Andrea Mantelli

An additive remanufacturing process for mechanically recycled glass fibers and thermally recycled carbon fibers was developed. The main purpose was to demonstrate the feasibility of an additive remanufacturing process starting from recycled glass and carbon fibers to obtain a new photo- and thermally-curable composite. 3D printable and UV-curable inks were developed and characterized for new ad-hoc UV-assisted 3D printing apparatus. Rheological behavior was investigated and optimized considering the 3D printing process, the recyclate content, and the level of dispersion in the matrix. Some requirements for the new formulations were defined. Moreover, new printing apparatuses were designed and modified to improve the remanufacturing process. Different models and geometries were defined with different printable ink formulations to test material mechanical properties and overall process quality on the final pieces. To sum up, 3D printable inks with different percentages of recycled glass fiber and carbon fiber reinforced polymers were successfully 3D printed.

Three different classes of thermosetting styrene-free resins were investigated to assess their suitability to constitute the matrix phase in the reformulation of composites reinforced with mechanically recycled glass fibers. Resin reactivity and mechanical properties after curing were compared to commercial styrene-based, unsaturated polyester resins. The polymeric resin, acting as a binder, could be properly selected depending on the desired reactivity, processability, and mechanical behavior. Some prototypal examples of reformulated composites with different types and contents of recycled glass fibers were produced and mechanically tested. The combination of the epoxy resin with up to 60 wt% of mechanically recycled glass fibers resulted in an increase of elastic modulus up to 7.5 GPa.

Coating processes are emerging for new applications related to remanufactured products from End-of-Life materials. In this perspective, their employment can generate interesting scenarios for the design of products and solutions in circular economy frameworks, especially for composite materials. This chapter would give an overview of coating design and application for recycled glass fiber reinforced polymers on the base of the experimentation made within the FiberEUse project. New cosmetic and functional coatings were developed and tested on different polymer composite substrates filled with mechanically recycled End-of-Life glass fibers. Afterwards, recycled glass fiber reinforced polymer samples from water-solvable 3D printed molds were successfully coated. Finally, new industrial applications for the developed coatings and general guidelines for the coating of recycled glass fiber reinforced polymers were proposed by using the FiberEUse Demo Cases as a theoretical proof-of-concept.

Fused filament fabrication allows the direct manufacturing of customized and complex products although the layer-by-layer appearance of this process strongly affects the surface quality of the final parts. In recent years, an increasing number of post-processing treatments has been developed for the most used materials. Contrarily to other additive manufacturing technologies, metallization is not a common surface treatment for this process despite the increasing range of high-performing 3D printable materials. The objective of this work is to explore the use of physical vapor deposition sputtering for the chromium metallization of thermoplastic polymers and composites obtained by fused filament fabrication. The thermal and mechanical properties of five materials were firstly evaluated by means of differential scanning calorimetry and tensile tests. Meanwhile, a specific finishing torture test sample was designed and 3D printed to perform the metallization process and evaluate the finishing on different geometrical features. Furthermore, the roughness of the samples was measured before and after the metallization, and a cost analysis was performed to assess the cost-efficiency. To sum up, the metallization of five samples made with different materials was successfully achieved. Although some 3D printing defects worsened after the post-processing treatment, good homogeneity on the finest details was reached. These promising results may encourage further experimentations as well as the development of new applications, i.e., for the automotive and furniture fields.

Within the complex framework of additive manufacturing, direct ink writing (DIW) processes significantly contribute to extending the range of 3D‐printable materials (i.e., thermosetting resins, ceramics, hydrogels). Thanks to this technology, viscous inks are easily extruded for the creation of 3D structures. Nevertheless, the quick recovery of the solid‐like behavior after extrusion remains one of the most crucial open issues for 3D‐printable inks. The main goal herein is to improve the printability of a UV‐curable thermosetting composite ink reinforced with mechanically recycled glass fiber composites by modifying its rheological behavior. The overall process is optimized, leading to the definition of the optimal extrusion parameters for these types of materials. Furthermore, the retraction mode is successfully developed for the DIW of recycled composites. Additional features are achieved, thanks to the aforementioned improvements, such as 3D complex shapes, assembled pieces, and/or moving built‐in mechanisms, increasing the number of new potential applications of recycled glass fiber‐reinforced polymers.

