Ozden Isbilir

The use of hybrid materials including carbon fiber reinforced plastics (CFRPs) and lightweight metals such as titanium are increasing particularly in aerospace applications. Multi-material stacks require a number of holes for the assembly purposes. In this research, drilling trials have been carried out in CFRP, Ti-6Al-4V and CFRP/Ti-6Al-4V stack workpieces using AlTiN coated tungsten carbide drill bit. The effects of process parameters have been investigated. The thrust force, torque, burr formation, delamination, surface roughness and tool wear have been analyzed at various processing condition. The experimental results have shown that the thrust force, torque, burr formation and the average surface roughness increase with the increased feed rate and decrease with the increased cutting speed in drilling of Ti-6Al-4V. In drilling CFRP, delamination and the average surface roughness has similar tendency with the cutting parameters however thrust force and torque rises with the increased cutting speed. The results showed that after making 15 holes in CFRP/Ti-6Al-4V stack, measured thrust forces were increased by 20% in CFRP and by 45% in Ti-6Al-4V. Delamination was found to be much smaller in drilling of CFRP in stack from compared to drilling single CFRP. Tool life was significantly shortened in drilling of stack due to the combination of the wear mechanisms.

Drilling is a key factor in the manufacturing of holes required for the assemblies of composite laminates in aerospace industry. The quality of holes can be controlled by the choice of tool geometry and process parameters. Simulation of drilling process is an effective method in optimizing the drill geometry and process parameters in order to improve hole quality and reduce the drill wear. In this research, we have developed three-dimensional finite element model for drilling carbon fiber-reinforced. A three-dimensional progressive intra-laminar failure model based on the Hashin’s theory is considered. Also, an inter-laminar delamination model which includes the onset and growth of delamination by using cohesive contact zone was developed. It is shown that the induced thrust force, torque, damaged area and delamination are predicted very well with the given drill geometry and process parameters. The delamination area resulted from drilling of carbon fiber-reinforced polymer was predicted successfully using the developed model. The current finite element model using three-dimensional elements and improved damage models showed much better capability in simulation of the drilling process of CFC compared to the previous model using shell elements.

Drilling of Ti6Al4V is investigated experimentally and numerically. A 3D finite element model developed based on Lagrangian approach using commercial finite element software ABAQUS/explicit. 3D complex drill geometry is included in the model. The drilling process simulations are performed at the combinations of three cutting speeds and four feed rates. The effects of cutting parameters on the induced thrust force and torque are predicted by the developed model. For validation purpose, experimental trials have been performed in similar condition to the simulations. The forces and torques measured during experiment are compared to the results of the finite element analysis. The agreement of the experimental results for force and torque values with the FE results is very good. Moreover, surface roughness of the holes was measured for mapping of machining.

This study aims to investigate drilling process in carbon-fiber reinforced plastic (CFRP) composites with multilayer TiAlN/TiN PVD-coated tungsten carbide drill. The effect of process parameters have been investigated in drilling of Hexcel M21-T700GC. Thrust force and torque were measured online throughout the drilling experiments. Delamination were observed using optical microscope and analyzed via a developed algorithm based on digital image processing technique. Surface roughness of each hole was measured using a surface profilometer. In addition, the progression of tool wear in various surfaces of drill was observed using tool microscope and measured using image software. Our results indicate that the thrust force and torque increased with the increasing cutting speed and feed rate. Delamination and average surface roughness that rose with the increase in feed rate, however, decreased with the increasing cutting speed. The average surface roughness tended to increase with the increase in feed rate and decrease with the increasing cutting speed in drilling of carbon-fiber reinforced plastic (CFRP). Feed rate was found as the predominant factor on the drilling outputs. Abrasive wear was observed on both flank and relief surfaces, which created edge wear on cutting edges. No sign of chipping or plastic deformation has been observed on the surfaces of drills.