Kristine Irtiseva

Among the various methods for collecting oil spills and oil products, including from the water surface, one of the most effective is the use of sorbents. In this work, three-component bio-based composite granular adsorbents were produced and studied for oil products’ pollution collection. A bio-based binder made of peat, devulcanised crumb rubber from used tyres, and part fly ash as cenospheres were used for absorbent production. The structure, surface morphology, porosity, mechanical properties, and sorption kinetics of the obtained samples were studied. Composite hydrophobicity and sorption capacity to oil products, such as diesel fuel (DF) and motor oil (MO), were determined. The obtained pellets are characterised by a sufficiently pronounced ability to absorb oil products such as DF. As the amount of CR in the granules increases, the diesel absorption capacity increases significantly. The case of 30-70-0 is almost three times higher than the granules from homogenised peat. The increase in q is due to two factors: the pronounced surface hydrophobicity of the samples (Θ = 152°) and a heterogeneous porous granule structure. The presence of the cenosphere in the biocomposite reduces its surface hydrophobicity while increasing the diesel absorption capacity. Relatively rapid realisation of the maximum saturation by the MO was noted. In common, the designed absorbent shows up to 0.7 g·g⁻¹ sorption capacity for MO and up to 1.55 g·g⁻¹ sorption capacity for diesel. A possible mechanism of DF absorption and the limiting stages of the process approximated for different kinetic models are discussed. The Weber–Morris diffusion model is used to primarily distinguish the limiting effect of the external and internal diffusion of the adsorbate on the absorption process.

Among the various methods for collecting oil spills and oil products, including from the water surface, one of the most effective is the use of sorbents. In this work, three-component bio-based composite granular adsorbents were produced and studied for oil products pollution collection. A bio-based binder made of peat, devulcanised crumb rubber from used tyres, and part fly ash as cenospheres were used for absorbent production. The structure, surface morphology, porosity, mechanical properties, and sorption kinetics of the obtained samples were studied. Composite hydrophobicity and sorption capacity to oil products such as diesel fuel (DF) and motor oil (MO) were determined. The obtained pellets are characterised by a sufficiently pronounced ability to absorb oil products such as DF. As the amount of CR in the granules increases, the diesel absorption capacity increases significantly. The case of 30-70-0 is almost 3 times higher than the granules from homogenised peat. The increase in q is due to two factors: pronounced surface hydrophobicity of the samples (Θ = 152°) and a heterogeneous porous granule structure. The presence of the cenosphere in the biocomposite reduces its surface hydrophobicity while increasing the diesel absorption capacity. Relatively rapid realisation of the maximum saturation by the MO was noted. In common, the designed absorbent shows up to 0.7 g·g^-1 sorption capacity for MO and up to 1.55 g·g^-1 sorption capacity for diesel. A possible mechanism of DF absorption and the limiting stages of the process approximated for different kinetic models are discussed. The Weber-Morris diffusion model is used to primarily distinguish the limiting effect of external and internal diffusion of adsorbate on the absorption process

The utilisation of industrial residual products to develop new value-added materials and reduce their environmental footprint is one of the critical challenges of science and industry. Development of new multifunctional and bio-based composite materials is an excellent opportunity for the effective utilisation of residual industrial products and a right step in the Green Deal’s direction as approved by the European Commission. Keeping the various issues in mind, we describe the manufacturing and characterisation of the three-component bio-based composites in this work. The key components are a bio-based binder made of peat, devulcanised crumb rubber (DCR) from used tyres, and part of the fly ash, i.e., the cenosphere (CS). The three-phase composites were prepared in the form of a block to investigate their mechanical properties and density, and in the form of granules for the determination of the sorption of water and oil products. We also investigated the properties’ dependence on the DCR and CS fraction. It was found that the maximum compression strength (in block form) observed for the composition without CS and DCR addition was 79.3 MPa, while the second-highest value of compression strength was 11.2 MPa for the composition with 27.3 wt.% of CS. For compositions with a bio-binder content from 17.4 to 55.8 wt.%, and with DCR contents ranging from 11.0 to 62.0 wt.%, the compressive strength was in the range from 1.1 to 2.0 MPa. Liquid-sorption analysis (water and diesel) showed that the maximum saturation of liquids, in both cases, was set after 35 min and ranged from 1.05 to 1.4 g·g ⁻¹ for water, and 0.77 to 1.25 g·g⁻¹ for diesel. It was observed that 90% of the maximum saturation with diesel fuel came after 10 min and for water after 35 min.

The utilisation of the industrial residual products to develop new value-added materials and to reduce footprint is one of the critical challenges of science and industry. Development of the new multifunctional and bio-based composites materials is an excellent opportunity for the effective utilisation of industrial residual products. Keeping the different issues in mind, in this work, we describe the manufacturing and characterisation of the three-phases bio-based composites. The key components are bio-based binder made of peat, devulcanised crumb rubber (DCR) from used tires and part of the fly ash, i.e. the cenosphere (CS). The three-phase composite prepared in the form of a block were investigated for their mechanical properties and density. The three-phase composite was prepared in the form a) of a block were investigated for their mechanical properties, and density and b) a form of granules for determination of the water and oil products sorption were investigated. We have also investigated the dependence of the properties on the DCR and CS fraction. It has been found, that maximum compression strength (in block form) observed for composition without CS and DCR addition was- 79.3 MPa, while the second-highest value of compression strength is 11.2 MPa for composition with 27.3 wt% of CS. For compositions with bio binder content from 17.4 to 55.8 wt% and with DCR contents in range from 11.0 to 62.0 wt%, the compression strength is in the range from 1.1 to 2.0 MPa. Liquid sorption analysis (water and diesel) showed that the maximum saturation of liquids in both cases is set after 35 minutes and ranges from 1.05 to 1.4 g·g -1 for water and 0.77 to 1.25 g·g-1 for diesel. It was noted that 90% of the maximum saturation with diesel fuel comes after 10 minutes and for water after 35 minutes.

Synthesis or humification of humic substances (HSs) is the second widely applied organic compound transformation process after photosynthesis. Peat decomposition process results in a production of a HSs which has a high demand in agriculture, forestry, and gardening areas. Addition of the KOH is good option for environmental protection and K⁺ belongs to the nitrogen, potassium and phosphorous (NKP) mineral component. A homogenization process in a customize for commerce, where peat treatment technology was improved with the help of the cavitation effect. This effect was provided with the help of the high-speed mixer-disperser (HSMD) developed at Riga Technical University. Mechanical cavitation causes relatively high energy shifts from mechanical movement of cavitation causing elements to the liquid medium which causes efficient destruction of particles inside a suspension. Values of the peat particle diameter at 50 % in the cumulative distribution before and after 1, 2, and 3 homogenization cycles were measured in the present study. The aim of the present study was to find the optimal conditions (KOH concentration, cavitation cycles and reaction temperature) to produce potassium humate (K-HSs) regarding sustainable regenerative approach aspects. Cavitation treatment of the tested peat particle diameter at 50 % in the cumulative distribution (d₅₀) from 267 down to 129 µm; the peak in the size range from 160 up to 409 µm completely disappears and significantly decreases the number of Dalton’s which causes the more efficient formation of fulvic acid caused by increased concentration of carbonyl and carboxyl groups as compared with the conventional homogenization method.