Bo Ruan

Aeolian sand is widely distributed in the Takramagan Desert, Xinjiang, China, which cannot be directly used as railway subgrade filling. It is beneficial for environmental protection to use fiber and cement-reinforced aeolian sand as railway subgrade filling. The present work is to explore the enhancement of tensile strength in cemented aeolian sand via the incorporation of polypropylene fibers under conditions of elevated temperature and drying curing. The purpose Is to delve into the examination of the temperature’s impact on not only the mechanical attributes but also the microstructure of cemented aeolian sand reinforced with polypropylene fiber (CSRPF). For this, a comprehensive set of tests encompassing splitting tensile strength (STS) assessments and nuclear magnetic resonance (NMR) examinations is conducted. A total of 252 CSRPF specimens with varying fiber content (0, 6‰, 8‰, and 10‰) are tested at different curing temperatures (30 °C, 40 °C, 50 °C, 60 °C, 70 °C, and 80 °C). The outcomes of the NMR examinations indicate that elevating the curing temperature induces the expansion of pores within CSRPF, both in size and volume, consequently contributing to heightened internal structural deterioration. STS tests demonstrate that the STS of CSRPF decreases as the curing temperature increases. Meanwhile, the STS of CSRPF increases with fiber content, with optimal fiber content being 8‰. Regression models accurately predict the STS, with the curing temperature exhibiting the greatest influence, followed by the fiber content according to sensitivity analysis. The research results provide a valuable reference for the use of CSRPF as railway subgrade filling under high temperature and drying conditions.

The aim of this study was to investigate the effect of roughness and relative density on the mechanical properties of sand–concrete pile interface. A series of direct shear tests were carried out on the interface using a large-scale direct shear apparatus with various relative densities of sand (73%, 47%, and 23%) and concrete blocks with four roughness values (I = 0, 10, 20, and 30 mm). Various mechanical properties (such as shear stress, volume change, peak shear strength, secant friction angle, and normalized friction coefficient) from the interface tests were compared with trends obtained from the pure sand direct shear test. For the smooth interface, the shear stress–horizontal displacement curves of the dense sand specimen exhibited a slight softening response, which became more apparent as the roughness increased. The curves of the loose sand specimen demonstrated a hardening response. The volumetric response was influenced by the combination of normal stress, relative density, and roughness. The peak shear strength demonstrated a nonlinear increasing trend as the normal stress increased. With an increase in the normal stress, the secant friction angle and peak friction coefficient decreased as exponential and power functions, respectively. Additionally, a critical roughness value I_cr resulted from the tests, which halted the upward trend of the peak friction coefficient and normalized the secant friction angle when I exceeded I_cr.

A series of triaxial compression tests were conducted to investigate the influence of the fiber content and confining pressure on the shearing characteristics of cement‐stabilized clay reinforced with glass fibers. The glass fiber contents were 0, 1‰, 2‰, 3‰, and 4‰ by weight of the dry soil. The stress strain and volume change behavior, shear strength, and energy absorption of the test specimen were obtained. The results indicate that the inclusion of glass fibers can increase the shear strength, inhibit the volumetric dilation of the test specimen, and improve its brittle behavior. The cohesion of the cement‐stabilized clay reinforced with 4‰ glass fiber content is 2.8 times greater than that of the cement‐stabilized clay. The effect of the fiber content on the friction angle is not obvious. It is found that the glass fiber reinforcement is more substantial under a low confining pressure. The scanning electron microscopy test results show that the surface of the glass fiber is wrapped with cement hydrate crystals, which increases the bite force and friction between the fiber and the soil particles. A single fiber is similar to an anchor in the soil, which enhances the mechanical properties of the cement‐stabilized clay reinforced with fibers.