Lihui Yao

Benzophenone (BP) and N‐vinylpyrrolidone (NVP) were used to modify the surface of polylactide (PLA) films by UV grafting method. The effects of light distance, temperature, reaction time, and modifier concentration on the structure and properties of PLA films were investigated by Fourier transform infrared spectroscopy, X‐ray photoelectron spectroscopy (XPS), nuclear magnetic resonance spectroscopy, differential scanning calorimetry (DSC), and universal testing machine (UTM). With BP and NVP UV grafting, the hydrophilicity of PLA films is improved, but their thermal and mechanical properties are reduced under different surface modification condition. Base on the principle of good surface hydrophilicity, better mechanical and thermal properties, the hydrolytic degradation performance of modified PLA films in artificial seawater at 70°C was studied by scanning electron microscopy, XPS and DSC. The research results show that the degradation of modified PLA films mainly occurs in the amorphous region, and the degradation process conforms to surface hydrolysis mechanism. The grafting modification of NVP is better than BP to accelerate the degradation process of PLA films in artificial seawater. The degradation of modified PLA undergoes water molecule erosion and autocatalytic degradation reaction. The degradation of BP‐PLA obeys the first‐order kinetics in part, while the degradation of NVP‐PLA is more complex. Therefore, surface hydrophilicity modification is an effective technique for improving the degradability of PLA.

Collagen (Col) hydrogels are an important biomaterial with many applications in the biomedical sector. However, deficiencies, including insufficient mechanical properties and a rapid rate of biodegradation, hamper their application. In this work, nanocomposite hydrogels were prepared by combining a cellulose nanocrystal (CNC) with Col without any chemical modification. The high-pressure, homogenized CNC matrix acts as nuclei in the collagen’s self-aggregation process. The obtained CNC/Col hydrogels were characterized in terms of their morphology, mechanical and thermal properties and structure by SEM, rotational rheometer, DSC and FTIR, respectively. Ultraviolet-visible spectroscopy was used to characterize the self-assembling phase behavior of the CNC/Col hydrogels. The results showed an accelerated assembling rate with the increasing loading of CNC. The triple-helix structure of the collagen was preserved with a dosage of CNC of up to 15 wt%. The CNC/Col hydrogels demonstrated an improvement in both the storage modulus and thermal stability which is attributed to the interaction between the CNC and collagen by the hydrogen bonds.

Hydrogel adhesives are attractive for applications in intelligent soft materials and tissue engineering, but conventional hydrogels usually have poor adhesion. In this study, we designed a strategy to synthesize a novel adhesive with a thin hydrogel adhesive layer integrated on a tough substrate hydrogel. The adhesive layer with positive charges of ammonium groups on the polymer backbones strongly bonds to a wide range of nonporous materials’ surfaces. The substrate layer with a dual hydrogen bond system consists of (i) weak hydrogen bonds between N,N-dimethyl acrylamide (DMAA) and acrylic acid (AAc) units and (ii) strong multiple hydrogen bonds between 2-ureido-4[1H]-pyrimidinone (UPy) units. The dual hydrogen-bond network endowed the hydrogel adhesives with unique mechanical properties, e.g., toughness, highly stretchability, and insensitivity to notches. The hydrogel adhesion to four types of materials like glass, 316L stainless steel, aluminum, Al₂O₃ ceramic, and two biological tissues including pig skin and pig kidney was investigated. The hydrogel bonds strongly to dry solid surfaces and wet tissue, which is promising for biomedical applications.

Different Fe ₃ O ₄ particles are synthesised with silane and carboxylic acid, surface modified by co‐precipitation, and subsequently are characterised by Fourier transform infrared spectroscopy, wide‐angle X‐ray diffraction, laser particle size analyser (LPSA) and thermogravimetric analyser (TG). Based on the LPSA results, Fe ₃ O ₄ particles are micrometre size due to the experimental condition and modifiers. It is therefore suggested that the vacuum freeze‐drying and the long‐chain modifiers tend to obtain small size particles. The modifiers density on the surface of Fe ₃ O ₄ particles is obtained by TG and formula calculation. It is shown that the silane coupling agent is more effective modifier for Fe ₃ O ₄ particles compared with carboxylic acid. In accordance with the molecular structure and functional group number of carboxylic acids, different carboxylic acids have different modifiers density.

Two new Brønsted acids [2,2′-ethylidene-bis (4,6-di-tert-butylphenol)] phosphoric acid (EDBPPOOH) and (3,3′,5,5′-tetra-tert-butylbiphenyl-2,2′-diol) phosphoric acid (TBPO-POOH) were synthesised and fully characterised by 1H NMR and 13C NMR spectra and mass spectra. The ringopening polymerisation (ROP) of ɛ-caprolactone (ɛ-CL) catalysed by the two Brønsted acids proceeded at 110°C without a solvent or at ambient temperature in toluene. Experimental results indicated that the two Brønsted acids were efficient catalysts for the ROP of ɛ-CL with moderate number-average molar mass (Mn) and narrow polydispersity indices (PDI). The catalytic activity of TBPO-POOH is higher than EDBP-POOH in the ROP of ɛ-CL. After benzyl alcohol was added, it was able to accelerate the polymerisation process. The polymerisation can also occur with the addition of water with a monomer/catalyst/initiator mole ratio of 100: 1: 1. The living polymerisation was ascertained by the linear relationships of the Mn vs. monomer conversion, then it was further confirmed by a second-feed experiment of a double monomer producing double Mn. A kinetic study of the relationships between monomer concentration and time revealed a first-order dependence on monomer concentration in the polymerisation. End-group analysis of 1H NMR spectra and electrospray-ionisation mass spectra suggests that the two Brønsted acids are capable of catalysing and initiating the ROP of ɛ-CL.