Taiyo Shimizu

A monolithic chitosan aerogel below 0.1 g cm ⁻³ in apparent density was prepared as a biopolymer-based, record-breaking ultralight porous material via ambient pressure drying.

The affinity between carbon nanotubes (CNTs) and organic compounds is of substantial importance since it strongly relates to the dispersibility of CNTs in those compounds. Several affinity evaluation methods have been developed so far, and the concept of the Hansen solubility parameter is a representative method widely used in the field of nanocarbon materials. Here, we demonstrate that CNT-loaded silica columns can effectively assess the affinity of organic compounds for CNT surface by exploiting the chromatographic retention time as a criterion. Obtained trends of the affinity of organic compounds for CNT were compared to those based on Hansen solubility parameter distance values. Most organic compounds showed similar trends, but one exceptional compound was observed. Simple CNT dispersion tests were conducted with these organic compounds to demonstrate the advantage of the chromatographic assessment. Further, we conducted comparison experiments using a pyrene-functionalized column and other CNT-loaded columns to elucidate the characteristics of each CNT column. The chromatographic approaches using CNT columns would be beneficial for realizing CNT suspensions with improved CNT dispersibility.

Virtual experiment of carbon nanotube (CNT) film based on artificial intelligence is examined. As reported in many previous papers, artificial intelligence can create many kinds of images and data and using those technics many researchers have tried to develop the high functional materials using AI. In this study, one of the deep learning technics, such as generative adversarial network, is introduced to derive the images and properties of CNT films, and its application is explained.

Radical scavenging activities are attractive properties not only for scientific fields e.g. biomedicine, but for the materials industry. In this study, we report that carbon nanotubes (CNTs) can scavenge radicals from organic peroxides, while radicals from azo-type radical initiators exhibit only a few effects from the presence of CNTs. In addition, experimental results suggest the possibility that captured peroxide radicals generate active radical sites on the CNT surface, from which polymerization can take place. These results indicate the importance of selecting an appropriate radical initiator.

Aerogels have many attractive properties but are usually costly and mechanically brittle, which always limit their practical applications. While many efforts have been made to reinforce the aerogels, most of the reinforcement efforts sacrifice the transparency or superinsulating properties. Here we report superflexible polyvinylpolymethylsiloxane, (CH₂CH(Si(CH₃)O_2/2))_n, aerogels that are facilely prepared from a single precursor vinylmethyldimethoxysilane or vinylmethyldiethoxysilane without organic cross-linkers. The method is based on consecutive processes involving radical polymerization and hydrolytic polycondensation, followed by ultralow-cost, highly scalable, ambient-pressure drying directly from alcohol as a drying medium without any modification or additional solvent exchange. The resulting aerogels and xerogels show a homogeneous, tunable, highly porous, doubly cross-linked nanostructure with the elastic polymethylsiloxane network cross-linked with flexible hydrocarbon chains. An outstanding combination of ultralow cost, high scalability, uniform pore size, high surface area, high transparency, high hydrophobicity, excellent machinability, superflexibility in compression, superflexibility in bending, and superinsulating properties has been achieved in a single aerogel or xerogel. This study represents a significant progress of porous materials and makes the practical applications of transparent flexible aerogel-based superinsulators realistic.

Reactions of chloromethyltrimethoxysilane (CMTMS) and its derived colloidal network polychloromethylsilsesquioxane (PCMSQ) have been investigated to extend the material design strategy toward functionalized and mechanically reinforced aerogels. In a carefully designed sol–gel system, CMTMS has afforded transparent aerogels in the presence of cationic surfactant. The surface chloromethyl groups with polarity and reactivity are shown to be useful for supporting nanostructures, with photoluminescent carbon dots (C-dots) prepared from polyethylenimine and citric acid as an example. Furthermore, since nucleophilic substitution (S_N2) reactions on the surface chloromethyl groups are found to control the equilibrium of formation/dissociation of siloxane bonds, a new gelation strategy triggered by S_N2 reactions in sol–gel has been developed. In the presence of nucleophilic organic species such as polyamines, a hybrid network consisting of PCMSQ cross-linked with a polyamine nucleophile can be prepared to enhance mechanical properties of aerogel.

Transparent, low-density ethenylene-bridged polymethylsiloxane [Ethe-BPMS, O_2/2(CH₃)Si–CH═CH–Si(CH₃)O_2/2] aerogels from 1,2-bis(methyldiethoxysilyl)ethene have successfully been synthesized via a sol–gel process. A two-step sol–gel process composed of hydrolysis under acidic conditions and polycondensation under basic conditions in a liquid surfactant produces a homogeneous pore structure based on cross-linked nanosized colloidal particles. Visible-light transmittance of the aerogels varies with the concentration of the base catalyst and reaches as high as 87% (at a wavelength of 550 nm for a 10 mm thick sample). Gelation and aging temperature strongly affect the deformation behavior of the resultant aerogels against uniaxial compression, and the obtained aerogels prepared at 80 °C show high elasticity after being unloaded. This highly resilient behavior is primarily derived from the rigidity of ethenylene groups, which is confirmed by a comparison with other aerogels with similar molecular structures, ethylene-bridged polymethylsiloxane and polymethylsilsesquioxane. Applicability of the addition reaction using a Diels–Alder reaction of benzocyclobutene has also been investigated, revealing that a successful addition takes place on the ethenylene linkings, which is verified using Raman and solid-state NMR spectroscopies. Insights into the effect of molecular structure on mechanical properties and the availability of surface functionalization provided in this study are important for realizing transparent aerogels with the desired functionality.