Additive manufacturing (AM) allows for optimized part design, reducing weight compared to conventional manufacturing. However, the microstructure, surface state, distribution, and size of internal defects (e.g., porosities) are very closely related to the AM fabrication process and post-treatment operations. All these parameters can have a strong impact on the corrosion and fatigue performance of the final component. Thus, the fatigue-corrosion behavior of the 3D-printed (L-PBF) AlSi10Mg aluminum alloy has been investigated. The influence of load sequence (sequential vs. combined) was explored using Wöhler diagrams. Surface roughness and defects in AM materials were examined, and surface treatment was applied to improve surface quality. The machined specimens showed the highest fatigue properties regardless of load sequence by improving both the roughness and removing the contour layer containing the highest density of defect. The impact of corrosion was more pronounced for as-printed specimens as slightly deeper pits were formed, which lowered the fatigue-corrosion life. As discussed, the corrosion, fatigue and fatigue-corrosion mechanisms were strongly related to the local microstructure and existing defects in the AM sample.

In this study, the fatigue strength of 316 L stainless steel manufactured by selective laser melting (SLM) is evaluated. The effect of powder layer thickness and postmachining is investigated. Specimens were produced with 30 and 50 µm layer thickness and tested under high cycle fatigue in as-printed and postmachined conditions. Examination of the specimens reveals that in the as-printed condition, fatigue strength suffers from high roughness and surface tensile residual stresses as well as defects such as pores and lack of fusion voids. After machining, the fatigue strength was improved due to lower surface roughness, presence of compressive residual stresses, and removal of surface porosity. The results show that increasing the layer thickness (within the range tested) has a minor negative impact on fatigue strength; however, it has a major positive impact on the productivity of the SLM process. In addition, it is clear that the impact of postmachining on fatigue is far greater than that of the layer thickness.