Cristina-Daniela Ghițulică

This study explores the influence of precursor nature on the structural and mechanical characteristics of hydroxyapatite–yttria partially stabilized zirconia (HAp–YSZ) nanocomposites designed for biomedical applications. Precursor powders for obtaining these ceramic composites were synthesized via wet coprecipitation, using different calcium phosphate precursors: dibasic and monobasic ammonium phosphates for hydroxyapatite, and zirconyl chloride with yttrium acetate for YSZ. The dried precipitated powders were thermally treated at 600 °C and 800 °C and characterized by X-ray diffraction (XRD), thermal analysis (DTA–TG), transmission electron microscopy (TEM), and BET surface area measurements. The nanocomposites containing 70–90 wt.% HAp and 10–30 wt.% YSZ were sintered between 1000 °C and 1400 °C. Microstructural and physical properties were evaluated using scanning electron microscopy (SEM), open porosity, and compressive strength testing. Results revealed that precursor type and calcination temperature strongly affected crystallinity, particle size, and phase composition, influencing both porosity and mechanical strength of the final materials. An optimal sintering temperature of approximately 1200 °C was identified, balancing densification and phase stability. The findings demonstrate that controlling precursor chemistry and heat treatment enables fine-tuning of nanocomposite structure and performance, supporting their potential as bioactive, mechanically enhanced ceramics for orthopedic implant applications.

Bioactive glasses in the SiO₂-CaO-P₂O₅ system represent emerging materials for hard-tissue-regeneration applications. This article focuses on the synthesis, characterization, and biological interaction of glasses doped with Mg²⁺ and/or Zn²⁺, with an emphasis on their effects on biomineralization, antibacterial behavior, and interactions with preosteoblasts from the MC3T3-E1 cell line. The bioglasses were synthesized using the sol-gel method, and the vitreous nature remained predominant even after thermal treatment at 600 °C for 2 h. From an in vitro perspective, the synthesized bioglasses demonstrated strong cell adhesion and proliferation (notably in the case of Mg²⁺ doping), low cytotoxicity, and antibacterial properties (especially in Zn²⁺-doped samples). Additionally, the simultaneous doping with Mg²⁺ and Zn²⁺ of the bioactive glass matrix is a prospective strategy for developing biomaterials with a “dual” biological characteristics–both osteoinductive and antibacterial.

This study explores the potential utilization of walstromite (BaCa₂Si₃O₉) as a foundational material for creating new bioceramics in the form of scaffolds through 3D printing technology. To achieve this objective, this study investigates the chemical–mineralogical, morphological, and structural characteristics, as well as the biological properties, of walstromite-based bioceramics. The precursor mixture for walstromite synthesis is prepared through the sol–gel method, utilizing pure reagents. The resulting dried gelatinous precipitate is analyzed through complex thermal analysis, leading to the determination of the optimal calcination temperature. Subsequently, the calcined powder is characterized via X-ray diffraction and scanning electron microscopy, indicating the presence of calcium and barium silicates, as well as monocalcium silicate. This powder is then employed in additive 3D printing, resulting in ceramic scaffolds. The specific ceramic properties of the scaffold, such as apparent density, absorption, open porosity, and compressive strength, are assessed and fall within practical use limits. X-ray diffraction analysis confirms the formation of walstromite as a single phase in the ceramic scaffold. In vitro studies involving immersion in simulated body fluid (SBF) for 7 and 14 days, as well as contact with osteoblast-like cells, reveal the scaffold’s ability to form a phosphate layer on its surface and its biocompatibility. This study concludes that the walstromite-based ceramic scaffold exhibits promising characteristics for potential applications in bone regeneration and tissue engineering.

The present study aimed to identify, generate, and validate a set of indicators of the social dimension of higher education in the context of quality assurance systems, with a focus on immigrant students and those with disabilities. For this purpose, two research methods were implemented: the systematic analysis of specialized literature and focus groups. The literature review sought to update conceptualizations and good practices in the European and national context. The focus groups were conducted with stakeholders relevant for the social dimension of higher education: academic and non-academic staff, immigrant students, and students with disabilities. The corroborated results revealed a complex structure of potential indicators. The most important criteria were the category of beneficiaries (students with disabilities and immigrant students), the reflected social value (equality, equity, diversity, and inclusion), the target of the specific measures (aimed at students or at academic and non-academic staff), the direction of the measures (top-down or bottom-up), the stage of the educational process to which the indicators refer (recruitment admission, participation, graduation and post-graduation), the level of implementation of the measures (primary measures and secondary measures/meta-measures). The indicators identified in this study allow multiple uses. In relation to the objective of the study, the most important is the possibility of use in the evaluation of the social dimension of higher education in the context of quality assurance systems.

Student-centred learning (SCL) is a key quality assurance standard promoted across the European Higher Education Area (EHEA), as established by the Standards and Guidelines for Quality Assurance in the EHEA (ESG, 2015). Its implementation requires articulated commitment, decision and practice undertaken by institutions, teaching staff and students. The current literature on quality academic learning and teaching explains SCL through various factors that range from the creation of a student-centred higher education culture to the implementation of active and innovative learning strategies. However, the national quality assurance policies and practices might vary importantly. The present paper aims to offer a view on the latest thinking and evidence regarding the SCL approaches in the EHEA and Romanian higher education, analysed from the quality assurance perspective. Our research had a dual focus. We performed a systematic review of the strategies and frameworks used by quality assurance agencies to assess SCL implementation in higher education. We also explored the perspective of Romanian higher education management and academic representatives on the SCL and its use for the design of quality higher education study programs. Our main research questions were: (1) What are the strategies and practices employed by the EHEA quality assurance agencies for the assessment of SCL implementation in higher education institutions? (2) What is the perception of Romanian higher education stakeholders on the concept of SCL, its implementation and its impact on curriculum development and students’ learning? (3) What are the critical factors of SCL implementation that can be considered in elaborating future effective assessment procedures? Our study contributes to improving higher education quality assurance procedures by highlighting possible future guidelines for supporting and evaluating the implementation of SCL approaches.

