In this work, polyamide 66/polyphenylene oxide (PA66/PPO) composites, including the flame retardants 98 wt% aluminum diethylphosphinate + 2 wt% polydimethylsiloxane (P@Si), Al(OH)₃-coated red phosphorus (RP*), and glass fiber (GF), were systematically studied, respectively. The limiting oxygen index (LOI), UL-94 vertical burning level, and thermal and mechanical properties of the PA66/PPO composites were characterized. The results showed that the P@Si and RP flame retardants both improved the LOI value and UL-94 vertical burning level of the PA66/PPO composites, and PA66/PPO composites passed to the UL-94 V-0 level when the contents of P@Si and RP* flame retardants were 16 wt% and 8 wt%. On the other hand, the mechanical properties of the PA66/PPO composites were reduced from a ductile to a brittle fracture mode. The addition of GF effectively made up for these defects and improved the mechanical properties of the PA66/PPO composites containing the P@Si and RP*, but it did not change the fracture mode. P@Si and RP* flame retardants improved the thermal decomposition of PA66/PPO/GF composites and reduced the maximum mass loss rates, showing that the PA66/PPO/GF composites containing the P@Si and RP* flame retardants could be used in higher-temperature fields.

In this work, polyamide 1010 (PA1010) films were prepared by melt-quenching. A wide-angle X-ray diffractometer (WAXD) with a thermal stretching stage was used to investigate the structure transformation, crystallinity and degree of orientation in the course of simultaneous thermally stretched PA1010. The crystallinity increased along with the increase of draw ratio and then decreased as the draw ratio was over 2.00 times—which the maximum value reached when the draw ratio was about 2.00 times. The degree of orientation of γ-PA1010 was much greater at higher temperature than room temperature (RT); the difference gradually became weaker with the increase of draw ratio. There was a linear relationship between the draw ratios and tensile force at higher temperatures, and the tensile force increased with the increase of draw ratios. The tensile force may induce crystallization and promote orientation in the course of simultaneous thermally stretched PA1010. These phenomena are beneficial to understand the structure-processing-performance relationship and provide some theoretical basis for the processing and production.