Andre Zborowski

Manganese oxide nanoparticles (MnO_x NPs) are finding applications in several environmentally important areas such as farming and energy storage. MnO_x NPs span a range of metal oxidation states that open up a wide range of applications in catalysis as well. As a result, it is important to understand how such materials can impact human health through incidental exposure. In this study, we examined a range of commercially available Mn₂O₃ NPs and compared our characterization data to those supplied by manufacturers. Discrepancies were noted and then measured values were used to assess the biological impact of these materials on three mammalian cell lines—A549, HepG2 and J774A.1 cells. Cell toxicity assays showed that all Mn₂O₃ particles exhibited cytotoxic effects that may be correlated, at least in part, to the production of reactive oxygen species. All eight nanoforms also activated caspase 3 but not caspase 1, although the magnitude of these changes varied greatly between materials.

Cerium oxide nanoparticles are promising materials as novel nanoscale therapeutics and are commonly used materials in industrial processes. Most cytotoxicity studies on cerium oxide nanoparticles are made from in-lab prepared materials making comparison between studies challenging, especially when performed on unique cell lines under non-standard conditions. Using commercially available nanoparticles we show that particle stability/agglomeration may be critical in determining the cytotoxicity in some cell lines, while in other cell lines, larger sized primary particles are linked to higher cytotoxicity, contrasting what has been reported in the literature for smaller cerium nanoparticles. To accelerate the development of cerium oxide enabled commercial processes and biomedical innovations, a clearer understanding of the interactions between cerium oxide nanoparticles and cells is needed to better understand their fate in and impact on biological systems.

Nickel oxide (NiO) nanoparticles from several manufacturers with different reported sizes and surface coatings were characterized prior to assessing their cellular toxicity. The physical characterization of these particles revealed that sizes often varied from those reported by the supplier, and that particles were heavily agglomerated when dispersed in water, resulting in a smaller surface area and larger hydrodynamic diameter upon dispersion. Cytotoxicity testing of these materials showed differences between samples; however, correlation of these differences with the physical properties of the materials was not conclusive. Generally, particles with higher surface area and smaller hydrodynamic diameter were more cytotoxic. While all samples produced an increase in reactive oxygen species (ROS), there was no correlation between the magnitude of the increase in ROS and the difference in cytotoxicity between different materials.

A primary concern of commercial mined oil sands operations is the extent to which one can minimize the content of water and solids contaminants in the solvent-diluted bitumen products resulting from the bitumen production processes. During bitumen production, particles of about 2 µm or less may be responsible for the stabilization of water-in-bitumen emulsions that form during aqueous extraction of bitumen and purification of bitumen froth subsequently during the froth treatment processes, thus leading to the presence of those contaminants in solvent-diluted bitumen products. In this study, we separate and analyze sub-2 µm clay solids isolated from typical bitumen froth fed to a froth treatment plant at a commercial mined oil sands operation. Analytical transmission electron microscopy (TEM) with spatially-resolved energy-dispersive X-ray spectroscopy (EDX) and electron energy-loss spectroscopy (EELS) demonstrate key differences in morphology and composition between sub-2 µm clay aggregates with two distinct wettability characteristics: hydrophilic vs. biwettable particle surfaces. In particular, clay platelets with <200 nm lateral dimensions and thicknesses of a few atomic layers, which are intermixed within coarser sub-2 µm clay aggregates, are found to confer clear differences in morphological characteristics and wettability behaviors to the sub-2 µm clay aggregates. The <200 nm clay platelets found within sub-2 µm biwettable clays tend to arrange themselves with random orientations, whereas <200 nm clay platelets within sub-2 µm hydrophilic clays typically form well-ordered face-to-face stacks. Moreover, in biwettable sub-2 µm clay aggregates, <200 nm clay platelets often cover the surfaces of ~1–2 µm sized mineral particles, whereas similarly sized mineral particles in hydrophilic sub-2 µm clay aggregates, in contrast, generally have exposed surfaces without clay platelet coverage. These biwettable vs. hydrophilic behaviors are attributed to a difference in the surface characteristics of the <200 nm clay platelets caused by toluene-unextractable organic carbon coatings. Nanometer-scale carbon mapping reveals an inhomogeneous toluene-unextractable organic carbon coating on the surfaces of <200 nm platelets in biwettable clays. In contrast, hydrophilic clays have a significantly lower amount of toluene-unextractable organic carbon, which tends to be concentrated at steps or near metal oxide nanoparticles on clay particle surfaces. Mixing surface-active organic species, such as asphaltene, resin, or carboxylic organic acids of various types with inorganic solids can lead to a dramatically enhanced emulsion stability. Consequently, understanding the origin and characteristics of sub-2 µm clay solids in bitumen froth is important to (i) clarify their potential role in the formation of stable water-in-oil emulsions during bitumen production and (ii) improve froth treatment process performance to further reduce contaminant solids in solvent-diluted bitumen products. We discuss the implications of our results from these two perspectives.