Despite the growing global interest in 3D printed carbon fiber reinforced polymers, most of the applications are still limited to high-performance sectors due to the low effectiveness–cost ratio of virgin carbon fibers. However, the use of recycled carbon fibers in 3D printing is almost unexplored, especially for thermoset-based composites. This paper aims to demonstrate the feasibility of recycled carbon fibers 3D printing via UV-assisted direct ink writing. Pyrolyzed recycled carbon fibers with a sizing treatment were firstly shredded to be used as a reinforcement of a thermally and photo-curable acrylic resin. UV-differential scanning calorimetry analyses were then performed to define the material crosslinking of the 3D printable ink. Because of the poor UV reactivity of the resin loaded with carbon fibers, a rheology modifier was added to guarantee shape retention after 3D printing. Thanks to a customized 3D printer based on a commercial apparatus, a batch of specimens was successfully 3D printed. According to the tensile tests and Scanning Electron Microscopy analysis, the material shows good mechanical properties and the absence of layer marks related to the 3D printing. These results will, therefore, pave the way for the use of 3D printed recycled carbon fiber reinforced polymers in new fields of application.

Despite the large use of composites for industrial applications, their end-of-life management is still an open issue for manufacturing, especially in the wind energy sector. Additive manufacturing technology has been emerging as a solution, enhancing circular economy models, and using recycled composites for glass fiber-reinforced polymers is spreading as a new additive manufacturing trend. Nevertheless, their mechanical properties are still not comparable to pristine materials. The purpose of this paper is to examine the additive re-manufacturing of end-of-life glass fiber composites with mechanical performances that are comparable to virgin glass fiber-reinforced materials. Through a systematic characterization of the recyclate, requirements of the filler for the liquid deposition modeling process were identified. Printability and material surface quality of different formulations were analyzed using a low-cost modified 3D printer. Two hypothetical design concepts were also manufactured to validate the field of application. Furthermore, an understanding of the mechanical behavior was accomplished by means of tensile tests, and the results were compared with a benchmark formulation with virgin glass fibers. Mechanically recycled glass fibers show the capability to substitute pristine fillers, unlocking their use for new fields of application.

Purpose: The purpose of this study is to demonstrate the potential of three-dimensional printing technology for the remanufacturing of end-of-life (EoL) composites. This technology will enable the rapid fabrication of environmentally sustainable structures with complex shapes and good mechanical properties. These three-dimensional printed objects will have several application fields, such as street furniture and urban renewal, thus promoting a circular economy model. Design/methodology/approach: For this purpose, a low-cost liquid deposition modeling technology was used to extrude photo-curable and thermally curable composite inks, composed of an acrylate-based resin loaded with different amounts of mechanically recycled glass fiber reinforced composites (GFRCs). Rheological properties of the extruded inks and their printability window and the conversion of cured composites after an ultraviolet light (UV) assisted extrusion were investigated. In addition, tensile properties of composites remanufactured by this UV-assisted technology were studied. Findings: A printability window was found for the three-dimensional printable GFRCs inks. The formulation of the composite printable inks was optimized to obtain high quality printed objects with a high content of recycled GFRCs. Tensile tests also showed promising mechanical properties for printed GFRCs obtained with this approach. Originality/value: The novelty of this paper consists in the remanufacturing of GFRCs by the three-dimensional printing technology to promote the implementation of a circular economy. This study shows the feasibility of this approach, using mechanically recycled EoL GFRCs, composed of a thermoset polymer matrix, which cannot be melted as in case of thermoplastic-based composites. Objects with complex shapes were three-dimensional printed and presented here as a proof-of-concept.