Bioceramics are the most promising materials used for hard tissue reconstruction. In this study, wollastonite/hydroxyapatite (HAp/WS)-type composite ceramic structures were synthesized with the aim of reaching a material with improved properties for use in bone tissue regeneration. The scaffolds were synthesized using a foam replica method, starting from ceramic powders with different mass ratios. These were subsequently studied and compared to identify the ideal mass ratio in terms bioactive character, appropriate mechanical properties, but also microstructural influence. The results indicate that all of the samples showed a highly porous microstructure with interconnected pores and high mineralization after 21 days of immersion in SBF. The porous structures with 90% and 70% mass contents of hydroxyapatite presented a well-defined structure and the highest values of mechanical compressive strength. Biocompatibility evaluation showed that osteoblast-like cells are able to penetrate the inner volume of the structures, exhibiting a biocompatible behavior in terms of morphological features and viability following 7 days of incubation. All results show that the porous composite ceramics with 90% and 70% mass contents of hydroxyapatite are promising materials for bone tissue regeneration.

The present work focused on the synthesis and characterization of scaffold type biomaterials based on calcium silicate doped with magnesium ions for bone regeneration with potential applications in tissue engineering. Starting from the idea that calcium silicate, with a scaffold type structure, presents relatively weak mechanical properties and a fast degradation rate, it was considered to dope it with magnesium ions to obtain materials with improved properties from mechanical and biological points of view, which can be an alternative to the classical methods of bone regeneration. Magnesium was selected because it plays an important role in the human body, maintaining bone health, and even more it promotes the process of osteogenesis. Therefore, in this study, scaffolds based on calcium silicate doped with magnesium ions were obtained by replicating a polymer sponge.

Mesoporous bioactive glass nanoparticles (MBGNs) are widely recognized for their ability to bond to hard tissue, while the ions released from the BG structure enhance specific cellular pathways. In this study, the SiO₂-P₂O₅-CaO-MgO-ZnO system was used to successfully synthesize MBGNs by a microemulsion-assisted sol-gel method. The MBGNs calcinated at 600 °C/3 h had a typical phosphosilicate structure together with a poorly crystalline hydroxyapatite (HAp). The addition of ZnO not only led to a higher degree of crystallinity of HAp but also induced a higher porosity of the particles. All MBGNs had a mesoporous structure with an interconnected network of slit shape pores. For each type of composition, two families of highly dispersed spherical nanoparticles could be identified. In vitro tests in simulated body fluid (SBF) proved that after only 3 days of immersion all the materials were covered with a layer of brushite whose degree of crystallinity decreases in the presence of Zn²⁺. The antibacterial assay revealed a strong inhibitory effect for all samples after 40 h of contact. Simultaneously, MBGNs did not increase the intracellular oxidative stress while it stimulated the cell proliferation process.

As bone diseases and defects are constantly increasing, the improvement of bone regeneration techniques is constantly evolving. The main purpose of this scientific study was to obtain and investigate biomaterials that can be used in tissue engineering. In this respect, nanocomposite inks of GelMA modified with hydroxyapatite (HA) substituted with Mg and Zn were developed. Using a 3D bioprinting technique, scaffolds with varying shapes and dimensions were obtained. The following analyses were used in order to study the nanocomposite materials and scaffolds obtained by the 3D printing technique: Fourier transform infrared spectrometry and X-ray diffraction (XRD), scanning electron microscopy (SEM), and micro-computed tomography (Micro-CT). The swelling and dissolvability of each scaffold were also studied. Biological studies, osteopontin (OPN), and osterix (OSX) gene expression evaluations were confirmed at the protein levels, using immunofluorescence coupled with confocal microscopy. These findings suggest the positive effect of magnesium and zinc on the osteogenic differentiation process. OSX fluorescent staining also confirmed the capacity of GelMA-HM5 and GelMA-HZ5 to support osteogenesis, especially of the magnesium enriched scaffold.

The main objective was to produce 3D printable hydrogels based on GelMA and hydroxyapatite doped with cerium ions with potential application in bone regeneration. The first part of the study regards the substitution of Ca²⁺ ions from hydroxyapatite structure with cerium ions (Ca_10-xCe_x(PO₄)₆(OH)₂, xCe = 0.1, 0.3, 0.5). The second part followed the selection of the optimal concentration of HAp doped, which will ensure GelMA-based scaffolds with good biocompatibility, viability and cell proliferation. The third part aimed to select the optimal concentrations of GelMA for the 3D printing process (20%, 30% and 35%). In vitro biological assessment presented the highest level of cell viability and proliferation potency of GelMA-HC5 composites, along with a low cytotoxic potential, highlighting the beneficial effects of cerium on cell growth, also supported by Live/Dead results. According to the 3D printing experiments, the 30% GelMA enriched with HC5 was able to generate 3D scaffolds with high structural integrity and homogeneity, showing the highest suitability for the 3D printing process. The osteogenic differentiation experiments confirmed the ability of 30% GelMA-3% HC5 scaffold to support and efficiently maintain the osteogenesis process. Based on the results, 30% GelMA-3% HC5 3D printed scaffolds could be considered as biomaterials with suitable characteristics for application in bone tissue engineering.