Mohamed Aburaia

The most widely used 3D process, fused deposition modeling (FDM), has insufficient interlayer adhesion due to its layer-by-layer forming method. A support material is also essential for the hollow parts and cantilevers. Moreover, the polymer materials used have limited mechanical properties. These issues have restricted the application of FDM in high-performance fields. Continuous fiber-reinforced thermoplastic composites (CFRTPCs) have high mechanical properties and have recently become the focus of research in the field of 3D printing. This paper, using pipe parts as an example, proposes a hybrid of pure polymer (pure PLA used) and CFRTPC (flax fiber pre-impregnated filament) material to develop a printing method based on the outstanding mechanical properties of CFRTPC material. After studying the printing path planning algorithm, the CFRTPC filament is laid along the axial and radial directions on the surface of the polymer base to improve the printed parts’ properties. The method feasibility and algorithm accuracy are verified through the development of five-axis printing equipment with a double nozzle. Through the printed sample’s tensile, compression and bending tests, the results show that the tensile, compressive and bending properties of PLA pipe can be significantly enhanced by laying CFRTPC filament along the axial and radial directions of the pipe. To summarize, the introduction of CFRTPCs greatly improved the mechanical properties of the printed parts, and the implementation of our method provides an effective way to solve the defects of the FDM process.

Continuous fiber-reinforced manufacturing has many advantages, but the fabrication cost is high and its process is difficult to control. This paper presents a method for printing fiber-reinforced composite on the common fused filament fabrication (FFF) platform. Polylactic Acid (PLA) and Polyethylene terephthalate (PET) fibers are used as printing materials. A spatial continuous toolpath planning strategy is employed to reduce the workload of post-processing without cutting the fiber. Experimental results show that this process not only enables the printing of models with complex geometric shapes but also supports material recycling and reuse. A material recovery rate of 100% for continuous PET fiber and 83% for PLA were achieved for a better environmental impact. Mechanical tests show that the maximum tensile strength of continuous PET fiber-reinforced thermoplastic composites (PFRTPCs) is increased by 117.8% when compared to polyamide-66 (PA66).

Additive manufacturing has been applied in many fields, but its layer-by-layer fabrication process leads to a weak inter-layer bond strength of printed parts, so it cannot meet the higher requirements for mechanical properties of the industry. At present, many researchers are studying the printing path planning method to improve the mechanical properties of printed parts. This paper proposes a method to plan the printing path according to the actual stress of pipe parts, and introduces the realization process of an algorithm in detail, and obtains the printing control G-code. Additionally, a 5-axis material extrusion platform was built to realize the printing of polylactic acid pipes with plane and space skeleton curves, respectively, which verified the feasibility and applicability of the method and the correctness of the planning path with standard material extrusion filaments. Finally, the tensile and bending experiments prove that axial printing enhances the mechanical properties of pipe parts.

For the traditional three-axis (3D) configuration of the additive manufacturing (AM) platform, when printing the target model with a multi-branched structure, it is imperative to construct adequate support structures. To eliminate the use of support during the printing process, a non-directional unsupported 3D printing method for five-axis AM is proposed in this paper. By carrying out the K-means clustering algorithm, the coarse partition of the model is obtained, and then the fine decomposition represented by a sequence of separating planes is determined by a local dynamic search adjustment algorithm according to manufacturing constraints. The multi-branched structure of the model is divided into simple subparts so that the general model can be built in different directions and be printed with its own parts as the support. Two case studies were carried out for verification. The experimental results showed that the branch-model can be printed without support using the non-directional unsupported 3D printing method, and the non-directional unsupported 3D printing can save 18.72–20.60% of materials and 20.60–23.33% of time compared to conventional 3D printing.