Lukas Schmidt

Recycling of lithium-ion batteries (LIBs) remains challenging due to high energy requirements, losses of key elements like lithium, and the heterogeneity of waste streams arising from different cathode chemistries. This study evaluates multiple recycling methods for LIBs black mass (BM), to recover critical raw materials and other valuable components. Three types of BM including nickel–manganese–cobalt (NMC), lithium iron phosphate (LFP) and a heterogeneous mixture of cell phones and laptops (HL; German: Handy/Laptops), were treated using froth flotation, pyrometallurgy, and biohydrometallurgy and their respective recovery efficiencies were assessed. The flotation results revealed that the HL sample had the lowest mis-recovery of non-ferrous metals into the froth product (around 10%), leading to further flotation only for HL. During screening, 94–99% of iron, phosphorus, and carbon in LFP-type BM were recovered in the fine fraction (<45 µm), while 92–99% of lithium, cobalt, manganese, nickel, and carbon in NMC-type BM were recovered in the same fraction. During precipitation, 99% of iron and 100% of phosphorus were recovered from LFP bioleachates at pH 3, while ~97–100% of dissolved cobalt, manganese, and nickel were recovered from NMC bioleachates. These findings confirm that no single recycling method is optimal for all battery chemistries.

This paper studies the integration of direct reduced iron (DRI) and hot briquetted iron (HBI) into the steelmaking process via an electric arc furnace (EAF). Considering a variety of DRI production techniques distinguished by different reactor types, this paper provides a comparative overview of the current state. It delves into significant challenges, such as the susceptibility of DRI to reoxidation and the necessity of thorough handling to maintain its quality. The effectiveness of several reoxidation mitigation strategies, including the application of thin oxide layers, briquetting, various coatings, and nitride formation in ammonia-based reduction processes, is evaluated. Most existing studies have primarily focused on the reoxidation of DRI rather than on HBI, despite the fact that HBI may undergo reoxidation. The importance of DRI/HBI in offering an alternative to the integrated steelmaking route is highlighted, focusing on how it changes the EAF process compared to those for melting scrap. This paper also identifies several research prospects for further DRI/HBI applications in steel production.

In this work, the carbothermic reduction of iron- and zinc-bearing products is studied through in situ microwave heating, dielectric properties monitoring, and mass spectrometry up to high temperatures (1000 °C). The results are correlated to the information provided by conventional analysis techniques such as differential scanning calorimetry (DSC) and thermogravimetry (TG). This combination allows a detailed study of seven different process stages with an accurate determination of the reaction temperatures, providing new evidence about the particular conditions of this microwave-driven reduction process. The presented results suggest that molecular vibrations imposed by the microwave field are presumably the reason for reactions taking place at lower temperatures than those observed in the conventional process. This work also explores the influence of other parameters, such as the apparent density or the amount of carbonaceous material, on the resulting dielectric properties, providing useful information for the development of a potential microwave industrial application in the metallurgy field.