A versatile synthesis method for pyrochlore oxides containing Ir and Ru with lanthanides Pr, Nd, Eu, Gd, Tb, and Ho is herein presented. Based on the systematic synthesis and Rietveld refinement results, the lattice constants were tunable depending on the ionic radius of the lanthanide used. Subsequently, Pr-based pyrochlore oxides containing Ru and Ir in different ratios were fabricated for the oxygen evolution reaction (OER) in alkaline media, and the OER activity of these catalysts increased when the content of Ir and Ru was the same. Thus, the co-substitution of Ir and Ru in pyrochlore oxides is a novel synthesis strategy for electrocatalysts, which provides great potential for the fabrication of other pyrochlore oxides with various architectures and compositions for application in electrocatalysis.

Dry reforming of methane can be used for suppressing the rapid growth of greenhouse gas emissions. However, its practical implementation generally requires high temperatures. In this study, we report an optimal catalyst for low-temperature dry reforming of methane with high carbon coking resistance synthesized from NiYAl alloy. A facile two-step process consisting of preferential oxidation and leaching was utilized to produce structurally robust nanoporous Ni metal and Y oxides from NiYAl₄. The catalyst exhibited an optimal carbon balance (0.96) close to the ideal value of 1.0, indicating the optimized dry reforming pathway. This work proposes a facile route of the structural control of active metal/oxide sites for realizing highly active catalysts with long-term durability.

The exploration of a new family of flexible and high-performance electromagnetic shielding materials is of great significance to the next generation of intelligent electronic products. In this paper, we report a simple magnetic-electrospinning (MES) method for the preparation of a magnetic flexible film, γ-Fe₂O₃ nanoparticle-embedded polymeric nanofibers. By introducing the extra magnetic field force on γ-Fe₂O₃ nanoparticles within composite fibers, the critical voltage for spinning has been reduced, along with decreased fiber diameters. The MES fibers showed increased strength for the magnetic field alignment of the micro magnets, and the attraction between them assisted the increase in fiber strength. The MES fibers show modifications of the magnetic properties and electrical conductivity, thus leading to better electromagnetic shielding performance.