Neazar Baghdadi

This investigation aimed at evaluating the efficiency of micro and nanoclays as a low-cost material for the removal of crystal violet (CV) dye from an aqueous solution. The impacts of various factors (contact time, pH, adsorbent dosage, temperature, initial dye concentration) on the adsorption process have been taken into consideration. Six micro and nanoclay samples were obtained by treating clay materials collected from different locations in the Albaha region, Saudi Arabia. Out of the six tested micro and nanoclays materials, two (NCQ1 and NCQ3) were selected based on the highest adsorption efficiency for complete experimentation. The morphology and structure of the selected micro and nanoclay adsorbents were characterized by various techniques: SEM-EDX, FTIR, XRF, XRD, and ICP-MS. The XRF showed that the main oxides of both nanoclays were SiO₂, Al₂O₃, Fe₂O₃, K₂O, CaO, and MgO, and the rest were impurities. All the parameters affecting the adsorption of CV dye were optimized in a batch system, and the optimized working conditions were an equilibrium time of 120 min, a dose of 30 mg, a temperature of 25 °C, and an initial CV concentration of 400 mg/L. The equilibrium data were tested using nonlinear isotherm and kinetic models, which showed that the Freundlich isotherm and pseudo-second-order kinetics gave the best fit with the experimental data, indicating a physico-chemical interaction occurred between the CV dye and both selected micro and nanoclay surfaces. The maximum adsorption capacities of NCQ1 and NCQ3 adsorbents were 206.73 and 203.66 mg/g, respectively, at 25 °C. The thermodynamic factors revealed that the CV dye adsorption of both micro and nanoclays was spontaneous and showed an exothermic process. Therefore, the examined natural micro and nanoclays adsorbents are promising effective adsorbents for the elimination of CV dye from an aqueous environment.

Superparamagnetic iron oxide nanoparticles have been coated with a low affinity CXCR4 receptor antagonist to give a high affinity multivalent CXCR4 binding construct.

Conducting polymers have attracted significant attention due to their easy fabrication, morphology modification, and their electrical properties. Amongst them, polypyrrole (PPy) has attractive thermoelectric (TE) properties. Engineering of this polymer in one-dimensional (1D) nanostructured form is found to enhance its TE performance. This was achieved in the present work by using multi-walled carbon nanotubes (MWCNTs) as a core template to direct the self-assembly of PPy and also to further enhance its TE performance. The growth of PPy on the sidewalls of MWCNTs was performed in an acidic medium based oxidative in situ polymerization. Various concentrations of MWCNTs within the range 1.1–14.6 wt.% were used to form the MWCNTs/PPy nanocomposites in 1D core-shell structures. The morphology and microstructure results of the produced nanocomposite samples showed that this MWCNTs were successfully coated by thick and thin layers of PPy. At low concentrations of MWCNTs, thick layers of PPy are formed. While at high concentrations thin layers are coated. The formed 1D nanocomposites have enhanced TE performance, particularly those containing higher contents of MWCNTs. The power factor and figure of merit values for the formed 1D nanocomposites recorded around 0.77 µV/mK² and 1 × 10⁻³ at room temperature (RT), respectively. This enhancement was attributed to the perfect coating and good interaction between PPy and MWCNT through π–π stacking between the polymer chains and these nanotubes. These results might be useful for developing future TE materials and devices.

The composite of ceria has been widely studied as an electrode material for supercapacitors applications due to its high energy density. Herein, we synthesize CeO₂/NiO nanocomposite via a hydrothermal route and explore its different aspects using various characterization techniques. The crystal structure is investigated using X-ray diffraction, Fourier transform infrared, and Raman spectroscopy. The formation of nanoflakes which combine to form flower-like morphology is observed from scanning electron microscope images. Selected area scans confirm the presence of all elements in accordance with their stoichiometric amount and thus authenticate the elemental purity. Polycrystalline nature with crystallite size 8–10 nm having truncated octahedron shape is confirmed from tunneling electron microscope images. Using X-ray photoelectron spectroscopy the different oxidation states of Ce and Ni are observed which play the role of active sites in the electrochemical performance of this nanocomposite material. Cyclic Voltammetry(CV) measurements at different scan rates and Galvanic Charge Discharge (GCD) measurements at different current densities are performed to probe the electrochemical response which revealed the potential of CeO₂/NiO nanocomposite as an electrode material for energy storage devices.

Microwave irradiation is found to be effective to provide highly crystalline nanostructured materials. In this work, this technique has been used to produce highly improved thermoelectric (TE) material based on aluminum (Al) doped zinc oxide (ZnO) nanostructures (NSs). The effect of Al dopant at the concentration range 0.5–3 mol % on the structural and TE properties has been investigated in more details. The optimum concentration of Al for better TE performance is found to be 2 mol %, which could significantly increase the electrical conductivity and reduce the thermal conductivity of ZnO NSs and thus enhance the TE performance. This concentration showed almost metallic conductivity behavior for ZnO NSs at low temperatures, e.g., below 500 K. The electrical conductivity reached 400 S/m at room temperature, which is around 200 times greater than the value recorded for the pure ZnO NSs. Remarkably, the measured room temperature thermal conductivity of the microwave synthesized ZnO NSs was very low, which is around 4 W/m·K. This value was further reduced to 0.5 W/m·K by increasing the Al doping to 3 mol %. The figure of merit recorded 0.028 at 675 K, which is 15 times higher than that of the pure ZnO NSs. The output power of a single leg module made of 2 mol % Al doped ZnO NSs was 3.7 µW at 485 K, which is higher by 8 times than that of the pure sample. These results demonstrated the advantage of the microwave irradiation rout as a superior synthetic technique for producing and doping promising TE nanomaterials like ZnO NSs.