Zesong Wang

We proposed a differential fiber-optic refractive index sensor based on coupled plasmon waveguide resonance (CPWR) in the C-band. The sensor head is a BK7 prism coated with ITO/Au/ITO/TiO₂ film. CPWR is excited on the film by the S-polarized components of an incident light. The narrow absorption peak of CPWR makes it possible to realize dual-wavelength differential intensity (DI) interrogation by using only one incident point. To implement DI interrogation, we used a DWDM component to sample the lights with central wavelengths of 1529.55 and 1561.42 nm from the lights reflected back by the sensor head. The intensities of the dual-wavelength lights varied oppositely within the measurement range of refractive index, thus, a steep slope was produced as the refractive index of the sample increased. The experimental results show that the sensitivity is 32.15/RIUs within the measurement range from 1.3584 to 1.3689 and the resolution reaches 9.3 × 10⁻⁶ RIUs. Benefiting from the single incident point scheme, the proposed sensor would be easier to calibrate in bio-chemical sensing applications. Moreover, this sensing method is expected to be applied to retro-reflecting SPR sensors with tapered fiber tip to achieve better resolution than wavelength interrogation.

To develop the hard and self-lubricating coatings applied for the industrial dry-cutting and die-casting machining tool fields, a series of MoTiAlN/MoN/Mo multilayered coatings were deposited on Si substrates under low substrate rotation by cathodic multi-arc ion plating. XRD, SEM, TEM, RBS, nanoindentation, and tribology tester were used to monitor the phase structure, morphology, component, nanohardness, and friction coefficient of the coatings. It was found that the coatings deposited at various substrate rotations comprised paramount cubic B1 structure TiAlN and Mo₂N phases. The micrographs confirmed that the mean modulation period and total physical thickness of multilayered TiAlN/Mo₂N coatings with a sharp interface fabricated at 2 revolutions per minute (rpm) were 26 nm and 1.15 μm. The mean nanohardness and friction coefficient were ca. 30 GPa and 0.4, respectively. RBS results along with the SIMNRA code allowed to estimate the total atomic concentrations and the physical thickness of individual sublayer as well as the modulation period of multilayered coatings, which demonstrated an efficiency of this approach for characterization of nano-multilayered structures.

Fiber-optic surface plasmon resonance (SPR) sensors possess the advantages of small size, flexible, allowing for a smaller sample volume, easy to be integrated, and high sensitivity. They have been intensively developed in recent decades. However, the polarizing nature of the surface plasmon waves (SPWs) always hinders the acquisition of SPR spectrum with high signal-noise ratio in wavelength modulation unless a polarizer is employed. The addition of polarizer complicates the system and reduces the degree of compactness. In this work, we propose and demonstrate a novel, polarization-independent fiber-optic SPR sensor based on a BK7 bi-prism with two incident planes orthogonal to each other. In the bi-prism, TM-polarized components of non-polarized incident lights excite SPWs on the first sensing channel, meanwhile the TE components and the remaining TM components are reflected, then the reflected TE components serve as TM components of incident lights for the second sensing channel to excite SPWs. Simulations show the proposed SPR structure permit us to completely eliminate the polarization dependence of the plasmon excitation. Experimental results agree well with the simulations. This kind of devices can be considered an excellent option for development of simple and compact SPR chemical sensors.