Yu Wang

With the increase of cement output, the demand for cement expansion agents increases, and composite expansion agents have become the development trend. The purpose of this study is to study the microscopic change process and expansion effect of calcium oxide and magnesium oxide double expansion agents. After calcination at different temperatures, the change process of microscopic morphology of calcined products was observed. Through calcining dolomite at 900 °C, the mixture D900 of calcium oxide and magnesium oxide was obtained. To prepare mixed cement, 10 wt %, 20 wt %, and 30 wt % of D900 were added into cement to prepare mixed cement. At the same time, the compressive strength, deformation, and porosity of mixed cement were measured. The results show that adding D900 improves the expansion rate of early cement paste and reduces the compressive strength. After 120 days, the compressive strength of 20 wt % cement paste is higher than that of blank cement paste, and the porosity of 20 wt % cement paste is the lowest among the three mixed cements. This shows that 20 wt % is a more suitable substitute.

In the marine environment, sulfate ions and chloride ions are abundant. Therefore, sulfate attack and chloride ion attack are common failure forms of marine concrete. Mg–Al hydrotalcite is a layered bimetallic hydroxide, which can be used as guest molecular adsorbent. In this experiment, we synthesized Mg–Al hydrotalcite, and the crystal state, surface morphology, and composition of this adsorbent were investigated by modern micro-analysis technology. Mg–Al hydrotalcite was added into the prepared target ion solution, to explore the influence of various factors on the adsorption performance of Mg–Al hydrotalcite, and then calcined Mg–Al hydrotalcite was added into cement paste, to study the mechanical properties and durability of the paste samples. The experimental results show that the optimum conditions for adsorption of chloride ions by calcined Mg–Al hydrotalcite are an adsorption time of 4 h, temperature of 35 °C, LDO (calcined Mg-Al hydrotalcite) dosage of 3.5 g/L, and a pH of 8. The adsorption effect of sulfate ion is best when the adsorption time is 6 h, the temperature is 35 °C, the dosage of LDO is 4 g/L, and the pH = 8. The optimal adsorption conditions of calcined Mg–Al hydrotalcite for chloride ion and sulfate ion are not completely the same, and the adsorption of these two ions in mixed solution shows competitive adsorption. Compared with the common paste specimens without Mg–Al hydrotalcite, the mechanical properties and deformation properties of cement specimens can be significantly improved by adding Mg–Al hydrotalcite.

Boric acid, a weak acid, is often used to shield neutrons in water cooling systems in nuclear power stations. The leakage of boric acid in water cooling systems damages the concrete structure and affects the safety of nuclear power engineering. In this experiment, concrete specimens were cured with boric acid at 20, 40, and 70 °C to study the effect of boric acid on the microstructure and properties of concrete. X-ray diffraction (XRD) and thermogravimetry and differential scanning calorimetry (TG-DSC) were used to analyze the change in mineral composition. The microstructure was examined by scanning electron microscope (SEM). The porosity of the concrete was examined by mercury intrusion porosimetry (MIP). The results show that the performance of specimens was stable under the curing conditions of 20 and 40 °C. Under the curing environment of 70 °C, the performance of concrete cured with 0, 2000, and 7000 ppm concentrations was stable, but the compressive strength of the 180,000 ppm specimen was reduced by 27.8% and suffered the most serious loss of mass and surface corrosion, with the most harmful pores. The high concentration of boric acid seriously damaged the surface structure of concrete, which is the main reason for its loss of properties. This situation is extremely dangerous in nuclear power engineering, so the effect of boric acid leakage cannot be ignored.