phenolic resin decreased by 35.5%, and THR decreased to 51 MJ/m². Compared with pure phenolic resin, the heat release rate and total heat release of modified phenolic resin decreased significantly. This suggests that aluminum diethylphosphinate and melamine play a nitrogen-phosphorus synergistic effect in the phenolic resin, which improves the thermal stability and flame retardancy of the phenolic resin.

Chlorinated polyvinyl chloride (CPVC), as a new type of engineering plastic waste, has been used widely due to its good heat resistance, mechanical properties and corrosion resistance, while it has become an important part of solid waste. The pyrolysis behaviors of CPVC waste were analyzed based on thermogravimetric experiments to explore its reaction mechanism. Compared with polyvinyl chloride (PVC) pyrolysis, CPVC pyrolysis mechanism was divided into two stages and speculated to be dominated by the dehydrochlorination and cyclization/aromatization processes. A common model-free method, Flynn-Wall-Ozawa method, was applied to estimate the activation energy values at different conversion rates. Meanwhile, a typical model-fitting method, Coats-Redfern method, was used to predict the possible reaction model by the comparison of activation energy obtained from model-free method, thereby the first order reaction-order model and fourth order reaction-order model were established corresponding to these two stages. Eventually, based on the initial kinetic parameter values computed by model-free method and reaction model established by model-fitting method, kinetic parameters were optimized by Shuffled Complex Evolution algorithm and further applied to predict the CPVC pyrolysis behaviors during the whole temperature range.