This study investigates the preparation of ultrahigh-strength AZ80 magnesium alloy bulks using room temperature multidirectional forging (MDF) at different strain rates. The focus is on elucidating the effects of multidirectional loading and strain rates on grain refinement and the subsequent impact on the mechanical properties of the AZ80 alloy. Unlike hot deformation, the alloy subjected to room temperature MDF exhibits a lamellar twinned structure with multi-scale interactions. The key to achieving effective room temperature MDF of the alloy lies in combining multidirectional loading with small forging strains per pass (6%). This approach not only maximizes the activation of twinning to accommodate deformation but ensures sufficient grain refinement. Microstructural analysis reveals that the evolution of the grain structure in the alloy during deformation results from the competition between {10$\overline{1}$2} twinning or twinning variant interactions and detwinning. Increasing the forging rate effectively activates more twin variants, and additional deformation passes significantly enhance twin interaction levels and dislocation density. Furthermore, at a higher strain rate, more pronounced dislocation accumulation facilitates the transformation of twin structures into high-angle grain boundaries, promoting texture dispersion and suppressing detwinning. The primary strengthening mechanisms in room temperature MDF samples are grain refinement and dislocation strengthening. While increased dislocation density raises yield strength, it reduces post-yield work hardening capacity. After two passes of MDF at a higher strain rate, the alloy achieves an optimal balance of strength and ductility, with a tensile strength of 462 MPa and an elongation of 5.1%, significantly outperforming hot-deformed magnesium alloys.