Yunpeng Chu

At present, phosphogypsum, as an industrial by-product, is a solid waste in phosphoric acid production, and its accumulation has caused serious environmental pollution. Furthermore, due to the insufficient insulation properties of traditional wall materials, the issue of a rising proportion of building energy consumption in total social energy consumption has become increasingly pressing. The study investigated vitrified beads as a light aggregate and phosphogypsum, mineral powder, and quicklime as an inorganic composite cementitious system to prepare the phosphogypsum-based lightweight thermal insulation material. The effect mechanism of the initial material ratio on the mechanical properties and micro-morphology of insulation materials was studied by macroscale mechanical property testing, X-ray diffraction, and scanning electron microscopy. Meanwhile, in order to meet the performance indexes specified in relevant standards, insulation materials were modified by adding sulfate aluminate cement, basalt fibers, and a waterproof agent to improve the strength, toughness, and water resistance. Based on the single-factor experimental design, the optimal dosage of various admixtures was obtained. The results indicated that the optimal properties of the sample were achieved when the binder–bead ratio was 1:4, the water–binder ratio was 1.6, the dosage of hydroxypropyl methylcellulose was 0.1%, and the solid content of waterborne acrylic emulsion was 24%. The optimal dosages of cement and fibers were 8% and 0.9%, respectively. The cement hydration products and gypsum crystals lapped through each other, filling the pores in the matrix and increasing the strength of the sample. In addition, the fibers could form a disordered network structure inside the matrix, disperse external force, weaken the stress concentration at the tip of internal cracks, and significantly improve the toughness of the modified sample. By incorporating 2.0% paraffin emulsion in the mortar and spraying 5 dilutions of sodium methyl silicate on the external surface, dense protective layers were formed both inside and outside the modified sample. The water absorption rate reduced from 30.27% to 23.30%, and the water resistance was increased to satisfy the specified requirement for the insulation material.

As one of the most dangerous geological hazards in the world, debris flows can destroy trees and structures, break electrical, water, and gas lines, and disrupt bridges and roadways in a short period of time, threatening life and property. In particular, fast-moving large boulders carried by debris-induced destructive impact loading can strike objects without warning. To resist impact loading caused by rocks in debris, this paper proposed an innovative grid-type debris dam (or Sabo dam) design composed of symmetrical cross-sections of steel tubular flange beams and columns. This paper studied the dynamic performance of the tubular flange columns under impact loading by conducting lab tests and numerical simulations. Moreover, the dynamic response of the grid-type debris dam was simulated under various loading conditions. Comparing three different types of columns with similar configurations under the same loading condition, the tubular flange column proposed in this research exhibits better performance in overall strain, displacement, acceleration, and bending conditions. Furthermore, the results also prove that the proposed structure has excellent interoperability and energy absorption capabilities. When increasing the testing impact load, the failure modes of the dam change from dent at the impact point to local buckling and total failure of the structure, which indicates that the structure has superior performance under impact loading.